Surface treatment process for reducing roughness of electrolytic copper foil

A technology of surface treatment and electrolytic copper foil, which is applied in the coating process of metal materials and printed circuit components, etc., can solve the problems of insufficient surface roughness, increased glue thickness, and decreased MIT performance, so as to reduce surface roughness , excellent resistance to normal temperature, good corrosion resistance and etching effect

Active Publication Date: 2014-11-19
SHANDONG JINBAO ELECTRONICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

LP copper foil for FPC, the tensile strength and elongation can generally be made relatively high, but the surface roughness is not low enough, which increases the thickness of the glue in FPC products, resulting in a sharp decline in MIT performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface treatment process for reducing roughness of electrolytic copper foil
  • Surface treatment process for reducing roughness of electrolytic copper foil
  • Surface treatment process for reducing roughness of electrolytic copper foil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In this embodiment, a surface treatment process for reducing the roughness of electrolytic copper foil, the process flow is:

[0033] LP wool foil-pickling-micro etching-nickel plating-zinc alloy-passivation-silane coupling agent-drying-VLP copper foil.

[0034] Using LP wool foil, the surface is pickled to remove the oxide layer; then a micro-etching solution composed of hydrochloric acid-copper sulfate is sprayed on the wool surface of the copper foil to react the "mountains" into tiny tumor-like particles; A layer of nickel-zinc alloy, a layer of chromium-zinc alloy; finally a layer of silane coupling agent is applied and dried.

[0035] The specific process steps are as follows:

[0036] 1) Pickling: Dilute industrial pure concentrated sulfuric acid to 10% dilute sulfuric acid by volume percentage, pump it into the pickling tank, and soak the copper foil in the pickling solution for 3S;

[0037] The purpose of pickling is to remove oxides on the surface of the electrolytic w...

Embodiment 2

[0049] A surface treatment process for reducing the roughness of electrolytic copper foil. The specific treatment conditions are as follows:

[0050] 1) Pickling: Dilute industrial pure concentrated sulfuric acid into dilute sulfuric acid with a concentration of 12% by volume, pump it into the pickling tank, and soak the copper foil in the pickling solution for 1S;

[0051] 2) Micro-etching: Dissolve copper sulfate pentahydrate with hot water (40°C), add industrially pure concentrated hydrochloric acid, and mix evenly to etch the rough surface (crystal growth surface) sprayed on the copper foil; the specific process conditions are : CuSO 4 240 g / L, HCl 30g / L, temperature 40℃, time 25s;

[0052] 3) Nickel-zinc alloy plating: dissolve nickel sulfate and zinc sulfate in water and mix them, add industrially pure concentrated sulfuric acid, and pump them into a nickel-zinc alloy plating tank for electroplating after mixing; the specific process conditions are: Zn 2+ 1.5 g / L, Ni 2+ 7 g / ...

Embodiment 3

[0057] A surface treatment process for reducing the roughness of electrolytic copper foil. The specific treatment conditions are as follows:

[0058] (1) Pickling: 15% sulfuric acid, 1S time;

[0059] (2) Micro-etching: CuSO 4 200 g / L, HCl 70g / L, temperature 35℃, time 40s;

[0060] (3) Nickel-zinc alloy plating: Zn 2+ 2.0 g / L, Ni 2+ 7 g / L, H 2 SO 4 150g / L, temperature 45℃, current density 6.7A / dm 2 , Time 1S.

[0061] (4) Passivation: Cr 6+ 5g / L, Zn 2+ 0.2 g / L, K 4 P 2 O 7 80 g / L, 10.5, temperature is 32℃, current density is 6.8 A / dm 2 ; Processing time 3s.

[0062] (5) Silane coupling agent: KH560 5g / L, temperature 35℃, treatment time 1.5s.

[0063] (6) Drying: temperature 240℃, treatment time 5s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a surface treatment process for reducing roughness of an electrolytic copper foil, belonging to the technical field of electrolytic copper foil production processes. The surface treatment process comprises the following steps of: carrying out treatment steps of acid washing, micro etching, nickel-zinc alloy plating, passivating, coupling, drying and the like on the electrolytic copper foil with surface roughness (Rz) of 3-5 microns to form a VLP (Very Low Profile) copper foil, wherein the surface roughness (Rz) is reduced to 0.5-1.5 micron. The surface treatment process disclosed by the invention has the advantages that: the treated copper foil surface is reddish-brown and has excellent corrosion resistance, etching property and excellent normal-temperature and high-temperature oxidation resistance so as to be suitable for flexible copper-clad plates.

Description

Technical field [0001] The invention relates to a surface treatment process for reducing the roughness of electrolytic copper foil, and belongs to the technical field of high-precision electrolytic copper foil production technology. Background technique [0002] At present, electrolytic copper foil is one of the main raw materials for PCB production. There are two production processes: rolling method and electrolytic method. Rolled copper foil has greater advantages in terms of elongation and bending resistance, which makes the previous flexible printing FPC manufacturers only use rolled copper foil. In recent years, with the improvement of electrolytic copper foil production technology, some Japanese copper foil manufacturers have developed a variety of high-quality electrolytic copper foils that can meet the requirements of FPC. Due to the improvement of electrolytic copper foil manufacturing technology and price advantages, electrolytic copper foil is increasingly used in F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D7/06C23G1/10C23F1/18C25D3/56C23C22/33H05K1/02
Inventor 杨祥魁徐树民刘建广马学武宋召霞徐策王涛
Owner SHANDONG JINBAO ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap