Production method of vacuum insulation wall thermal insulation board by using expanded vitrified microspheres

A technology of expanding vitrified microbeads and production methods, which is applied to chemical instruments and methods, thermal insulation, insulation improvement, etc., can solve the problems of low cost, easy to burn, etc., and achieve the effects of easy construction, long weather resistance, and no discharge of three wastes

Active Publication Date: 2011-12-28
潍坊三强集团有限公司
View PDF7 Cites 56 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] After the 1980s, the world's climate became warmer and energy sources were increasingly exhausted. Under the dual pressures of environmental protection and energy sources, new requirements were brought to external wall insulation, which required both good thermal insulation performance and high flame retardancy. External wall insulation materials are mainly organic materials such as polystyrene and polyurethane. These materials have good thermal insulation performance and construction performance, and the cost is relatively low. However, these materials have fatal shortcomings and are easy to burn. The combustion performance is B2

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A production method for producing a vacuum insulation wall insulation board by using expanded vitrified microbeads, comprising the following contents:

[0021] a. With a bulk density of 80-100kg / m3, a floating rate of 95%, a spherical vitrification rate of 90%, a water absorption rate of 45%, and a particle size of 0.2mm, 60 parts of expanded vitrified microbeads, 5 parts of 12mm glass fibers, Put 10 parts of silica fume, 5 parts of bentonite, and 1 part of getter into the drum stirring tank, and then slowly and evenly add 2 parts of 890 wetting agent and 17 parts of ethylene-vinyl acetate emulsion during the stirring process to prevent local agglomeration and stir Paste material;

[0022] b. Evenly spread the stirred paste material on the microwave baking line according to the thickness of 10mm for baking, and cut the board into pieces after the moisture content of the board is below 1%;

[0023] c. Put the cut plate into a vacuum machine assembly line to vacuum, and ...

Embodiment 2

[0027] A production method for producing a vacuum insulation wall insulation board by using expanded vitrified microbeads, comprising the following contents:

[0028] a, with a bulk density of 100-120kg / m3, a floating rate of 90%, a spherical vitrification rate of 95%, a water absorption rate of 40%, and a particle size of 60 parts of expanded vitrified microbeads of 1mm, 5 parts of 12mm glass fibers, silicon Put 10 parts of ash, 5 parts of bentonite, and 1 part of getter into the drum stirring tank, and then slowly and evenly add 2 parts of X-405 wetting agent and 17 parts of acrylic emulsion during the stirring process to prevent local agglomeration and stir to form a paste shape material;

[0029] b. Evenly spread the stirred paste material on the microwave baking line according to the thickness of 15mm for baking, and cut the board into pieces after the moisture content of the board is below 1%;

[0030] c. Put the cut plate into a vacuum machine assembly line to vacuum, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method for producing a heat insulation board for a vacuum heat insulation wall body by utilizing small expanded and vitrified balls, and the method comprises the following steps: putting the small expanded and vitrified balls, glass fiber, silica fume, bentonite and a getter into a stirring kettle, adding a wetting agent and a bonding agent, and stirring for forming a paste-like material; uniformly spreading the well stirred paste-like material on a micro-wave baking line according to the required thickness for baking, and further cutting into blocks when the water content in the board is below 1%; further placing the board which is cut into the blocks on a vacuum machine assembly line and vacuum pumping till the vacuum degree is below 200Pa; and cutting and packaging the heat insulation board for the vacuum heat insulation wall body. By applying the method provided by the invention for production, the process is simple, the emission of three wastes can be avoided, the produced heat insulation board for the vacuum heat insulation wall body is easy to construct, the fireproof property can be realized, the heat insulation board for the vacuum heat insulation wall body can play great roles in heat preservation and heat insulation, the combustion performance is grade A, the weight is light, the weather-resistant time is long, and the service life can be above 30 years.

Description

technical field [0001] The invention relates to a method for producing a vacuum heat insulation wall insulation board by using expanded vitrified microspheres and other heat insulation materials, and belongs to the technical field of building material production. Background technique [0002] Vacuum insulation panel is a kind of vacuum insulation material, which is composed of filling core material and vacuum protection surface layer. It can effectively avoid heat transfer caused by air convection, so the thermal conductivity can be greatly reduced, less than 0.006w / m.K, And it does not contain any ODS materials, and has the characteristics of environmental protection and high efficiency and energy saving. It is currently the most advanced high-efficiency thermal insulation material in the world. Compared with traditional insulation materials, vacuum insulation panels can meet the same thermal insulation technical requirements, and have the advantages of thin layer, small si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/80E04B1/94C04B26/04B28C7/04B28C5/00B28B1/00
CPCY02B80/12Y02A30/242Y02B80/10
Inventor 王海林胥帅
Owner 潍坊三强集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap