Environment-friendly flame-retardant glass fiber reinforced PA6 (Polyamide 6) material and preparation method thereof

A glass fiber, environmentally friendly technology, applied in the field of environmentally friendly flame retardant glass fiber reinforced PA6 materials and their preparation, can solve the problems of low CTI value and GWIT value, unsuitable for electricity environment, etc. The effect of friction coefficient and comprehensive performance balance

Inactive Publication Date: 2014-12-03
SHANGHAI SUNNY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some traditional methods are (GF+decabromodiphenylethane+antimony trioxide) compound system, (GF+brominated polystyrene+antimony trioxide) compound system, but the CTI value and GWIT of these compound systems The value is not high, not suitable for high-demand electricity environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly flame-retardant glass fiber reinforced PA6 (Polyamide 6) material and preparation method thereof
  • Environment-friendly flame-retardant glass fiber reinforced PA6 (Polyamide 6) material and preparation method thereof
  • Environment-friendly flame-retardant glass fiber reinforced PA6 (Polyamide 6) material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 3

[0028] A method for preparing environmentally friendly flame-retardant glass fiber reinforced PA6 material with high CTI value and high GWIT value, characterized in that the method is as follows: raw materials are weighed according to weight ratio: PA6 44.5%, compound flame retardant 20% , antimony trioxide 4.8%, glass fiber 20%, commercially available maleic anhydride grafted POE10%, antioxidant (1330) 0.1%, iron oxide 0.6%; put into high mixer and mix for 2 minutes, discharging, Then use a twin-screw extruder to extrude and granulate, the processing temperature is 230° C., and the screw rotation speed is 300 rpm.

[0029] The compound flame retardant is compounded by our company itself, and is composed of three components, and its mass percentage is BPS: 50%; magnesium hypophosphite: 25%; talcum powder: 25%.

Embodiment 4

[0031] A method for preparing environmentally friendly flame-retardant glass fiber reinforced PA6 material with high CTI value and high GWIT value. Antimony oxide 3%, glass fiber 21%, commercially available maleic anhydride grafted POE 2%, antioxidant (1330) 1%, iron oxide 1%; put into high mixer and mix for 5 minutes, discharge, and then Use a twin-screw extruder to extrude and granulate, the processing temperature is 220° C., and the screw rotation speed is 400 rpm.

[0032] The compound flame retardant is compounded by our company itself, and is composed of three components, and its mass percentage is BPS: 50%; magnesium hypophosphite: 25%; talcum powder: 25%.

[0033] The glass fiber is an alkali-free glass fiber, and the glass fiber is added into the silane coupling agent to make its surface treated with the silane coupling agent.

Embodiment 5

[0035] A method for preparing environmentally friendly flame-retardant glass fiber reinforced PA6 material with high CTI value and high GWIT value. Antimony oxide 15%, glass fiber 30%, commercially available maleic anhydride grafted POE 2%, antioxidant (1330) 0.5%, iron oxide 0.5%; put into high mixer and mix for 3 minutes, discharge, and then use A twin-screw extruder extruded and granulated, the processing temperature was 200° C., and the screw rotation speed was 350 rpm.

[0036] The compound flame retardant is compounded by our company itself, and is composed of three components, and its mass percentage is BPS: 50%; magnesium hypophosphite: 25%; talcum powder: 25%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly flame-retardant glass fiber reinforced PA6 (Polyamide 6) material and a preparation method thereof. The environment-friendly flame-retardant glass fiber reinforced PA6 material is prepared from the following components in parts by weight: 45-82 parts of PA6, 6-20 parts of compound flame retardant, 3-15 parts of antimony trioxide, 20-30 parts of glass fiber, 2-10 parts of compatilizer, 0.1-1 part of antioxidant and 0.1-1 part of oxide. The method comprises the following steps of: weighing raw materials according to a formula, and putting into a highly mixing machine for mixing for 2-5 minutes; and discharging, and extruding and pelletizing by using a double-screw extruder to obtain the environment-friendly flame-retardant glass fiber reinforced PA6 material. Compared with the prior art, the environment-friendly flame-retardant glass fiber reinforced PA6 material has the advantages of high glowing filament ignition temperature (GWIT), environment friendliness, balanced comprehensive performance, high CTI (Comparative Tracking Index) value, high GWIT value and the like.

Description

technical field [0001] The present invention relates to one kind, especially relates to a kind of high CTI value, high GWIT value environment-friendly flame-retardant glass fiber reinforced PA6 material and its preparation method. Background technique [0002] Nylon (Nylon), Chinese name polyamide, English name Polyamide (referred to as PA), is a general term for thermoplastic resins containing repeated amide groups -[NHCO]- on the main molecular chain. Its name is determined by the specific number of carbon atoms in the synthetic monomer, such as: nylon-6, 66, 1010, 610. It has high crystallinity and obvious melting point; it has high surface hardness, wear resistance, small friction coefficient, and self-lubrication and noise reduction. It has good low temperature performance and certain heat resistance (it can be used below 100 degrees). Non-toxic, odorless, non-mildew, self-extinguishing, good weather resistance, but poor dyeing. In the 21st century, electronic, elect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/02C08K13/06C08K3/22C08K7/14C08K3/32C08K3/34
Inventor 郭建鹏娄小安
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com