Odorless ethylene propylene diene monomer rubber waterproof coating and preparation method thereof

A technology of EPDM rubber and waterproof coating is applied in the field of architectural waterproof coating, which can solve the problem of uneven thickness, and achieve the effects of increasing anti-corrosion performance, improving performance and improving elongation.

Inactive Publication Date: 2011-02-09
北京立高科技股份有限公司
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides an EPDM odorless waterproof coating and a preparation method thereof, which solves the technical pro...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Embodiment 1, this EPDM odorless waterproof coating includes dry raw materials and solvents, and the optimal proportioning of the dry raw materials with the total mass parts of the coating is as follows:

[0054] 100 parts of EPDM rubber;

[0055] 30 copies of SBR;

[0056] 60 copies of SBS;

[0057] 60 parts of terpene resin;

[0058] 5.5 parts of nano zinc oxide;

[0059] 55 parts of nano calcium carbonate;

[0060] 6.3 parts of nano titanium dioxide;

[0061] Described solvent is as follows with coating gross mass part proportioning:

[0062] 185 parts of odorless solvent;

[0063] 260 parts of benzene-free solvent.

[0064] One or more mixtures of leveling agent, dispersant, defoamer, thickener, antifreeze or preservative can also be added to the dry raw material.

[0065] The odorless solvent is an alkane solvent with a distillation range of 120-130 degrees.

[0066] The benzene-free solvent is methyl isopropyl ketone, methyl isobutyl ketone, isopropyl aceto...

Embodiment 2

[0068] Embodiment two, this EPDM odorless waterproof coating includes dry raw materials and solvents, and the proportioning of the dry raw materials in total mass parts of the coating is as follows:

[0069] 80 parts of EPDM rubber;

[0070] 35 copies of SBR;

[0071] 70 copies of SBS;

[0072] 50 parts of terpene resin;

[0073] 3 parts of nano zinc oxide;

[0074] 45 parts of nano calcium carbonate;

[0075] 4 parts of nano titanium dioxide;

[0076] Described solvent is as follows with coating gross mass part proportioning:

[0077] 160 parts of odorless solvent;

[0078] 280 parts of benzene-free solvent.

[0079]

Embodiment 3

[0080] Embodiment three, this EPDM odorless waterproof coating includes dry raw materials and solvents, and the proportioning of the dry raw materials in total mass parts of the coating is as follows:

[0081] 120 parts of EPDM rubber;

[0082] 25 copies of SBR;

[0083] 50 copies of SBS;

[0084] 70 parts of terpene resin;

[0085] 7 parts of nano zinc oxide;

[0086] 65 parts of nano calcium carbonate;

[0087] 10 parts of nano titanium dioxide;

[0088] Described solvent is as follows with coating gross mass part proportioning:

[0089] 200 parts of odorless solvent;

[0090] 220 parts of benzene-free solvent.

[0091]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a odorless ethylene propylene diene monomer (EPDM) rubber waterproof coating and a preparation method thereof. The coating comprises the following dry materials by the total mass parts of the coating: 80-120 parts of EPDM rubbers, 25-35 parts of SBR, 50-70 parts of SBS, 50-70 parts of terpene resins, 3-7 parts of nanometer zinc oxide, 45-65 parts of nanometer calcium carbonate, 4-10 parts of nanometer titanium dioxide, 155-215 parts of odorless solvent and 200-300 parts of non-toluene solvent. Three kinds of nanoparticles are added to the coating, and through scientific proportioning, the fillers can be uniformly dispersed in the solvents with the rubbers, thus solving the precipitation problem of the coating and greatly improving intermixing. The content of solid in the coating is improved from 40% to 48%, thus the coating is easy to be thicker during construction. The waterproof coating also has the functions of ozone decomposing, sterilizing and self-cleaning. After the odorless solvent is added, the product has the characteristic of odorlessness and is more environment-friendly, and the quality of the product is further ensured.

Description

technical field [0001] The invention relates to a building waterproof coating, in particular to a waterproof coating added with nanometer materials and a preparation method thereof. Background technique [0002] Waterproof coating is a new material widely used in industrial and civil buildings after asphalt waterproofing and mortar waterproofing. In solvent-based waterproof coatings with synthetic rubber as the main film-forming material, the tensile strength and crack resistance of the coating film are important factors affecting the performance of the coating. The existing EPDM waterproof coating has a relatively single formula, and the coating's own performance, bactericidal performance, and environmental protection performance all need to be improved. [0003] Although the existing acrylic waterproof coatings added with nanoparticles aim to improve the performance of the coating and enhance its bactericidal effect, the calcium carbonate and talcum powder added in a larg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D109/06C09D7/12C09D123/16C09D145/00C09D153/02
Inventor 段霓华王政昌曹海涛房文静
Owner 北京立高科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka