Moisture-resistant epoxy resin paint for transformer

A technology of epoxy resin paint and epoxy resin, which is applied in the direction of coating, surface pretreatment, and equipment for coating liquid on the surface, etc., which can solve problems such as difficulty in controlling molecular weight, uneven batches of paint quality, and small process range , to achieve the effects of stable and easy control of the production process, improved consistency of finished products, and improved surface finish

Active Publication Date: 2013-04-03
铜陵常江传动工具有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The epoxy resin paint for transformers produced by the traditional method has the following defects: ordinary industrial phenol and xylene are used as solvents, which have a strong smell, strong irritation, and pollute the environment; it is difficult to control the molecular weight during the synthesis process, resulting in uneven paint quality batches and affecting Batch stability; the process range is small, and the furnace temperature / speed has a great influence on the application of coated wire rods, which has high requirements for coating applications, and it is difficult to form a smooth surface; the adhesion is small and the heat resistance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of epoxy resin varnish for anti-humidity transformer, it is made up of the raw material of following parts by weight (kg):

[0024] Modified epoxy resin 135, phenolic resin 30, melamine formaldehyde resin 20, antirust pigment zinc phosphate 20, diethylene glycol diacrylate phthalate 6, polyacrylic acid 1, fatty alcohol polyoxyethylene ether ammonium sulfate 0.3, Isopropyl tris (dioctyl pyrophosphate acyloxy) titanate 0.4, dicumyl peroxide 0.1, monoethanolamine 0.2-0.6, defoamer polydimethylsiloxane 0.3, diisooctyl succinate Sodium ester sulfonate 0.2.

[0025] A moisture-resistant epoxy resin paint for transformers and a preparation method thereof, comprising the following steps:

[0026] (1) Preparation of modified epoxy resin: including the following steps:

[0027] Preparation of modified epoxy resin, preparation of epoxy resin emulsifier, preparation of finished products;

[0028] Preparation of modified epoxy resin: The modified epoxy resin is composed of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses moisture-resistant epoxy resin paint for a transformer. The moisture-resistant epoxy resin paint is composed of the following raw materials in parts by weight: 125-135 parts of modified epoxy resin, 20-30 parts of phenolic resin, 15-20 parts of melamino-formaldehyde resin, 10-20 parts of anti-rust pigment zinc phosphate, 5-6 parts of phthalic acid diethylene glycol acrylate, 1-2 parts of polyacrylic acid, 0.3-0.5 part of fatty alcohol-polyoxyethylene ether ammonium sulfate, 0.2-0.4 part of isopropyl tri(dioctyl pyrophosphoric acid acyloxy) titanate, 0.1-0.3 part of dicumyl peroxide, 0.2-0.6 part of monoethanolamine, 0.1-0.3 part of defoamer polydimethylsiloxane, and 0.1-0.2 part of dioctyl sodium sulfosuccinate. According to the invention, a finished product of emulsion prepared by using the modified epoxy resin is used as a main film-forming material, so that the entire production process is stable and is easy to control, the product consistency is improved greatly, and the stability among batches is good; and the phthalic acid diethylene glycol acrylate is selected as the solvent, so that the odor of the finished product is improved greatly, and environment pollution is reduced when the phthalic acid diethylene glycol acrylate is used in production.

Description

technical field [0001] The invention mainly relates to an epoxy resin paint for a moisture-resistant transformer, which belongs to the field of chemical industry. Background technique [0002] Epoxy resin paint for transformers is widely used in the manufacture of special coils (such as DY coils, electric tool coils, and various transformer coils) due to their excellent moisture resistance and deformation resistance. The epoxy resin paint for transformers produced by the traditional method has the following defects: ordinary industrial phenol and xylene are used as solvents, which have a strong smell, strong irritation, and pollute the environment; it is difficult to control the molecular weight during the synthesis process, resulting in uneven paint quality batches and affecting Batch stability; the process range is small, and the furnace temperature / speed has a great influence on the application of coated wire rods, which has high requirements for coating applicatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/08C09D161/06C09D161/28C09D7/12C08F283/10B05D1/18B05D3/02
Inventor 李新满王章奎
Owner 铜陵常江传动工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com