Temperature-resistance thermal-insulation heavy-duty anticorrosion coating

A heavy-duty anti-corrosion and coating technology, applied in anti-corrosion coatings, coatings and other directions, can solve problems such as affecting the adhesion of thermal insulation coatings, uneven paint film, etc., to achieve good thermal insulation, excellent anti-corrosion, and improved media resistance. Effect

Inactive Publication Date: 2011-07-27
SHANGHAI HILONG SHINE NEW MATERIAL
View PDF9 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned heat-insulating coatings one does not mention the important index of thermal conductivity; the other is that hollow glass beads are used in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A heat-resistant heat-insulating heavy-duty anti-corrosion coating, the mass percentage of its raw material composition is:

[0043] Epoxy-modified silicone 25%, can use the products of Jiangsu Sanmu Group or Dow Corning or Degussa or Changzhou Jianuo Silicone Co., Ltd. or Wacker Chemical Company;

[0044] Novolac epoxy resin 8%, adopt 438 of Dow Chemical Company or 638S product of Nanya Epoxy Resin Co., Ltd.;

[0045] Modified amine curing agent 12%, using the products of American Cardolite company;

[0046] Modified polysiloxane leveling agent 0.7%, using the product model 435 of Deqian (Shanghai) Chemical Company;

[0047] Polysiloxane defoamer 0.01%, using the product of Deqian (Shanghai) Chemical Company model 6800;

[0048] Polyacrylate dispersant 0.5%, adopt BYK company model BYK-354 product;

[0049] Toughening agent 3%, using one or more of nitrile rubber, polysulfide rubber, epoxy-terminated polyurethane, etc.;

[0050] Zinc phosphate 6.77%, its chemical f...

Embodiment 2

[0061] A heat-resistant heat-insulating heavy-duty anti-corrosion coating, the mass percentage of its raw material composition is:

[0062] Epoxy modified silicone 20%;

[0063] Novolak epoxy resin 10%;

[0064] Modified amine curing agent 10%;

[0065] Modified polysiloxane leveling agent 1%;

[0066] Polysiloxane defoamer 0.05%;

[0067] Polyacrylic acid dispersant 1%;

[0068] Toughener 6%;

[0069] Zinc phosphate 7.9%;

[0070] Carbon black 0.05%;

[0071] Barite powder 4%;

[0072] Titanium dioxide 7%;

[0073] Potassium titanate whiskers 28%;

[0074] Nanoporous substance 5%; The sources of the above raw materials are the same as in Example 1.

[0075] The preparation steps of the above-mentioned heat-resistant and heat-insulating heavy-duty anti-corrosion coating are the same as in Example 1.

Embodiment 3

[0077] A heat-resistant heat-insulating heavy-duty anti-corrosion coating, the mass percentage of its raw material composition is:

[0078] Epoxy modified silicone 15%;

[0079] Novolak epoxy resin 15%;

[0080] Modified amine curing agent 6%;

[0081] Modified polysiloxane leveling agent 0.5%;

[0082] Polysiloxane defoamer 0.08%;

[0083] Polyacrylic acid dispersant 0.8%;

[0084] Toughener 9%;

[0085] Zinc phosphate 8%;

[0086] Carbon black 0.01%;

[0087] Barite powder 7%;

[0088] Titanium dioxide 6%;

[0089] Potassium titanate whiskers 18.61%;

[0090] Hollow glass microsphere 14%; The source of above-mentioned raw material is with embodiment 1.

[0091] The preparation steps of the above-mentioned heat-resistant and heat-insulating heavy-duty anti-corrosion coating are the same as in Example 1.

[0092] The performance index of a kind of heat-resistant and heat-insulating heavy-duty anti-corrosion coating of the present invention and coating is shown in th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of coating, in particular to temperature-resistance thermal-insulation heavy-duty anticorrosion coating, which comprises the following raw material components in percentage by mass: 10 to 40 percent of epoxy modified organosilicon resin, 5 to 20 percent of novolac epoxy resin, 8 to 20 percent of modified amine curing agent, 2 to 10 percent of flexibilizer, 0.1 to 1 percent of modified polysiloxane flatting agent, 0.01 to 0.1 percent of polysiloxane defoaming agent, 0.1 to 1 percent of polyacrylate dispersant, 4 to 11 percent of zinc phosphate, 4 to 10 percent of barite powder, 3 to 8 percent of titanium white, 0.01 to 0.1 percent of carbon black, 15 to 40 percent of potassium titanate whiskers and 2 to 20 percent of nano porous material. The organosilicon-modified epoxy resin adopted by the invention combines the high performance of epoxy resin and organosilicon resin, and the organosilicon-modified epoxy resin and the novolac epoxy resin compensate for respective defects. The coating has high anticorrosion performance, high high-temperature-resistance performance and high insulating performance, and the adhesion force, medium-resistance performance and thermal-insulation and heat-preservation performance of the coating are improved considerably.

Description

technical field [0001] The invention relates to the technical field of coatings in chemical technology, in particular to a heat-resistant, heat-insulating and heavy-duty anti-corrosion coating. Background technique [0002] Heat insulation coating is an effective means of heat insulation, and its research originated from the need for aircraft temperature control. Now, the application of thermal insulation coatings in the petroleum industry (used for oil storage equipment and the casing of transportation pipelines) has achieved good results. It reduces the volatilization of oil products and ensures the safety of storage tanks. However, high temperature resistant and heat insulating paint is a special kind of paint, which not only has the characteristics of general paint, but also has the functions of high temperature resistance and heat insulation. Due to the development of new technologies and the increase in demand, people have put forward higher and higher requirements fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/00C09D163/04C09D7/12C09D5/08
Inventor 杨铭方军锋粟鹰任飙
Owner SHANGHAI HILONG SHINE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap