Polypropylene material for automobile interior trimming parts and preparation method thereof

A technology for polypropylene materials and automotive interior parts, which is applied in the field of polypropylene materials for automotive interior parts and its preparation, can solve the problems of insufficient rigidity, poor cold resistance, poor weather resistance, etc., and achieves good thermal stability performance, bending Excellent modulus and impact strength, high heat resistance effect

Active Publication Date: 2012-07-25
NINGBO JOYSONQUIN AUTOMOTIVE SYST HLDG CO LTD
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its cold resistance is poor, weather resistance is not good, high temperature is rigid enough
[0003] In the current technology, because some properties of PP are not ideal, it needs to be modified to improve toughness, cold resistance, weather resistance, dyeability, and further improve mechanical properties and heat resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene material for automobile interior trimming parts and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Each raw material was weighed according to the data corresponding to Example 1 in Table 1.

[0029] Mix the components uniformly in a high-speed mixer, control the speed at 300-400 rpm, melt and knead in a twin-screw extruder, extrude and granulate, control the barrel temperature at 200-220°C, and extrude The polypropylene material is cooled and molded in cold water at 10-40°C to obtain the polypropylene material for automotive interior parts.

[0030] Table 1: Formula table of polypropylene materials for automotive interior parts Unit: kg

[0031] Example 1

Embodiment 2

[0033] Each raw material was weighed according to the data corresponding to Example 2 in Table 1. The method described in Example 1 was used to prepare the polypropylene material for automotive interior parts.

Embodiment 3

[0035] Each raw material was weighed according to the data corresponding to Example 3 in Table 1. The method described in Example 1 was used to prepare the polypropylene material for automotive interior parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polypropylene material for automobile interior trimming parts and a preparation method of the polypropylene material. The polypropylene material for automobile interior trimming parts comprises the following components in part by weight: 30-80 parts of polypropylene, 5-10 parts of ethylene propylene terpolymer and 10-25 parts of talcum powder. The polypropylene material can be prepared just through weighting each raw material in certain proportion; after the raw materials are uniformly mixed, carrying out fusing and mixing on the obtained mixture; and carrying out extruding and granulation to obtain the polypropylene material. Through mixing the polypropylene with the ethylene propylene terpolymer, the toughness and cold resistance of the polypropylene material can be improved, and the polypropylene material is good in ozone resistance, oxidation resistance and erosion resistance; meanwhile, the polypropylene material has a shockproof effect; and after the talcum powder is added, the friction coefficient of the polypropylene material can be reduced, and the self lubricity of the polypropylene material can be improved. The polypropylene material for automobile interior trimming parts disclosed by the invention has the appearance and performance of a rubber body; and the polypropylene material can be prepared into automobile interior trimming parts suchas outer side plates for driver seats, small cover lids, inner plates of side plates, plastic parts for inner side plates, outer side plates for passenger seats, door-sheet armrest frames and door trimming plates and the like through an injection molding process.

Description

technical field [0001] The invention relates to a plastic material and a preparation method thereof, in particular to a polypropylene material for automotive interior parts and a preparation method thereof. Background technique [0002] Polypropylene, abbreviated as PP, was first put into industrial production in Italy in 1957 and is another important plastic species after polyethylene (PE). It has good heat resistance, and it will not be destroyed when it is cooked at 135°C for 1000 hours. The specific heat capacity and thermal conductivity of PP are smaller than that of PE, but its thermal insulation is better than that of PE. PP is a non-polar polymer with excellent dielectric and electrical insulation properties. The electrical properties are basically not affected by ambient humidity and electric field frequency. Within the allowable operating range, the increase in temperature will reduce the electrical properties. Its High arc resistance. PP has good chemical resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/16C08K13/02C08K3/34C08K5/098C08K5/3417C08K3/30
Inventor 赵海应张荣福印玲
Owner NINGBO JOYSONQUIN AUTOMOTIVE SYST HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products