Base paper of antiflaming environment-friendly rich mineral paper and manufacturing method of the base paper

An environmentally friendly stone paper and base paper technology, applied in the field of light industrial papermaking, can solve the problems of large wood consumption, water resources, pollutant discharge, etc., and achieve the effects of promoting ecological environmental protection, promoting ecological environmental protection of the earth, and obvious social benefits.

Inactive Publication Date: 2012-08-15
KUNMING IRON & STEEL HLDG CO LTD
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems that the existing base paper of environment-friendly paper consumes a large amount of wood and water resources and produces a large amount of pollutant discharge, the present invention provides a base paper of flame-retardant and environment-friendly stone paper and its preparation method, which has the advantages of environmental protection and fire resistance. combustion function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Prepare materials according to the following components by mass to 100kg:

[0037] Polypropylene 8kg HDPE 3kg

[0038] Calcium carbonate powder (1250 mesh) 31 kg Talc powder (1250 mesh) 3kg

[0039] Magnesium hydroxide (1250 mesh) 30 kg Aluminate coupling agent 2 kg

[0040] 1010 from phenols 0.15kg DLTDP from amines 0.05kg

[0041] Ethoxylated fatty alkylamine 0.1kg Ethoxylated lauramide 0.2kg

[0042] Zinc stearate 1kg PE wax 0.5kg

[0043] Rutile titanium dioxide 1 kg Antimony trioxide 9.5 kg

[0044] Chlorinated paraffin (the mass fraction of chlorine is more than 70%) 10.5 kg;

[0045] (2) Mixing the components in step (1) evenly to obtain a mixture;

[0046] (3) Mix the mixture obtained in step (2) for 10 minutes as usual to obtain the mixture;

[0047] (4) Extrude the compounded material obtained in step (3) into masterbatch at 190°C as usual;

[0048] (5) Form the masterbatch obtained in step (4) at 210°C with a calender as usual, then cool it as usu...

Embodiment 2

[0050] (1) Prepare materials according to the following components by mass to 100kg:

[0051] Linear polyethylene 10kg Chlorinated polyethylene 5kg

[0052]Calcium carbonate (800 mesh) 40 kg Magnesium hydroxide (1250 mesh) 28kg

[0053] Aluminate coupling agent 2kg Phosphite DSTDP 0.2kg

[0054] Ethoxylated fatty alkylamine 0.3kg Paraffin wax 0.5 kg

[0055] PP wax 2kg Rutile titanium dioxide 2 kg

[0056] Antimony trioxide 3kg Tetrabromobisphenol A 7kg;

[0057] (2) Mixing the components in step (1) evenly to obtain a mixture;

[0058] (3) Mix the mixture obtained in step (2) for 10 minutes as usual to obtain the mixture;

[0059] (4) Extrude the compounded material obtained in step (3) into masterbatch at 180°C as usual;

[0060] (5) Form the masterbatch obtained in step (4) at 210°C with a calender as usual, then cool it as usual, corona until the corona value reaches 40 dyne, and coat it to obtain a flame-retardant and environmentally friendly Stone paper wallpaper ...

Embodiment 3

[0062] (1) Prepare materials according to the following components by mass to 100kg:

[0063] Chlorinated polypropylene 18.3kg Talc powder 60kg

[0064] Titanate coupling agent (NDZ-201) 1kg Ethoxylauramide 0.5kg

[0065] Propyl functional group 168 0.2kg Calcium stearate 1kg

[0066] Paraffin wax 2kg Anatase titanium dioxide 5kg

[0067] Zinc borate 3kg Hexabromobenzene 2kg

[0068] Tris(2,3-dichloropropyl)phosphate 3kg Hexabromocyclododecane 4kg

[0069] (2) Mixing the components in step (1) evenly to obtain a mixture;

[0070] (3) Mix the mixture obtained in step (2) for 15 minutes as usual to obtain the mixture;

[0071] (4) Extrude the compounded material obtained in step (3) into masterbatch at 170°C as usual;

[0072] (5) Form the masterbatch obtained in step (4) at 190°C with a calender as usual, then cool it as usual, corona until the corona value reaches 39 dyne, and coat it to obtain a flame-retardant and environmentally friendly Stone paper wallpaper base pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides base paper of antiflaming environment-friendly rich mineral paper and a manufacturing method of the base paper of the antiflaming environment-friendly rich mineral paper. Each 100 parts of base paper comprise the following ingredients by mass: 11-31 parts of synthetic resin, 60-80 parts of an inorganic filler, 1-2 parts of a coupling agent, 0.2 parts of an antioxidant, 0.2-0.5 parts of an antistatic agent, 1-3 parts of a lubricant, 1-5 parts of a colorant and 5-20 parts of a fire retardant. The base paper of antiflaming rich mineral wallpaper obtained in the invention is rich mineral paper with high inorganic powder content and has the characteristics of appearance, whiteness, stiffness, printing and writing performances as those of multiple types of paper; and at the same time, the obtained base paper also has the characteristics of high strength, light resistance, moisture resistance, corrosion resistance, moth resistance, stable size, folding endurance, wide application and recyclability as those of multiple types of high-grade paper (including multiple types of synthetic paper).

Description

technical field [0001] The invention relates to a base paper of a novel flame-retardant and environment-friendly stone paper and a preparation method thereof, belonging to the technical field of light industry papermaking. Background technique [0002] Wallpaper, like other decorative materials, is constantly developing and changing with the development of world economy and culture. The use of wallpaper in different periods is a reflection of the comprehensive factors of local economic development level, new material science, and popular consumer psychology. At present, glue surface wallpaper is the most widely used. It is a kind of wallpaper with paper or cloth as the base material and polyvinyl chloride (PVC) as the surface layer. The usage rate in the world accounts for about 70%. The current wallpaper penetration rate in Japan and Russia is close to 100%, in Europe and the United States there is also a penetration rate of 90%, while in China the current penetration rate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L23/28C08K13/02C08K3/26C08K3/34C08K3/22C08K3/02C08K5/098
Inventor 刘海国郭嘉麟刘瑞铭赵华玲
Owner KUNMING IRON & STEEL HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap