Quick drying conductive anticorrosion paint for oil tank and method for preparing same

A conductive anti-corrosion, oil tank technology, applied in anti-corrosion coatings, conductive coatings, coatings and other directions, can solve the problems of little research on anti-static anti-corrosion paint, increased static voltage, electrostatic charge accumulation, etc., to achieve easy mass production , The effect of fast drying and easy construction

Inactive Publication Date: 2010-02-10
WUXI HUHUANG PAINT
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is mainly used on the outer wall of oil tanks for anti-corrosion protection, but there is little research on anti-static anti-corrosion paints on the inner walls of oil tanks and pipelines. During the storage and transportation of oil products in oil pipelines and storage tanks, due to relative motion Static charge is generated by friction. If it is not discharged in time, the static charge will accumulate, which will increase the static voltage, and it is very easy to discharge and cause fire, explosion and other unsafe factors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A quick-drying conductive anticorrosion paint for oil tanks, comprising the following components in parts by weight:

[0051] Component A:

[0052] Aliphatic hexamethylene diisocyanate 12 parts

[0053] 2.5 parts of polybasic acid ester

[0054] Component B:

[0055] Bisphenol A type epoxy resin 40 parts

[0056] Mica-coated tin oxide 13 parts

[0057] 13 parts of light color material coated with zinc oxide and tin oxide

[0058] 20 parts of rutile titanium dioxide

[0059] 10 parts of polybasic acid ester

[0060] Basic urethane copolymer 1 part

[0061] Fluorinated silicone 1 part

[0062] 2 parts polysiloxane polyether copolymer

[0063] The production method is as follows:

[0064] Component A: Mix according to the formula ratio, 1200 rpm, 30min.

[0065] Component B:

[0066] 1. Add the bisphenol A type epoxy resin in the formula quantity, 8 parts of polybasic dibasic acid ester, the basic urethane copolymer in the formula quantity, the fluorinated sili...

Embodiment 2

[0071] A quick-drying conductive anticorrosion paint for oil tanks, comprising the following components in parts by weight:

[0072] Component A:

[0073] Aliphatic biuret 10 parts

[0074] S100 aromatic solvent 2 parts

[0075] Component B:

[0076] Bisphenol A type epoxy resin 35 parts

[0077] Mica-coated antimony oxide 10 parts

[0078] Zinc oxide-coated titanium oxide light coloring material 10 parts

[0079] Barium sulfate 15 parts

[0080] S100 aromatic solvent 7 parts

[0081] 2 parts polycarboxylic acid containing amine derivative

[0082] Fluorinated silicone 1 part

[0083] 2 parts polysiloxane polyether copolymer

[0084] The production method is as follows:

[0085] Component A: Mix according to the formula ratio, 1000 rpm, 20min.

[0086] Component B:

[0087] 1. Add the bisphenol A type epoxy resin in the formula quantity, 5.6 parts of S100 aromatic solvent, the amine derivative polycarboxylic acid in the formula quantity, the fluorinated silicone in t...

Embodiment 3

[0092] A quick-drying conductive anticorrosion paint for oil tanks, comprising the following components in parts by weight:

[0093] Component A:

[0094] Aliphatic hexamethylene diisocyanate 15 parts

[0095] S150 aromatic solvent 3 parts

[0096] Component B:

[0097] Bisphenol A type epoxy resin 45 parts

[0098] 15 parts of mica-coated tin oxide

[0099] Zinc oxide-coated tin oxide light coloring material 15 parts

[0100] Quartz powder 30 parts

[0101] S150 aromatic solvent 14 parts

[0102] Basic urethane copolymer 3 parts

[0103] Fluorinated silicone 2 parts

[0104] 3 parts polysiloxane polyether copolymer

[0105] The production method is as follows:

[0106] Component A: Mix according to the formula ratio, 1200 rpm, 30min.

[0107] 1. Add the bisphenol A type epoxy resin in the formula quantity, 11.2 parts of S150 aromatic solvent, the basic urethane copolymer in the formula quantity, the fluorinated silicone in the formula quantity and the polysilicon i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fast dry oil tank conductive anticorrosion paint which comprises the following components: component A: non-yellowing firming agent and environment friendly solvent; component B: macromolecular epoxy resin, conductive material I, conductive material II, anticorrosion pigment, environmental friendly solvent, dispersant, foam killer and flatting agent. When the paint is used, the weight mixing ratio of the component A and the component B is 1 to 8. The invention also provides a preparation method for the fast dry oil tank conductive anticorrosion paint. With low surfaceresistivity of 10<5>-10<8> Omega, the fast dry oil tank conductive anticorrosion paint of the invention is provided with good conductivity. The specific resin selection combination is provided with fast drying speed and good adhesion. The paint film is provided with heat resistance, acid and alkali resistance and good anticorrosion performance, and can prevent the oil tank from being rusted. Thefast dry oil tank conductive anticorrosion paint has advantages of anticorrosion performance for various chemical media, god oil resistance, easy construction, nontoxic performance and no environmental pollution. The light color of the paint film can be matched with light color paint with beautiful coating effect.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to a conductive anticorrosion paint for an oil tank with the advantage of quick drying and a preparation method thereof. Background technique [0002] With the rapid development of the national economy, the application of special coatings has been continuously developed, and various structural facilities, equipment materials and other surface engineering have put forward higher requirements for surface coatings. Therefore, high-performance special coatings have become the research object of major companies. [0003] Anti-corrosion coatings involve a wide range of fields and there are many varieties. Mainly alkyd resin, chlorinated rubber, epoxy, chlorosulfonated polyethylene coating, etc. It is mainly used on the outer wall of oil tanks for anti-corrosion protection, but there is little research on anti-static anti-corrosion paints on the inner walls of oil tanks and pipe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/02C09D5/24C09D5/08C09D7/12
Inventor 胡胜初牛清平孙小清
Owner WUXI HUHUANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products