Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ecological wood and preparation method thereof

A technology of ecological wood and plant fiber, which is applied in the field of ecological wood and its preparation, can solve the problems of poor recyclable and reuse effect of composite ecological wood, poor flame retardant effect, and great harm to human body, and achieve good fire and flame retardant effect, Low cost, good moisture-proof effect

Active Publication Date: 2013-08-28
YIBAO FUJIAN POLYMER MATERIALS
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composite ecological wood has a certain waterproof, moisture-proof, insect-proof, and fire-proof effects, but it is not environmentally friendly. Its composition contains toluene, which is harmful to the human body, and its flame-retardant effect is not good. When it burns, it generates a lot of smoke , is easy to pollute the environment when discharged into the air. In addition, the recyclable and reuse effect of the composite ecological wood is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] An ecological wood, comprising the following components by weight, the name of each component, model / specification, parts by weight, and suppliers are shown in Table 1.

[0052] The raw material of table 1 embodiment one

[0053] Raw material name Model / Specification parts by weight supplier 1 Vinyl chloride copolymer resin BL—2 70 Jiangsu Bat Plastic Co., Ltd. 2 impact modifier NBR3305 10 blue 3 plant fibres 90 mesh 20 Mujiang Weihua Perfume Factory 4 coupling agent titanate 1 Taichang Chemical 5 smoke suppressant Imported from Taiwan 10 Dongguan Maoya Trading Co., Ltd. 6 white clay 800 mesh 15 Nanchang Lanxiang Chemical Co., Ltd. 7 lubricant PE wax 1 Dongguan Hengtai Chemical 8 activator Zinc oxide 4 Shanghai Jinghua Chemical Co., Ltd. 9 Environmental Flame Retardant Ammonium polyphosphate 8 Beijing Oriental Aohan Company 10 Heat stabilizers Calci...

Embodiment 2

[0062] An ecological wood, comprising the following components by weight, the name of each component, model / specification, parts by weight, and suppliers are shown in Table 2.

[0063] The raw material of table 2 embodiment two

[0064] 5 raw material Model / Specification number of copies supplier 1 Vinyl chloride copolymer resin BL—2 65 Jiangsu Bat Plastic Co., Ltd. 2 impact modifier NBR3305 10 blue 3 plant fibres 90 mesh 25 Mujiang Weihua Perfume Factory 4 coupling agent titanate 2 Taichang Chemical 5 smoke suppressant Imported from Taiwan 15 Dongguan Maoya Trading Co., Ltd. 6 white clay 800 mesh 10 Nanchang Lanxiang Chemical Co., Ltd. 7 lubricant PE wax 1.0 Dongguan Hengtai Chemical 8 activator Zinc oxide 5 Shanghai Jinghua Chemical Co., Ltd. 9 Environmental Flame Retardant Ammonium polyphosphate 9 Beijing Oriental Aohan Company 10 Heat stabilizers Calciu...

Embodiment 3

[0073] An ecological wood, comprising the following components by weight, the name of each component, model / specification, parts by weight, and suppliers are shown in Table 3.

[0074] The raw material of table 3 embodiment three

[0075] 5 raw material Model / Specification number of copies supplier 1 Vinyl chloride copolymer resin BL—2 60 Jiangsu Bat Plastic Co., Ltd. 2 impact modifier NBR3305 10 blue 3 plant fibres 90 mesh 30 Mujiang Weihua Perfume Factory 4 coupling agent titanate 3 Taichang Chemical 5 smoke suppressant Imported from Taiwan 20 Dongguan Maoya Trading Co., Ltd. 6 white clay 800 mesh 5 Nanchang Lanxiang Chemical Co., Ltd. 7 lubricant PE wax 1.5 Dongguan Hengtai Chemical 8 activator Zinc oxide 6 Shanghai Jinghua Chemical Co., Ltd. 9 Environmental Flame Retardant Ammonium polyphosphate 10 Beijing Oriental Aohan Company 10 Heat stabilizers Calc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of ecological wood and provides ecological wood and a preparation method thereof. The ecological wood has the advantages of good waterproof and moisture-proof effects, no harmful substances such as formaldehyde, methylbenzene and the like, good flame-retardant effect, small smoke production volume, good ductility, toughness and impact resistance, recyclability, acid / alkali corrosion resistance and long service life. The ecological wood comprises the following ingredients in parts by weight: 60-70 parts of chloride-vinegar copolymer resin, 9-11 parts of impact modifier, 20-30 parts of plant fiber, 1-3 parts of coupling agent, 10-20 parts of smoke inhibitor, 5-15 parts of activated clay, 0.5-1.5 parts of lubricant, 4-6 parts of activator, 8-10 parts of environment-friendly flame retardant, 4-8 parts of heat stabilizer, 0.5-1.5 parts of odorless crosslinker, 1-5 parts of foaming agent and 1-5 parts of deammoniation agent. The ecological wood is prepared in a manner that all the ingredients are subjected to pretreatment by the plant fiber, mixing by a closed mixer, cooking by an open mixer, tabletting by a tabletting machine and closed-pore foaming in a mold, cooling and mold stabilizing.

Description

technical field [0001] The invention relates to the field of ecological wood, in particular to an ecological wood and a preparation method thereof. Background technique [0002] At present, the decorative boards used for furniture, interior and exterior decoration, etc. generally use wooden boards, particle boards, density boards, fiber composite boards, gypsum and fiber composite boards, and fireproof boards. Among them: wooden boards, particle boards, density boards, fiber composite boards, gypsum and fiber composite boards have poor flame retardancy and fire resistance, and the amount of smoke generated during the combustion process is large, which cannot meet the requirements for flame retardancy and fire protection. limitations, and not water-resistant, not moisture-proof. The fireproof board is generally a fireproof sandwich panel made of metal as the panel and flame-retardant core material as the core layer, which is composited by hot pressing. It has good flame-ret...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K13/02C08K3/34C08J9/04B29B7/74B29C44/02
Inventor 侯汝红陈奕汲
Owner YIBAO FUJIAN POLYMER MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com