Environment-friendly water priming paint

A water-based primer and an environmentally friendly technology, applied in the field of paint making, can solve the problems of poor anode protection performance, high porosity, and lack of electrical conductivity, etc., and achieve excellent electrochemical anticorrosion performance, excellent organic solvent resistance, and resistivity. Anti-static effect

Inactive Publication Date: 2009-12-02
WUHAN FUMAISHI NEW MATERIAL CHEM
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thermal spraying of zinc and aluminum is sprayed on the metal substrate after melting and atomizing the wire rod, which has residual stress, high porosity, and poor shielding performance, so a sealing coating must be added, and the zinc mist generated during construction is harmful to the construction team. Personnel are at great risk
Both organic and inorganic zinc-rich coatings use high-fineness zinc powder as raw material, which has good shielding performance on metal substrates, but organic mostly uses epoxy resin as base material, which does not have conductivity, so its anodic protection performance is far inferior to that of thermal spray coatings. Zinc, aluminum and inorganic zinc-rich coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly water priming paint
  • Environment-friendly water priming paint
  • Environment-friendly water priming paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Environmental protection high-efficiency water-based primer of the present invention, its component weight is Kg:

[0033] Component one:

[0034] Silicate solution 60

[0035] Sodium oxide, potassium oxide mixed oxide 20

[0036] Acrylic Emulsion 15

[0037] Isopropanol 5

[0038] Component two:

[0039] Zinc powder 80

[0040] Active magnetic powder 20

[0041] 1. Add 60Kg of silicate solution in component 1, 20Kg of potassium oxide and sodium oxide mixture in metal oxides, 15Kg of acrylic emulsion, and 5Kg of isopropanol into the reaction kettle. Mixing at the bottom, after reacting for 3-72 hours, filter after passing the inspection, pack into barrels, and put into storage.

[0042] 2. Grind, grind, and mix 50Kg of zinc powder and 30Kg of active magnet powder in component two, inspect, pack, and leave the factory.

Embodiment 2

[0044] Environmental protection high-efficiency water-based primer of the present invention, its component weight is Kg:

[0045] Component one:

[0046] Silicate solution 50

[0047] Lithium oxide 30

[0048] Acrylic Emulsion 13

[0049] Catalyst, magnesium oxide mixture 7

[0050] Component two:

[0051] Zinc powder 70

[0052] Active magnetic powder 30

[0053] 1. Add 50Kg of silicate liquid in component 1, 30Kg of lithium oxide mixture in metal oxides, 13Kg of acrylic emulsion, 5Kg of catalyst and magnesium oxide mixture into the reaction kettle, under the condition of temperature 50-100℃ After mixing and reacting for 3-72 hours, filter after passing the inspection, pack into barrels, and put into storage.

[0054] 2. Grind, grind, and evenly mix 70Kg of zinc powder and 30Kg of active magnet powder in component two, inspect, pack, and leave the factory.

Embodiment 3

[0056] Environmental protection high-efficiency water-based primer of the present invention, its component weight is Kg:

[0057] Component one:

[0058] Silicate solution 45

[0059] Potassium oxide 25

[0060] Acrylic Emulsion 20

[0061] Catalyst, magnesium oxide mixture 10

[0062] Component two:

[0063] Zinc powder 75

[0064] Active magnetic powder 25

[0065] 1. Add 45Kg of silicate solution in component 1, 25Kg of potassium oxide in metal oxide, 20Kg of acrylic acid emulsion, 10Kg of catalyst and magnesium oxide mixture into the reaction kettle, and mix at a temperature of 50-100°C , after reacting for 3-72 hours, filter after passing the inspection, pack into barrels, and put into storage.

[0066] 2. Grind, grind, and mix 75Kg of zinc powder and 25Kg of active magnet powder in component two, inspect, pack, and leave the factory.

[0067] The production process of active magnetic powder is as follows:

[0068] Preparation method 1: Put 75Kg of magnet powder,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An environmentally friendly water-based primer, the weight percentages of its components are: component 1: 50-60% of silicate solution; 20-30% of metal oxide; 15-20% of acrylic emulsion; and 1-10% of auxiliary agent. Component 2: 70-80% zinc powder; 20-30% active magnet powder. Its advantages are: using water as solvent, non-toxic, non-polluting, and zero VOC emissions; after 30 minutes of surface drying, it can be washed with water; the coating surface can be matched with various anti-corrosion coatings, which can meet the needs of various long-term heavy-duty anti-corrosion projects ; Excellent resistance to organic solvents, and the coating film has excellent electrochemical anti-corrosion performance; can be continuously used at high temperature up to 650 ° C, can be welded, cut, and cut well; low resistivity can be anti-static, anti-radiation, UV-resistant, Salt spray resistance and long-term anti-corrosion effect; the flexibility of this product is better than that of general inorganic zinc-rich coatings.

Description

technical field [0001] The invention relates to the technical field of paint making, in particular to an environment-friendly and high-efficiency water-based primer. Background technique [0002] Most of the metal components are made of carbon steel, manganese steel, cast steel and other materials, and they are in the environment of alternating dry and wet, sunlight exposure, high-speed water flow, salt spray, water medium, and microbial adhesion for a long time, and different degrees of corrosion generally occur. The time depends on the degree of anti-corrosion treatment to prolong its service life. General anti-corrosion coatings, such as: chlorinated rubber, iron red epoxy, epoxy and other coatings only have shielding effect. Thermal spraying of zinc and aluminum is sprayed on the metal substrate after melting and atomizing the wire rod, which has residual stress, high porosity, and poor shielding performance, so a sealing coating must be added, and the zinc mist generat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D5/12
Inventor 王骏冯友援陈国清李云松
Owner WUHAN FUMAISHI NEW MATERIAL CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com