Translucent zirconia sintered body, process for producing the same, and use of the same

a zirconia and translucent technology, applied in the field of zirconia sintered body, can solve the problems of inability to give a sense of translucency, difficulty in achieving the effect of translucency, and difficulty in achieving the effect of high density, excellent translucency and high strength

Inactive Publication Date: 2011-02-03
TOSOH CORP
View PDF17 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0027]The translucent zirconia sintered body of the invention has a high density, high strength, and excellent translucency and is hence an excellent zirconia sintered body for use in dental applications, specifically, an excellent sintered body for use as a mill blank for a denture material or...

Problems solved by technology

Single crystals of zirconia give a sense of translucency, and single-crystal zirconia containing about 10 mol % yttria (cubic zirconia), which is used as jewelry and the like, has conventionally had a problem that the strength thereof is exceedingly low.
On the other hand, it is known that ordinary zirconia sintered bodies, which are polycrystalline objects, do not give a sense of translucency.
However, this translucent zirconia has had a problem concernin...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Translucent zirconia sintered body, process for producing the same, and use of the same
  • Translucent zirconia sintered body, process for producing the same, and use of the same
  • Translucent zirconia sintered body, process for producing the same, and use of the same

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0083]An aqueous solution of potassium hydroxide was added to a 0.4 mol / L aqueous solution of zirconium oxychloride to prepare an aqueous solution having a molar concentration ratio [OH] / [Zr] of 0.02. While this solution was being stirred in a flask equipped with a reflux condenser, a hydrolysis reaction was conducted at the boiling temperature for 350 hours. The conversion to the hydrated zirconia sol obtained was 99%. Distilled water was added to this hydrated zirconia sol to prepare a solution having a concentration of 0.3 mol / L in terms of zirconia concentration. This solution was used as a starting solution to conduct a hydrolysis reaction at the boiling temperature for 200 hours while intermittently discharging 5% by volume of the solution from the reaction vessel and feeding an aqueous zirconium oxychloride solution to which 0.3 mol / L aqueous sodium hydroxide solution had been added ([OH] / [Zr]=0.02). This aqueous zirconium oxychloride solution was fed at intervals of 30 minut...

example 2

[0089]A zirconia powder was obtained in the same manner as in Example 1, except that the alumina sol was added in an amount of 0.12% by weight in terms of alumina content. The properties of the zirconia powder obtained are shown in Table 1. Thereafter, the zirconia powder obtained was dispersed in water to obtain a zirconia slurry having a slurry concentration of 50%. An acrylic binder and poly(vinyl alcohol) were added to the slurry in an amount of 3 wt % based on the zirconia contained in the zirconia slurry, and a thickener was added to regulate the viscosity. Thereafter, the slurry was granulated by spraying to produce zirconia granules. The zirconia granules obtained had an average particle diameter of 45 μm and a bulk density of 1.20 g / cm3.

[0090]Subsequently, the zirconia granules obtained above were press-molded by CIP (pressure, 2 t / cm2) and sintered under the conditions of 1,450° C.

[0091]The sintering temperature for the sintered body obtained and the properties of the sint...

example 3

[0093]A zirconia powder was obtained under the same conditions as in Example 1, except that the alumina sol was added in an amount of 0.17% by weight in terms of alumina content. The properties of the zirconia powder obtained are shown in Table 1. This zirconia powder was used to obtain zirconia granules by the same method as in Example 2. The zirconia granules obtained had an average particle diameter of 40 μm and a bulk density of 1.18 g / cm3.

[0094]Subsequently, the zirconia granules obtained above were press-molded and sintered under the conditions of 1,400° C. The sintering temperature for the sintered body obtained and the properties of the sintered body, i.e., density, bending strength, crystal grain diameter, and monoclinic fraction after the deterioration test, are shown in Table 2.

[0095]The sintered body obtained had a total light transmittance of 39% and was ascertained to be a sintered body having excellent translucency. The monoclinic fraction after the deterioration test...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Temperatureaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

A subject of the invention relates to providing a powder for a translucent zirconia sintered body which is necessary for the production of a zirconia sintered body having a high sintered-body density and high strength and giving an excellent sense of translucency, without conducting any special sintering, such as HIP sintering. The invention relates to a technique for obtaining, through normal-pressure sintering, a translucent zirconia sintered body characterized by comprising zirconia which contains 2-4 mol % yttria as a stabilizer and has an alumina content of 0.2 wt % or lower, and by having a relative density of 99.8% or higher and a total light transmittance, as measured at a thickness of 1.0 mm, of 35% or higher. It is preferred that a powder containing 0-0.2 wt % alumina with a particle diameter of 0.01-0.5 μm, having a BET specific surface area of 5-16 m2/g and an average particle diameter of 0.3-0.7 μm, and having a rate of sintering shrinkage in normal-pressure sintering (Δρ/ΔT; g/cm3·° C.) of 0.0125 or higher but 0.0160 or lower should be subjected to normal-pressure sintering in the atmosphere.

Description

TECHNICAL FIELD[0001]The present invention relates to a zirconia sintered body produced by normal-pressure sintering, having a high sintered-body density and high strength, and having excellent translucency. More particularly, the invention relates to a zirconia sintered body for use in dental applications, which is suitable for use as a mill blank for a denture material or the like or as an orthodontic bracket.BACKGROUND ART[0002]Zirconia sintered bodies containing a small amount of Y2O3 in a solid solution state as a stabilizer have high strength and high toughness and are hence extensively utilized as materials for machine structures, such as cutting tools, dies, nozzles, and bearings, and materials for the living body, such as dental materials. In the case of dental materials, not only mechanical properties, i.e., high strength and high toughness, but also optical properties, i.e., translucency and color tone, are required from an aesthetic standpoint.[0003]Single crystals of zi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61C7/12C04B35/482A61C13/08
CPCC04B35/486C04B2235/3246C04B2235/3217C04B2235/3225C04B2235/444C04B2235/5409C04B2235/5436C04B2235/5445C04B2235/5454C04B2235/656C04B2235/6562C04B2235/72C04B2235/765C04B2235/77C04B2235/785C04B2235/96C04B2235/9615C04B2235/9653C04B2235/9669C01G25/00C01G25/02C01P2002/52C01P2002/54C01P2004/62C01P2006/10C01P2006/12B82Y30/00A61C7/14A61C13/0022A61C13/083C04B35/48C04B35/62675C04B35/6263C04B35/62695C04B2235/3218C04B2235/608A61K6/16A61K6/824A61K6/17A61K6/818
Inventor FUJISAKI, HIROYUKIKAWAMURA, KIYOTAKAIMAI, KOHEI
Owner TOSOH CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap