Capacitor thin film with homo-polypropylene as substrate and preparation method thereof

Abstract

The invention discloses a capacitor thin film with homo-polypropylene as a substrate and a preparation method of the capacitor thin film. The composition raw materials of the thin film in parts by weight are as follows: 20-30 parts of LDPE (Low Density Polyethylene), 30-40 parts of homo-polypropylene, 3-5 parts of epoxy linseed oil, 2-3 parts of polyvinyl alcohol, 1-2 parts of aluminum hydroxide, 1-2 parts of polyisobutene, 8-12 parts of diatomite, 1-2 parts of dicyclopentadienyl iron, 0.9-1.1 parts of poly-4-methyl-1-pentene, 0.5-0.7 part of permanent white, 9-11 parts of nano-clay, 2.0-2.5 parts of catechol, 1.2-1.6 parts of di(ethylene glycol) benzoate, 1.3-1.8 parts of dibutyl phthalate, 4-6 parts of calcium stearate, 1.5-2.0 parts of vinyl triethoxy silane, and 2.5-3.0 parts of modified tree ash. The thin film provided by the invention is manufactured by taking the homo-polypropylene as a main raw material and the low density polyethylene as an auxiliary raw material, and enabling a plurality of auxiliary additives and the homo-polypropylene as well as the low density polyethylene to be subjected to mixed extrusion, film blowing sizing, and cutting; the preparation method is simple; simultaneously, the diatomite, the nano-clay and the modified tree ash are added into the raw materials to enhance barrier property and air tightness of the thin film; and the thin film has the characteristics of good pressure resistance, good impact resistance, heat seal strength, and good heat seal performance.

Description

technical field [0001] The invention relates to a capacitor film material, in particular to a capacitor film with homopolypropylene as a matrix and a preparation method thereof. Background technique [0002] Film capacitors use metal foil as an electrode, which is stacked with plastic films such as polyethylene, polypropylene, polystyrene or polycarbonate from both ends, and wound into a cylindrical capacitor; in all Among the plastic film capacitors, the characteristics of polypropylene (PP) capacitors and polystyrene (PS) capacitors are the most significant. Of course, the price of these two capacitors is also relatively high. The quality of the capacitor film directly affects the service life and product performance of the capacitor. The demand for films is large and there are many types. It is difficult to meet the requirements of the market by using a single raw material to produce films, but each raw material has its shortcomings, so the produced films are difficult to...

AI Technical Summary

Problems solved by technology

[0002] Film capacitors use metal foil as an electrode, which is stacked with plastic films such as polyethylene, polypropylene, polystyrene or polycarbonate from both ends, and wound into a cylindrical capacitor; in all Among the plastic film capacitors, the characteristics of polypropylene (PP) capacitors and polystyrene (PS) capacitors are the most significant. Of course, the price of these two capacitors is also relatively high. The quality of the capacitor film directly affects the service life and product performance of the capacitor. The demand for films is large and there are many types. It is difficult to meet the requirements of the market by using a single raw material to produce films, but each raw material has its own shortcomings, so the produced films are difficult to meet the needs of various situations