Universal metallic surface silanization treating agent, preparation and use thereof

A silanization treatment, metal surface technology, applied in the direction of metal material coating process, etc., can solve problems such as failure to obtain large-scale application, economic and safety defects, system composition changes, etc., to improve practical application value, overcome Flammability and explosion hazard, strong resistance to salt spray

Inactive Publication Date: 2009-07-08
HUNAN UNIV
View PDF1 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the strong volatility and flammability of general alcohols, such as methanol, ethanol and propanol,
On the one hand, the volatilization of alcohol causes the composition of the system to change, causing the system to be unstable, and leads to a large amount of waste of alcohol; on

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1: Take 10 volumes of organic solvent chloroform, 5 volumes of silane coupling agent vinyl triethoxy silane, inject 100 volumes of deionized water with pre-adjusted pH into the silane main solution, mix them uniformly, and obtain a stable Complex phase system. The temperature of the system was controlled and reacted at 30°C for 4 hours to obtain an aqueous phase containing a suitable concentration of silanol and an oil phase containing an unhydrolyzed silane coupling agent. Treat the surface of the carbon steel sample with an alkaline cleaning agent in the temperature range of 60-70℃ for 5-30 seconds, rinse with deionized water, blow dry with compressed air, and directly immerse the pretreated metal in the water phase 5 minute. Take it out and dry it at 80°C for 30 minutes. In the simulated seawater solution, the corrosion rate is 0.0117mm / a measured by the corrosion electrochemical method, and the adhesion strength with the coating is measured by GB / T5210-85 "Metho...

Example Embodiment

[0020] Example 2: Take 10 volumes of organic solvent chloroform, 5 volumes of silane coupling agent γ-aminopropyltriethoxysilane, and pour 100 volumes of deionized water with pre-adjusted pH into the silane main solution and mix them evenly , To get a stable multiphase system. The temperature of the system was controlled to react for half an hour at 30°C to obtain an aqueous phase containing a suitable concentration of silanol and an oil phase containing an unhydrolyzed silane coupling agent. Treat the surface of the carbon steel sample with an alkaline cleaning agent in the temperature range of 60-70℃ for 5-30 seconds, rinse with deionized water, blow dry with compressed air, and directly immerse the pretreated metal in the water phase 5 minute. Take it out and dry it at 60°C for 50 minutes. In the simulated seawater solution, the corrosion rate is 0.092mm / a measured by the corrosion electrochemical method, and the adhesion strength with the coating is measured by GB / T5210-85 "Me...

Example Embodiment

[0021] Example 3: Take 10 volumes of organic solvent cyclohexane, 20 volumes of silane coupling agent γ-aminopropyltriethoxysilane, and 100 volumes of deionized water with pre-adjusted pH, and mix them evenly to obtain a stable multiphase system . The temperature of the system was controlled to react for half an hour at 55°C to obtain an aqueous phase containing a suitable concentration of silanol and an oil phase containing an unhydrolyzed silane coupling agent. Treat the surface of the carbon steel sample with an alkaline cleaning agent in the temperature range of 60-70°C for 5-30 seconds, rinse it with deionized water, and dry it with compressed air for later use. While stirring, add the filler, acrylic resin and initiator to the water phase and mix well. Using air as the carrier gas, spray the obtained uniform system on the pretreated metal surface and dry it at 80°C for 30 minutes. The thickness of the coating is about 0.1mm. In the simulated seawater solution, the corrosion ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Corrosion rateaaaaaaaaaa
Adhesive strengthaaaaaaaaaa
Corrosion rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a versatile metal surface silanization treating agent, a preparing method and an application thereof. The preparing method includes steps as follows: mixing an organic solvent with 5-20 volumes and an silane coupling agent with 5-20 volumes evenly for obtaining the silane main solution, injecting a pre-adjust PH value deionized water with 100 volumes into the silane main solution for obtaining composite mixing solution; controlling temperature of the composite mixing solution in 20-60 DEG C and hydrolysis during 0.5-12 hours; cooling to a room temperature, water phase is the metal surface silanization treating agent after the solution is layered; the organic phase can supply the silane coupling agent and uses repeatedly. The treating agent, the method and the application provided by the invention have advantages of lower cost, safe in utilization, simple manufacturing equipment, convenient for use and wide metal processing range, such as steel, galvanized steel, copper, zinc, aluminium, aluminium alloy and magnesium alloy. The method has better processing effect, strong ability of hydrolytic resistance, washing resistance and salt mist resistance, longer protective period for metal, and increases and enhances fact application value of the silanization treating technique, helps the development of the metal surface silanization treating technique industrialization.

Description

technical field [0001] The invention relates to a general metal surface silanization treatment agent and its preparation method and application. Background technique [0002] There are many reports on the metal surface pretreatment agent containing silane coupling agent, such as 200510127048.X discloses a chromium-free metal surface treatment agent, which is composed of a silicon-containing binder solution containing water and / or alcohol as a solvent , the concentration of its silica component is 8-25% by weight. In particular, a metal surface treatment agent comprising an alcohol solution of an alkoxysilane oligomer having a weight average molecular weight of 1,000-10,000 obtained through alkoxysilane hydrolysis and polycondensation reaction. However, there are still problems in the practical application of this surface treatment agent containing silane coupling agent containing water and / or alcohol. One of the problems is that the silanol solution formed after silane hyd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/05
Inventor 何德良王名浩崔正丹徐以兵舟舟
Owner HUNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap