Nickel-based welding rod for AC welding

A nickel-based electrode and welding core technology, applied in welding medium, welding equipment, welding/cutting medium/material, etc., can solve arc stability and poor slag coverage, poor weld shape, low content of diffusible hydrogen, etc. problems, to achieve the effect of smooth electrode surface, good slag detachability, and excellent thermal crack resistance

Inactive Publication Date: 2010-06-23
LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This coating type electrode has good slag removal and low diffusible hydrogen content, but the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031]The coating used in the electrode of the invention is mainly carbonate, fluoride and alloy, and a small amount of silicate and pressure-improving substances are added at the same time. The components and their mass parts are as follows: marble: 40, potassium titanate: 5, fluorite: 28, barium fluoride 2, bentonite: 3, zircon sand: 1, soda ash 2, manganese metal: 1, ferrosilicon : 7, aluminum-magnesium alloy: 1, barium carbonate 10.

[0032] The deposited metal composition is: C: 0.034%, S: 0.004%, P: 0.01%, Si: 0.03%, Mn: 1%, Fe: 7.8%, W: 2.7%, Mo: 18.8%, and the balance is Ni .

[0033] After mixing the raw materials of the coating above evenly, add potassium-sodium water glass of 43-48 Be at 20°C, accounting for 23-28% of the mass content of the solid component, for wet mixing. Nickel alloy welding wire is used as the welding core, and the welding rod is prepared on the hydraulic welding rod production equipment by conventional technology.

Embodiment 2

[0035] Others are the same as in Example 1, but the composition in parts by mass of the coating is as follows: marble: 46, potassium titanate: 3, fluorite: 23, barium fluoride 5, bentonite: 2, zircon sand: 2, soda ash 1.5, metal Manganese: 1.5, ferrosilicon: 4, aluminum-magnesium alloy: 4, barium carbonate 8.

Embodiment 3

[0037] Others are the same as in Example 1, but the composition of the coating is as follows: marble: 50, potassium titanate: 2, fluorite: 20, barium fluoride 7, bentonite: 1.5, zircon sand: 3, soda ash 1, metal Manganese: 3, ferrosilicon: 3, aluminum-magnesium alloy: 2.5, barium carbonate 7.

[0038] During AC welding, the electrodes of Examples 1-3 have stable arc, basically no spatter, good slag detachability, and excellent operation performance of the electrode; the shape of the weld seam is beautiful, and the height of the weld bead is moderate. The mechanical properties of deposited metal are: R P0.2 : 515Mpa, Rm: 765Mpa, A: 37.5%, Z: 41.5%, A at -196°C KV : 102J. The foreign ENi1008 electrode is AC welding, but its slag coverage is not good, and the price is very high; abroad, only Japan Kobelco provides an example value, and its -196°C impact value is 83J, while the average -196°C impact value of this example reaches 102J outperformed it by 22%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of welding materials, in particular to a nickel-based welding rod for AC welding, the welding rod adopts a high-nickel alloy welding wire which is in line with the requirements of GB/T13814-2008 on ENi1008 ingredients as a welding core, and a drug paper comprises the following components: 40-50% of marble, 2-5% of potassium titanate, 20-28% of fluorite, 2-7% of barium fluoride, 1.5-3% of bentonite, 1-3% of zircon sand, 1-2% of soda ash, 1-3% of metal manganese, 3-7% of ferrosilicon containing 43.0-47.0% of Si, 1-3% of magnesium alloy containing 47-53% of Al and 7-10% of barium carbonate. When in welding, the welding rod can realize stable arc, almost no spatter, good slag detachability and excellent operating performance of the welding rod; and the shape of a weld seam is beautiful, and a wetting angle of the weld seam is moderate.

Description

technical field [0001] The invention relates to a technology in the field of welding materials, in particular to a nickel-based welding rod for AC welding. Background technique [0002] With the development of industry, the application of 9% Ni steel is more and more extensive. 9% Ni steel is a low-carbon martensitic low-temperature steel with good low-temperature toughness, good welding performance and other special properties. For example, it is used as a non-magnetic steel in superconducting engineering and nuclear fusion engineering. At present, 9% Ni steel is mainly used as steel for liquefied natural gas or liquid nitrogen cryogenic vessels and is widely used by countries all over the world. [0003] As the application range of 9% Ni steel becomes wider and wider, the demand for supporting welding materials for 9% Ni steel is increasing. There are three main types of supporting welding materials for 9% Ni steel: [0004] (1) Inconel type with a Ni content of about 6...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/36
Inventor 黄连涛刘鹏飞张晓吴伦发
Owner LUOYANG SHUANGRUI SPECIAL ALLOY MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap