Ultraviolet cross-linked organosilicone modified acrylate copolymer emulsion

An acrylate, ultraviolet light technology, applied in the direction of coating, etc., can solve the problems of low slip and anti-adhesion

Active Publication Date: 2015-07-15
邯郸市瑞斯达乳胶科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the defects of existing common acrylate resins, which are cold, brittle and hot-tacky, and highly elastic acrylate materials have low slipperiness and anti-sticking properties, the purpose of the present invention is to provide a UV-crosslinked silicone-modified acrylate copolymer emulsion, The UV-crosslinked silicone-modified acrylate copolymer emulsion contains UV-active groups and alkoxysiloxane groups in the side chain of the copolymer to achieve double crosslinking, that is, UV self-crosslinking Self-crosslinking with silicone to form a flexible and highly elastic material with high surface smoothness, strong stain resistance, excellent anti-adhesive performance, and no residual small molecules

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet cross-linked organosilicone modified acrylate copolymer emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] 10 parts of 4-(2-hydroxy-3-allyloxy-propoxy)benzophenone, 10 parts of vinyltriethoxysilane, 19 parts of methyl methacrylate, 5 parts of methyl acrylate, acrylic acid 25 parts of butyl ester, 17 parts of isobutyl methacrylate, 8 parts of isobornyl acrylate, 3 parts of isooctyl methacrylate, 1 part of maleic acid and 2 parts of acrylic acid were used as a monomer composition. Among them, 4-(2-hydroxy-3-allyloxy-propoxy)benzophenone is a UV active monofunctional monomer, and vinyltriethoxysilane is an alkoxysiloxane monofunctional Degree monomers, others are the third monofunctional monomers.

[0047] A preparation method of an ultraviolet-light crosslinked silicone-modified acrylate copolymer emulsion, the steps of which are:

[0048] (1) Put 100 parts of the above-mentioned monomer composition, 2 parts of nonylphenol polyoxyethylene ether ammonium sulfate, 1.5 parts of octylphenol polyoxyethylene ether and 20 parts of primary distilled water into the 123.5 parts of the...

Embodiment 2

[0056]5 parts of 4-acryloxybenzophenone, 10 parts of methacryloxypropyl trimethoxysilane, 10 parts of methyl acrylate, 15 parts of methyl methacrylate, 5 parts of styrene, methacrylic acid 5 parts of isobutyl ester, 30 parts of n-butyl acrylate, 10 parts of isooctyl acrylate, 5 parts of octadecyl acrylate, 3 parts of 2-hydroxyethyl acrylate and 2 parts of methacrylic acid were used as a monomer composition. Among them, 4-acryloyloxybenzophenone is a UV active monofunctional monomer, methacryloxypropyltrimethoxysilane is an alkoxysiloxane monofunctional monomer, and others are the second Three monofunctional monomers.

[0057] A preparation method of an ultraviolet-light crosslinked silicone-modified acrylate copolymer emulsion, the steps of which are:

[0058] (1) Put 100 parts of the above-mentioned monomer composition, 1.5 parts of sodium lauryl sulfate, 3.5 parts of octylphenol polyoxyethylene ether and 20 parts of deionized water into a mixture equipped with a stirrer, te...

Embodiment 3

[0066] 2 parts of 4-(2-hydroxy-3-allyloxy-propoxy) benzophenone, 15 parts of methacryloxypropyl trimethoxysilane, 18 parts of styrene, 3 parts of n-propyl acrylate 32 parts of n-butyl acrylate, 5 parts of n-butyl methacrylate, 10 parts of isooctyl methacrylate, 10 parts of isodecyl acrylate, 2 parts of acrylamide and 3 parts of acrylic acid as a monomer composition. Among them, methacryloxypropyltrimethoxysilane is a UV active monofunctional monomer, methacryloxypropyltrimethoxysilane is an alkoxysiloxane monofunctional monomer, and others It is the third monofunctional monomer.

[0067] A preparation method of an ultraviolet-light crosslinked silicone-modified acrylate copolymer emulsion, the steps of which are:

[0068] (1) 100 parts of the above-mentioned monomer composition, 2 parts of octylphenol polyoxyethylene ether and 15 parts of deionized water are dropped into a reaction kettle with a stirrer, a temperature control device, a condensation device, a dropping device a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultraviolet cross-linked organosilicone modified acrylate copolymer emulsion which belongs to the field of high-molecular compounds. The ultraviolet cross-linked organosilicone modified acrylate copolymer emulsion is formed by constitutional repeating units and is a modified acrylate copolymer with a side chain containing an ultraviolet active group and an alkoxy siloxane group. The ultraviolet cross-linked organosilicone modified acrylate copolymer emulsion is obtained through the copolymerization reaction of an ultraviolet active single-functionality degree monomer, an alkoxy siloxane single-functionality degree monomer and a third single-functionality degree monomer. According to the ultraviolet cross-linked organosilicone modified acrylate copolymer emulsion, the side chain of the copolymer contains the ultraviolet active group and the alkoxy siloxane group, double crosslinking is realized, i.e. ultraviolet self-crosslinking and organosilicone self-crosslinking, and a high elastic material with good flexibility is formed, has high surface smoothness, strong contamination resistance, excellent adhesion resistance and no residual small molecules.

Description

technical field [0001] The present invention relates to a silicone-modified acrylate copolymer emulsion crosslinked by ultraviolet light, in particular to a silicone-modified acrylate copolymer emulsion obtained by participating in emulsion polymerization of ultraviolet light-active monomers, which belongs to polymer compounds field. Background technique [0002] Acrylate emulsion uses water as the reaction and dispersion medium, which is environmentally friendly and pollution-free. It is the main component of acrylic emulsion paint. Acrylate emulsion has many outstanding advantages, such as excellent light resistance, weather resistance, acid and alkali resistance, corrosion resistance and good oil resistance, and because of its low cost, acrylate emulsion is widely used in automobiles, construction and electromechanical products and other fields. However, conventional thermoplastic acrylate emulsions have disadvantages such as cold brittleness, hot stickiness, and low st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/18C08F230/08C08F220/14C08F222/02C08F220/06C08F212/08C08F220/28C08F220/56C08F218/08C08F2/30C08F2/26C08J3/28C08J3/24C09D133/08C09D143/04
Inventor 陈智陈嘉刘治生
Owner 邯郸市瑞斯达乳胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com