Low-Ag-content Pb-RE-Ag alloy electrode

An alloy electrode, pb-re-ag technology, applied in the field of electrochemistry, can solve the problems of easy crusting of anode slime, alloy phase, structure difficult to control, and decrease of cathode current efficiency, so as to improve mechanical properties and corrosion resistance , Improve the mechanical strength and electrochemical performance, and improve the effect of mechanical properties

Inactive Publication Date: 2012-06-20
CENT SOUTH UNIV
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of these electrodes have the following problems: (1) Poor mechanical properties, easy to creep and flex, causing cathode and electrode short circuit, resulting in a decrease in cathode current efficiency and serious local corrosion of the electrode; (2) High oxygen evolution potential of the electrode, making the electrode (3) The electrode corrosion rate is high, and the corrosion products pollute the electrochemical process products
The above-mentioned Pb alloy grid for lead-acid storage battery mainly plays the role of active material carrier and current collector, and is compatible with metal electrodeposition, wastewater treatment, electroplating, organic electrosynthesis in terms of function, performance index, alloy composition and manufacturing process, etc. There is a significant difference in the Pb alloy electrodes used
In the above-mentioned electrodes for electrodeposition, the alloys used are all based on Pb-Ag alloys, and other alloying elements such as Ca, Al, Sn, Cr and Co are added to the basis of traditional Pb-Ag alloys, in an attempt to further improve the Pb-Ag alloy. The performance of the alloy electrode may partially reduce the Ag content, but there are some performance improvements w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Firstly, metal lead and rare earth are placed in a vacuum electromagnetic induction melting furnace to prepare a lead rare earth master alloy Pb-La (4wt.%) with high rare earth content. Then Pb-La(4wt.%), Ag and Pb were melted and cast together to form Pb-La(0.001wt.%)-Ag(0.6wt.%) alloy electrode, the alloy is relatively Pb-Ag(0.8wt.%) ) alloy electrode in the zinc electrowinning process, the oxygen evolution potential is reduced by 20mV, the corrosion rate is reduced by 18%, and the tensile strength is increased by 30%.

Embodiment 2

[0033] Firstly, metallic lead and corresponding rare earths were smelted in a vacuum electromagnetic induction melting furnace to prepare lead rare earth master alloys Pb-Sm (2wt.%), Pb-Er (2wt.%) and Pb-Ce (2wt.%). Pb-Sm(2wt.%), Pb-Er(2wt.%), Pb-Ce(2wt.%), Ag and pure Pb were melted and cast together into Pb-Ce(0.9wt.%)-Er(0.5wt.%) .%)-Sm(0.6wt.%)-Ag(0.001wt.%) rolled alloy electrode. The life of the electrode can reach 3 years when it is used in the process of treating wastewater containing aromatic organic substances.

Embodiment 3

[0035] Firstly, metallic lead and corresponding rare earths were smelted in a vacuum electromagnetic induction melting furnace to prepare Pb-Nd (1.0wt.%) and Pb-Gd (0.5wt.%) master alloys respectively. Melting and casting the above alloy together with Ag, Bi and Pb into:

[0036]Pb-Nd(0.3wt.%)-Gd(0.05wt.%)-Bi(0.05wt.%)-Ag(0.4wt.%) alloy electrode. The combination is applied in the electro-galvanizing industry, and compared with Pb-Ag (0.8wt.%), the electrode corrosion rate is reduced by 81%, the anode potential is reduced by 60mV, and the content of impurity elements in the plating layer of the plated parts is reduced by 51%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A low-Ag-content Pb-RE-Ag alloy electrode comprises (by weight percentage) rare earth (RE) 0.001-2.0, silver (Ag) 0.001-0.6 and lead in balance. RE is selected from at least one of La, Ce, Nd, Sm, Eu, Tb, Dy, Ho, Er, Dm, Yb, and Lu, and the total RE content is 0.001wt.%-2.0wt.%. With the invention, alloy has low cost, high mechanical strength, good corrosion resistance, and good electrochemical property, can find wide application in fields including metal electrodeposition, electroplating, wastewater treatment and organic electrosynthesis, and is suitable for industrial application.

Description

technical field [0001] The invention belongs to the technical field of electrochemistry, and in particular relates to a Pb-RE-Ag alloy electrode with low silver content. Background technique [0002] The use of lead alloy electrodes has a history of hundreds of years. Because it can form an oxide film on the surface and has corrosion resistance, it is widely used in electrolytic deposition, electroplating, wastewater treatment, organic electrosynthesis and other fields. [0003] Lead alloy electrodes need to have the following properties, (1) good electrical conductivity; (2) strong corrosion resistance; (3) good mechanical strength and processing performance; (4) long life; catalytic performance. [0004] At present, Pb-Ca, Pb-Sn, Pb-Sb, Pb-Ag, Pb-Ag-Co, Pb-Ca-Al-Sn, Pb-Ag-Ca-Sr, Pb-Ag-Ca-Al have been developed successively -Sn-RE and other alloy electrodes. However, most of these electrodes have the following problems: (1) Poor mechanical properties, easy to creep and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25B11/04
Inventor 赖延清蒋良兴钟晓聪洪波吕晓军郝科涛桂俊峰于枭影李劼刘业翔
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap