Method for preparing brake block by calcium carbonate crystal whisker

A technology of calcium carbonate whiskers and brake pads, which is applied in the field of friction materials, and can solve the problems of easy stripping and shear force drop

Inactive Publication Date: 2008-06-25
信义集团公司
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the thermal ablation process can improve the recession to a certain extent, it cannot solve this problem, and the ablation is easy to cause other problems, such as: the shear force is reduced, easy to peel off; the uniformity of ablation; and Product consistency, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] For the problems existing in the prior art, according to the content of the invention, two groups of formulas (A formula and B formula) have been designed and tested. The experimental scheme and experimental results are as follows:

[0008] Formula A

Formula B

match

party

Group

to make

material name

parts by weight

material name

parts by weight

Nitrile modified phenolic resin

10

Silicon modified phenolic resin

12

steel fiber, aramid pulp

22

ceramic fiber, aramid pulp

28

iron oxide, aluminum oxide

5

Friction powder, aluminum oxide

10

graphite, copper sulfide

15

Graphite, copper sulfide, mica

10

calcium carbonate whiskers

10

calcium carbonate whiskers

10

Barium sulfate

35

Barium Sulfate, Potassium Titanate

40

tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a brake sheet through adopting calcium carbonate crystal whisker, belonging to the friction material field, wherein the following raw materials of corresponding part by weight are adopted: 5 to 15 portions of adhesive which adopts phenol formaldehyde resin, 20 to 30 portions of reinforcing material which is obtained through mixing steel fiber or ceramic fiber with one or several of aramid fiber, mineral fiber and glass fiber, 1 to 15 portions of grinding agent which comprises one or combination of several of aluminum sesquioxide, ferric oxide, magnesium oxide and friction powder, 5 to 15 portions of lubricant which comprises one or combination of several of graphite, molybdenum disulfide and mica, 5 to 15 portions of stabilizer calcium carbonate crystal whisker, and 30 to 50 portions of filler which comprises one or combination of several of barium sulfate, potassium titanate and magnesium oxide. The brake sheet, which is made through the method, can effectively increase porosity and improve the high-temperature resistance of material, thereby lowering the decomposition rate of organic material at a high temperature; meanwhile, the brake sheet can slow down the gaseous escape speed on a friction surface during fading, thereby reducing fading rate and the change rate of friction coefficient at high speed to less than 10 percent.

Description

technical field [0001] The invention relates to a method in which calcium carbonate whiskers are used for preparing brake pads in the field of friction materials. Background technique [0002] At present, the friction materials for automobiles in my country are dominated by semi-metals, which account for more than 70% of the total output. However, semi-metal friction materials have high product density, are easy to rust and scratch, and are prone to low-frequency noise during use. The disadvantage is that it can no longer meet people's higher and higher requirements for friction material products. Its upgraded product, ceramic-based friction material, overcomes the shortcomings of semi-metallic formula, has a stable friction coefficient, good braking comfort during use, and long service life, which has become the development trend of friction materials. In addition to binders, reinforcing fibers, and fillers, the basic composition of brake pads also has a very important clas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K3/14C08K7/08C08L61/14C08K3/26
Inventor 白克江张江山
Owner 信义集团公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products