Hot melt adhesive membrane for bonding bi-metallic composite plate and preparing method thereof
A hot-melt adhesive film, composite board technology, applied in the direction of adhesives, adhesive types, ester copolymer adhesives, etc., can solve the problems of poor bonding strength, water resistance and salt spray aging resistance, etc. The effect of durable bonding, high peel strength and simple bonding process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1
[0027] Mix 10% acrylate rubber, 10% polyethylene-acrylic acid, 30% chlorinated polyethylene, 20% rosin, and 30% calcium carbonate with a high-speed mixer and extrude at 150°C with an extruder Pelletizing, stretching, pulling, and winding through a casting machine to form a 0.15mm thick hot melt adhesive film. The 180° peel strength, water resistance, salt spray resistance, and weather resistance of the film to metal Al / Al, Cu / Cu, and stainless steel were investigated. The specific test results are shown in Table 1.
Example Embodiment
[0028] Example 2
[0029] Mix 20% of acrylic rubber, 30% of polyethylene-butyl acrylate, 20% of polymethyl methacrylate, 15% of maleic rosin, and 15% of white carbon black with a high-speed mixer. It is extruded and granulated at 180°C out of the machine, and then stretched, drawn, and wound by a casting machine to form a 0.15mm thick hot melt adhesive film. The 180° peel strength, water resistance, salt spray resistance, and weather resistance of the film to metal Al / Al, Cu / Cu, and stainless steel were investigated. The specific test results are shown in Table 1.
Example Embodiment
[0030] Example 3
[0031] Mix 30% polyethylene-acrylic acid, 30% polyethylene-methyl acrylate, 20% polyethylene-methyl acrylate-maleic anhydride copolymer, and 20% polyethylene with a high-speed mixer and extrude The machine is extruded and granulated at 150°C, and then stretched, drawn, and wound by a casting machine to form a 0.15mm thick hot melt adhesive film. The 180° peel strength, water resistance, salt spray resistance, and weather resistance of the film to metal Al / Al, Cu / Cu, and stainless steel were investigated. The specific test results are shown in Table 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap