High-wear resistance cable sheath material

A cable sheathing material, high wear-resistant technology, applied in the direction of insulated cables, cables, circuits, etc., can solve problems such as poor storage stability, achieve low shrinkage, good oil resistance, and reduce production costs.

Active Publication Date: 2013-08-28
ANHUI KANGLIYA CO LTD
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has high tensile strength, elongation and reversible crystallinity, good adhesion, aging resistance, heat resistance, oil resistance and chemical corrosion resistance. It can be used for a long time at 80-100 °C and has a certain flame retardancy. However, the disadvantage is that the storage stabilit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A high wear-resistant cable sheath material is characterized in that it is composed of the following raw materials in parts by weight (kg):

[0014] Neoprene DCR114 100, EPDM 4770R 20, Nano-Bauxite 20, Modified Filler 20-30, Dioctyl Sebacate 8-10, Propylene Glycol Polyester 3-4, Acetyl Citric Acid Triethyl ester 4-6, zinc oxide 2-4, chlorinated paraffin 6-8, antimony trioxide 2-3, triphenyl phosphite 2-4, antioxidant MB 1-2, accelerator CZ 1-2 , sulfur 0.8-1;

[0015] Described modified filler is made up of the following raw materials by weight:

[0016] 0.5% sulfuric acid solution 1000, barium sulfide 90, ethanol 40, aluminum hydroxide powder 15, sorbitan monooleate 12, distearoyloxyisopropoxyaluminate 3, titanium dioxide 4, methyl alcohol Triethoxysilane 2, Sodium polyacrylate 6, Dicumyl peroxide 2, Paohua alkali 6, Stearic acid 3, appropriate amount of water;

[0017] The above-mentioned sulfuric acid solution was continuously introduced into the above-mentioned b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-wear resistance cable sheath material. The high-wear resistance cable sheath material comprises the following raw materials by weight: 90 to 100 parts of chloroprene rubber DCR114, 10 to 20 parts of EPDM 4770R, 15 to 20 parts of nanometer bauxite, 20 to 30 parts of a modification filling material, 8 to 10 parts of dioctyl sebacate, 3 to 4 parts of polypropylene adipate, 4 to 6 parts of acetyl triethyl citrate, 2 to 4 parts of zinc oxide, 6 to 8 parts of chlorinated paraffin, 2 to 3 parts of antimony trioxide, 2 to 4 parts of triphenyl phosphite, 1 to 2 parts of the anti-aging agent MB, 1 to 2 parts of the promoter CZ and 0.8 to 1 part of sulphur. The cable sheath material produced in the invention has excellent physical properties, a stable dimension, low shrinking percentage, high tensile strength, great tearing strength, strong resilience and good resistance to oil, heat, burning, sunlight, ozone, acid and alkali and chemical reagents; and the modification filling material provided by the invention has good dispersibility and low surface tension, enables tensile strength and stress at definite elongation of the cable sheath material to be further improved, reduces heat generation and compression set, delays the ageing speed of the cable sheath material, is capable of resisting acid and alkali and allows production cost to be reduced.

Description

technical field [0001] The invention mainly relates to a cable sheath material, in particular to a high wear-resistant cable sheath material. Background technique [0002] Neoprene rubber has good physical and mechanical properties, oil resistance, heat resistance, flame resistance, sunlight resistance, ozone resistance, acid and alkali resistance, and chemical resistance. It has high tensile strength, elongation and reversible crystallinity, good adhesion, aging resistance, heat resistance, oil resistance and chemical corrosion resistance. However, the disadvantage is that the storage stability is poor. Therefore, using neoprene as a cable sheath material can ensure that it has strong heat resistance, aging resistance, oil resistance, corrosion resistance and other characteristics. Improving its storage stability further improves the performance of the cable sheathing material. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L11/00C08L23/16C08L67/02C08K13/06C08K3/34C08K5/11C08K3/22C08K5/526C08K3/06H01B7/17H01B7/18
Inventor 李训祥王新祥周志梅李贻凤胡云昌
Owner ANHUI KANGLIYA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap