Multifunctional waterproof antiseptic aldehyde-eliminating glue and preparation method

An aldehyde-removing glue agent, multi-functional technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, paints containing biocides, etc. Cost, short drying time, manpower saving effect

Inactive Publication Date: 2013-06-05
刘川
View PDF10 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Architectural waterproof coatings, anti-corrosion and anti-fungal agents, insect repellants, termite-proof agents, formaldehyde removers, and wall primers are all materials for building decoration. Existing technologies and products often have a single function and require multiple constructions to achieve Waterproof and moisture-proof, anti-corrosion and mildew-proof, insect-proof, termite-proof, formaldehyde removal, waste of manpower and high material cost
[0004] CN200410047075.1, "Wood Protective Agent", this patent is composed of dicyandiamide phosphate, boric acid, quaternary ammonium salt, silica sol, silane coupling agent, dispersant, alcohol solvent, water softener and water, and has ideal anti-corrosion and anti-corrosion properties. Mildew and insect resistance, but it is not waterproof and has poor anti-loss performance. The surface cannot be painted, let alone remove formaldehyde.
[0005]

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) Formula:

[0033] 48% water-based silicone acrylic emulsion 55 parts

[0034] 50% propiconazole emulsion 0.5 parts

[0035] 0.5 parts of 10% 1,2 benzisothiazolin-3-one emulsion

[0036] Disodium octaborate 2 parts

[0037] 10% bifenthrin emulsion 1 part

[0038] Urea 2 parts

[0039] 1.5 parts of adipic acid dihydrazide

[0040] Lauryl ester 4 parts

[0041] Ethylene glycol 2 parts

[0042] 31.5 parts of water

[0043] (2) Preparation method:

[0044] 1) Add water into the dispersing equipment, start stirring at 200 rpm, add 50% propiconazole emulsion, 10% 1,2 benzisothiazolin-3-one emulsion, 10% bifenthrin emulsion, Lauryl alcohol ester, ethylene glycol, disodium octaborate, urea, adipate dihydrazide and 48% water-based silicone acrylic emulsion, after stirring for 20 minutes, adjust the pH value to neutral;

[0045] 2) Inspected packaging.

Embodiment 2

[0047] (1) Formulation:

[0048] 48% water-based silicone styrene-acrylic emulsion 50

[0049] 50% propiconazole emulsion 1 part

[0050] 30% thiocyanate emulsion 1 part

[0051] Disodium octaborate 2 parts

[0052] 10% bifenthrin emulsion 1 part

[0053] Urea 2 parts

[0054] 1.5 parts of adipic acid dihydrazide

[0055] Lauryl ester 4 parts

[0056]2 parts propylene glycol

[0057] 35.5 parts of deionized water

[0058] (2) Preparation method:

[0059] 1) Add water to the dispersing equipment, start stirring at 300 rpm, add 30% thiocyanate emulsion, 50% propiconazole emulsion, 10% bifenthrin emulsion, lauryl alcohol ester, propylene glycol, octaboric acid two Sodium, urea, diacyl adipate and 48% water-based silicone styrene-acrylic emulsion, after stirring for 20 minutes, adjust the pH value to neutral;

[0060] 2) Inspected packaging.

Embodiment 3

[0062] (1) Formulation:

[0063] 48% water-based silicone styrene-acrylic emulsion 50 parts

[0064] 50% propiconazole emulsion 0.5 parts

[0065] 10% chlorothalonil emulsion 5 parts

[0066] Disodium octaborate 1.5 parts

[0067] 1.5 parts of 10% bifenthrin emulsion

[0068] Urea 2 parts

[0069] 1.5 parts of adipic acid dihydrazide

[0070] Lauryl ester 4 parts

[0071] 2 parts propylene glycol

[0072] 32 parts of water

[0073] (2) Preparation method:

[0074] 1) Add water to the dispersing equipment, start stirring at 100 rpm, add 50% propiconazole emulsion, 10% chlorothalonil emulsion, 10% bifenthrin emulsion, lauryl alcohol ester, propylene glycol, octaboric acid two Sodium, urea, adipic acid dihydrazide and 48% water-based silicone styrene-acrylic emulsion, after stirring for 20 minutes, adjust the pH value to neutral;

[0075] 2) Inspected packaging.

[0076] The embodiment products of the present invention are used to protect bamboo, wood, furniture,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses multifunctional waterproof antiseptic aldehyde-eliminating glue, and belongs to the technical field of construction materials, wherein the glue is mainly for sealing, waterproofness, moisture-proofness, anticorrosion, mold prevention, insect prevention, termite prevention and aldehyde elimination of materials such as bamboo wood, timber, rattan wood, wall faces, ground, emulsion varnish, wallpaper, floor boards and wooden doors. The multifunctional waterproof antiseptic aldehyde-eliminating glue is characterized by comprising 10-90 parts of water-dilutable resin, 0.01-30 parts of antiseptic and mold inhibitor, 0.01-20 parts of insect-resist agents, 0.01-15 parts of termite-resisting agents, 0.1-20 parts of aldehyde-eliminating agents, 0.1-30 parts of coalescing agents, 0.5-15 parts of anti-freezing agents and 5-95 parts of water. After being treated by the multifunctional waterproof antiseptic aldehyde-eliminating glue, products are strong in engaging force, environment-friendly, water-proof, moisture-proof, antiseptic, mold-proof, inset-proof, termite-proof and capable of eliminating aldehyde. Meanwhile, construction is easy and convenient. Besides, the invention further provides a preparation method of the multifunctional waterproof antiseptic aldehyde-eliminating glue.

Description

technical field [0001] The invention relates to a multifunctional waterproof anti-corrosion and aldehyde-removing glue and a preparation method thereof, which belong to the technical field of building materials and are suitable for waterproofing, moisture-proofing, anti-corrosion, mildew-proofing, insect-proofing and termite-proofing of bamboo, wood, rattan, building wall and ground And formaldehyde removal, especially suitable for the primer of building walls and floors, forming a closed alkali, waterproof, moisture-proof, anti-corrosion, mildew-proof, insect-proof, termite-proof and formaldehyde-free, protecting latex paint, wallpaper, floors and wooden doors. Background technique [0002] During the "Eleventh Five-Year Plan" period, my country decided to build a conservation-oriented, environment-friendly, and sustainable economic society, and building materials are waterproof, moisture-proof, anti-corrosion, mildew-proof, insect-proof, termite-proof, wood protection, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D125/14C09D133/04C09D133/00C09D183/00C09D131/04C09D129/04C09D123/08C09D161/28C09D7/12C09D5/00C09D5/08C09D5/14
Inventor 刘川
Owner 刘川
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap