Copper sulfide anode and preparation method thereof

A copper sulfide and positive electrode technology, applied in battery electrodes, electrical components, circuits, etc., can solve the problems of unfavorable large-area preparation, long preparation cycle, high equipment requirements, etc., to improve cycle stability, avoid long-term reaction, and conductivity Good results

Inactive Publication Date: 2015-03-11
XIANGTAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, an integrated porous electrode with a three-dimensional structure has a good prospect for lithium-sulfur batteries. However, at present, the preparation of integrated electrodes is mostly synthesized by sputtering or solution method, which requires high equipment, high cost, instability, and long preparation period. Long, and not conducive to large-area preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copper sulfide anode and preparation method thereof
  • Copper sulfide anode and preparation method thereof
  • Copper sulfide anode and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Preparation of copper sulfide integrated positive electrode: cut the foamed copper with a porosity of 94%, a pore diameter of 0.2mm, and a thickness of 2.5mm into discs with a diameter of 10mm, and press it to 0.2mm with a tablet press, and in 1mol / L HCl Use ultrasonic cleaning in the solution for 15 minutes, then ultrasonic cleaning in acetone solution for 15 minutes, and ultrasonic cleaning in deionized water for 10 minutes. The sulfur load is 0.03g / cm 2 Prepare foamed copper and elemental sulfur, weigh 2.9 mg of elemental sulfur ground to 50 μm, cover the elemental sulfur evenly on the foamed copper, place it in a tube furnace, and under the protection of nitrogen flow, the gas flow rate is 1.5 L / min, the flow rate 20cm / min; keep warm at 155°C for 3h, then raise the temperature to 350°C, keep warm for 1h, synthesize lamellar copper sulfide on the foamed copper skeleton, and the copper sulfide on the sheet has a snowflake-like shape, that is, the positive electrode, t...

Embodiment 2

[0052] Preparation of copper sulfide integrated positive electrode: Cut the foamed copper with a porosity of 96%, a pore diameter of 0.15 mm, and a thickness of 2.7 mm into discs with a diameter of 10 mm, and press it to 0.3 mm with a tablet press. Use ultrasonic cleaning in HCl solution for 30 minutes, then ultrasonic cleaning in acetone solution for 30 minutes, and ultrasonic cleaning in deionized water for 15 minutes. According to the sulfur loading capacity of foamed copper is 0.18g / cm 2 Prepare foamed copper and elemental sulfur, weigh 17.5 mg of elemental sulfur ground to 10 μm, cover the elemental sulfur evenly on the foamed copper, place it in a tube furnace, and under the protection of argon gas flow, the gas flow rate is 0.1L / min. The flow rate is 2cm / min; heat preservation at 155°C for 8 hours, and the lamellar copper sulfide is synthesized on the foamed copper skeleton. The copper sulfide on the sheet has a hexagonal columnar shape, and the positive electrode is ob...

Embodiment 3

[0055] Preparation of copper sulfide integrated positive electrode: foamed copper with a porosity of 98%, a pore diameter of 0.1mm, and a thickness of 3mm is cut into a disc with a diameter of 10mm, pressed to 0.5mm with a tablet press, and placed in a 2mol / L HCl solution Use ultrasonic cleaning for 60 minutes, then ultrasonic cleaning in acetone solution for 60 minutes, ultrasonic cleaning in deionized water for 20 minutes, the power of ultrasonic wave is 100W, vacuum dry the cleaned foamed copper at 80°C for 40 minutes, and set aside; The amount is 0.3g / cm 2 Prepare foamed copper and elemental sulfur, weigh 29 mg of elemental sulfur ground to 100 μm, cover the elemental sulfur evenly on the foamed copper, place it in a tube furnace, and under the protection of an argon atmosphere, the gas flow rate is 5 L / min, and the flow rate is 60cm / min; heat preservation at 155°C for 2 hours, heat preservation at 250°C for 1 hour, synthesize sheet-like copper sulfide on the foamed copper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a copper sulfide anode and a preparation method thereof, solving the problems of the conventional copper sulfide electrode that the bonding force of active substances and current collectors is poor and the anode conductivity is lowered because of a binder and also solving the problems of the integrated copper sulfide electrode which is synthesized in situ in a solution that the quantity of active substances is small and the preparation period is long. The copper sulfide anode is prepared by the following steps: uniformly spreading elemental sulfur which is prepared according to the sulfur carrying amount of foamy copper is 0.03-0.3g / cm<2> on the foamy copper, putting into a furnace, and carrying out in-situ reaction under a protection gas at a temperature of 155-350 DEG C so as to obtain the laminated copper sulphide which takes a foamy copper three-dimensional network structure as a framework, namely an integrated porous copper sulphide anode. By utilizing the copper sulfide anode, the application of the three-dimensional structured integrated porous anode in a lithium battery is widened, the energy density of a lithium battery anode is improved, and the performances of a lithium battery are improved. The copper sulfide anode is simple in preparation process, low in equipment requirement, low in cost and convenient for industrial production.

Description

technical field [0001] The invention relates to a lithium battery positive electrode material and a preparation method thereof, in particular to a copper sulfide positive electrode and a preparation method thereof. Background technique [0002] At present, the commercial lithium-ion battery cathode materials are mainly lithium transition metal oxides and lithium iron phosphate, with a specific capacity of 150-200mAh / g, graphite as the negative electrode, and an energy density of about 250Wh / kg. Gradually unable to meet the growing demand for high security, high energy density and long life power and energy storage power supply. Lithium-sulfur batteries are a type of battery system that uses sulfur or sulfur-containing compounds as the positive electrode and lithium or lithium storage materials as the negative electrode to realize the mutual conversion of electrical energy and chemical energy. The theoretical specific capacity of elemental sulfur is 1675mAh / g, and the energy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/136H01M4/1397
CPCY02E60/122Y02E60/10
Inventor 潘勇成娟娟朱经涛潘俊安雷维新朱岭曹丰文李真真
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com