Flame retardant smoke-suppression type humidity controlling functional coating and preparation method thereof

A functional coating and smoke-suppressing technology, which is applied in the coating and other directions, can solve the problems of poor scrub resistance and low strength

Inactive Publication Date: 2012-04-11
TIANJIN UNIV
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example can add halogen salt in quicklime and make inorganic moisture-regulating coating ([1] Gu Xupeng, the development of the health-care type coating that automatically adjusts indoor humidity, Applied Science and Technology, 2000, 27 (6): 8-29; [2] ] Li Qingwen, the preparation method of interior wall coating, Chinese patent, CN1624050A), but the strength of this type of coating is low, and scrub resistance is not good; Also can add diatomite, sepiolite, attapulgite in organic polymer coating , zeolite powder, kaolin and other one or several inorganic mineral humidity control components, but the humidity control performance of this kind of humidity control coating still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Rinse the purchased hydrotalcite raw material with deionized water and let it stand for 2 hours; dissolve hydrotalcite and sodium methacryl sulfonate in N,N'-dimethylacetamide organic solvent in a mass ratio of 3:2 , and fully stirred for 24h under the condition of heating to 78°C. Afterwards, the reaction solution was taken out, suction filtered, washed, vacuum-dried at 70° C. for 24 hours, ground and pulverized to obtain the organically modified hydrotalcite.

[0027] (2) Prepare a NaOH aqueous solution with a mass fraction of 25%, and slowly drop the metered NaOH solution into acrylic acid under ice-water bath conditions to obtain an acrylic acid-sodium acrylate solution with a neutralization degree of 70%; then press the sum of the mass of acrylic acid and sodium acrylate The mass ratio of acrylamide to acrylamide is 1:1. Add acrylamide into the above solution to prepare a monomer solution. Then, organically modified hydrotalcite with 2% mass of the monomer sol...

Embodiment 2

[0032] (1) Rinse the purchased hydrotalcite raw material with deionized water and let it stand for 2 hours; dissolve hydrotalcite and sodium methacryl sulfonate in N,N'-dimethylacetamide organic solvent in a mass ratio of 3:2 , and fully stirred for 24h under the condition of heating to 78°C. Afterwards, the reaction solution was taken out, suction filtered, washed, vacuum-dried at 70° C. for 24 hours, ground and pulverized to obtain the organically modified hydrotalcite.

[0033] (2) preparation mass fraction is the NaOH aqueous solution of 25%, under ice-water bath condition, metering NaOH solution is slowly dripped in acrylic acid, obtains the acrylic acid-sodium acrylate solution of 80% neutralization degree; Then press the sum of acrylic acid and sodium acrylate and The mass ratio of acrylamide is 5:1. Add acrylamide into the above solution to prepare a monomer solution. Then, organically modified hydrotalcite with 4% mass of the monomer solution was added into the monom...

Embodiment 3

[0037] (1) Rinse the purchased hydrotalcite raw material with deionized water and let it stand for 2 hours; dissolve hydrotalcite and sodium methacryl sulfonate in N,N'-dimethylacetamide organic solvent in a mass ratio of 3:2 , and fully stirred for 24h under the condition of heating to 78°C. Afterwards, the reaction solution was taken out, suction filtered, washed, vacuum-dried at 70° C. for 24 hours, ground and pulverized to obtain the organically modified hydrotalcite.

[0038] (2) preparation mass fraction is the NaOH aqueous solution of 25%, under ice-water bath condition, metering NaOH solution is slowly dripped in acrylic acid, obtains the acrylic acid-sodium acrylate solution of 90% neutralization degree; Then press the sum of acrylic acid and sodium acrylate and Acrylamide was added to the above solution at a mass ratio of 9:1 to prepare a monomer solution. Then, organically modified hydrotalcite with a mass of 8% of the monomer solution was added into the monomer so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame retardant smoke-suppression type humidity controlling functional coating and a preparation method thereof. The preparation method comprises the following steps of: firstly, preparing a hydrotalcite / poly(sodium acrylate-acrylamide) intercalation composite material component having high humidity capacity, humidity controlling ability and flame retardant property by areversed phase suspension polymerization method; and then adding the intercalation composite material component to styreneacrylate emulsion, inorganic stuffing, auxiliaries and water, and performing thorough stirring and mixing and even dispersion, thereby obtaining the inner wall coating having flame retardant, smoke suppressing and humidity controlling functions. The technical proposal of the invention provides the coating for an indoor building with the flame retardant and smoke suppressing properties and also the environmental humidity controlling function, thereby meeting the requirements of people for the environment comfort, the air quality and the fire-proof safety of the indoor buildings.

Description

technical field [0001] The invention relates to an interior wall coating and a preparation method thereof, in particular to a fire-retardant and smoke-suppressing humidity-regulating functional coating and a preparation method thereof. Background technique [0002] Interior wall paint is an essential building material required for building interior decoration. It is often coated on the surface of interior walls, ceilings, decorative wood panels, furniture and steel structural parts. With the advancement of science and technology and the improvement of people's living standards, people have higher and higher requirements for the comfort, air quality and safety of the indoor building environment, so building materials have gradually begun to "composite, multi-functional, and environmentally coordinated" direction of development. [0003] Like temperature, air humidity is also one of the important environmental parameters that affect the comfort of the indoor environment. A s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D133/02C09D133/26C09D7/12C09D5/00
Inventor 王吉会董飞张梦龙任曙凭
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com