Preparation method of aqueous vinylidene chloride base glue used in high-barrier plastic film

A vinylidene chloride, plastic film technology, applied in the direction of adhesives, etc., can solve the problems of weak adhesion, poor wettability, and cannot be used for high-barrier plastic film coating, etc., to achieve strong adhesion and good wettability. Effect

Inactive Publication Date: 2009-12-30
ANHUI UNIVERSITY +1
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that existing latex coatings cannot be used for high-barrier plastic film coatings due to poor wettability and weak cohesive force, the present invention provides a water-based vinylidene chloride primer for high-barrier plastic films Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The raw materials used in this embodiment are as follows:

[0025] Kettle material:

[0026] Deionized water 65Kg

[0027] Sodium alkyl sulfonate 0.5Kg

[0028] Tert-butyl hydroperoxide 0.004Kg;

[0029] Mixed monomer:

[0030] Vinylidene chloride (VDC) 85Kg

[0031] Methacrylic acid (MAA) 5Kg

[0032] 2-ethylhexyl acrylate (2-EHA) 10Kg;

[0033] Emulsifier: Alkylphenol polyoxyethylene ether (OP-35) 0.6Kg

[0034] 2-acrylamido-2-methylpropanesulfonic acid (AMPS) 0.3Kg

[0035] Deionized water 20Kg;

[0036] Initiator:

[0037] Initiator A: tert-butyl hydroperoxide 0.2Kg

[0038] Deionized water 10Kg

[0039] Initiator B: Diaphragm powder 0.2Kg

[0040] Deionized water 10Kg;

[0041] The preparation method of water-based vinylidene chloride primer for high-barrier plastic film comprises the following steps:

[0042] First add 65 kilograms of deionized water, 500 grams of sod...

Embodiment 2

[0054] The raw materials used in this embodiment are as follows:

[0055] Kettle material:

[0056] Deionized water 65Kg

[0057] Sodium alkyl sulfonate 0.5Kg

[0058] Tert-butyl hydroperoxide 0.004Kg;

[0059] Mixed monomer:

[0060] Vinylidene chloride (VDC) 75Kg

[0061]Itaconic acid 8Kg

[0062] Glycidyl methacrylate 17Kg;

[0063] Emulsifier: nonylphenol polyoxyethylene ether (NP-40) 0.4Kg

[0064] 2-acrylamido-2-methylpropanesulfonic acid (AMPS) 0.1Kg

[0065] Deionized water 20Kg;

[0066] Initiator:

[0067] Initiator A: tert-butyl hydroperoxide 0.2Kg

[0068] Deionized water 10Kg

[0069] Initiator B: carving white powder 0.2Kg

[0070] Deionized water 10Kg;

[0071] The preparation method of the water-based vinylidene chloride primer for high-barrier plastic film is the same as in Example 1, and the quality data of the water-based vinylidene chloride primer of the gained is as follows:

[0...

Embodiment 3

[0079] The raw materials used in this embodiment are as follows:

[0080] Kettle material:

[0081] Deionized water 65Kg

[0082] Sodium alkyl sulfonate 0.5Kg

[0083] Tert-butyl hydroperoxide 0.004Kg;

[0084] Mixed monomer:

[0085] Vinylidene chloride (VDC) 80Kg

[0086] N-methylolacrylamide 7Kg

[0087] n-butyl acrylate 13Kg;

[0088] Emulsifier: nonylphenol polyoxyethylene ether (NP-35) 0.9Kg

[0089] 2-acrylamido-2-methylpropanesulfonic acid (AMPS) 0.6Kg

[0090] Deionized water 20Kg;

[0091] Initiator:

[0092] Initiator A: tert-butyl hydroperoxide 0.2Kg

[0093] Deionized water 10Kg

[0094] Initiator B: carving white powder 0.2Kg

[0095] Deionized water 10Kg;

[0096] The preparation method of the water-based vinylidene chloride primer for high-barrier plastic film is the same as in Example 1, and the quality data of the water-based vinylidene chloride primer of the gained is as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of aqueous vinylidene chloride glue used in a high-barrier plastic film. The preparation method comprises the following steps: taking cheap and available vinylidene chloride as a main comonomer, and selecting the vinylidene chloride, polymerizable functional monomer, acrylic monomer and part of unsaturated fatty acid to be copolymerized in the presence of various emulsifiers by seeded semi-continuous emulsion polymerization to obtain an aqueous vinylidene chloride adhesive with good property. When the base glue is applied to the bottom layer of the plastic film (polypropylene, polyethylene, polyester and polyamide), the base glue has the advantages of good wettabilityand strong cohesive force, and the base glue is especially suitable for replacing a polyurethane adhesive as the base glue when coating the high-barrier plastic film.

Description

technical field [0001] The invention relates to a water-based vinylidene chloride adhesive used as a primer when coating a high-barrier plastic film. Background technique [0002] Adhesives for plastic films are usually based on solvent-based polyurethane adhesives. In recent years, people's attention has focused on the toxicity, flammability and pollution of the product. It is hoped that the adhesive used is a non-toxic, non-flammable and non-polluting green product dispersed in water. Due to the emphasis on environmental protection and personal health, a lot of research has been carried out on water-based adhesives at home and abroad, but the research mainly focuses on acrylic water-based adhesives. [0003] Patent CN 1223618C discloses the preparation and coating method of latex paint for disposable paper tableware. Patent CN1986583A relates to a special water-based PVDC latex for coating on special cloth and its preparation method. Patent CN 1294326C discloses a beverag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J127/08
Inventor 杨建军吴庆云张建安吴明元瞿贤超崔国庭
Owner ANHUI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com