Method for producing lead-free frosted glass wine bottle

A frosted glass and lead-free glass technology, applied in the field of glass manufacturing, can solve the problems of hindering blood synthesis and high lead toxicity, and achieve the effects of low production cost, simple process and convenient source of raw materials

Inactive Publication Date: 2013-09-18
XINYI XINAODE GLASS PROD LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass is a transparent or translucent solid substance that forms a continuous network structure when it is melted. During the cooling process, the viscosity gradually increases and hardens without crystallization. The silicate non-metallic material, the main variety is silicate glass, of which Silicate glass refers to the glass whose basic composition is silica, in which the content of silica is between 55% and 65%, and it also contains 15% sodium oxide, 15% calcium oxide and a certain amount of lead oxide. Because it contains a certain amount

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] The purchased lead-free white broken glass is sent to the washing machine and rinsed repeatedly with high-pressure water, and then dried naturally.

[0019] The washed lead-free white cullet accounting for 44% of the total, the local quartz sand accounting for 30% of the total, soda ash accounting for 9% of the total, and albite accounting for 12% of the total 4.6% of the calcite, 0.2% of the total amount of sodium sulfate, and 0.2% of the total amount of cobalt powder are sent to the blender and mixed uniformly to obtain the mixture, and the mixture is sent to the kiln through the conveyor. The coal is sent to the boiler for combustion, and the 540℃-560℃ gas obtained from the combustion is sent to the kiln through the gas pipeline for sealed combustion in the kiln, so that the temperature of the mixture reaches 1550℃, and keep this temperature for 28 hours to mix The material reaches a molten state, and a lead-free glass melt is obtained. The lead-free ...

Example Embodiment

[0020] Example 2

[0021] The purchased lead-free white broken glass is sent to the washing machine and rinsed repeatedly with high-pressure water, and then dried naturally.

[0022] The washed lead-free white cullet accounting for 45% of the total, the local quartz sand accounting for 29% of the total, soda ash accounting for 9% of the total, and albite accounting for 12% of the total 4.6% of the calcite, 0.2% of the total amount of sodium sulfate, and 0.2% of the total amount of cobalt powder are sent to the blender and mixed uniformly to obtain the mixture, and the mixture is sent to the kiln through the conveyor. The coal is sent to the boiler for combustion, and the 540℃-560℃ gas obtained from the combustion is sent to the kiln through the gas pipeline for sealed combustion in the kiln, so that the temperature of the mixture reaches 1555℃, and keep this temperature for 27 hours to mix The material reaches a molten state, and a lead-free glass melt is obtained. The lead-free ...

Example Embodiment

[0023] Example 3

[0024] The purchased lead-free white broken glass is sent to the washing machine and rinsed repeatedly with high-pressure water, and then dried naturally.

[0025] The washed lead-free white cullet accounting for 46% of the total, the local quartz sand accounting for 28% of the total, soda ash accounting for 9% of the total, and albite accounting for 12% of the total 4.6% of the calcite, 0.2% of the total amount of sodium sulfate, and 0.2% of the total amount of cobalt powder are sent to the blender and mixed uniformly to obtain the mixture, and the mixture is sent to the kiln through the conveyor. The coal is sent to the boiler for combustion, and the 540℃-560℃ gas obtained from the combustion is sent to the kiln through the gas pipeline for sealed combustion in the kiln, so that the temperature of the mixture reaches -1560℃, and keep this temperature for 26 hours. The mixture reaches a molten state, and a lead-free glass melt is obtained. The lead-free glass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing a lead-free frosted glass wine bottle. The product belongs to the field of glass manufacturing. The method comprises the steps of: by taking lead-free white cullet, white quartz sand, sodium carbonate, soda feldspar, calcite, anhydrous sodium sulphate and cobalt powder as materials and taking a washing machine, a mixing machine, a boiler, a kiln, a molding machine, an annealing box and a frosted glass box as equipments, preparing the lead-free frosted glass wine bottle after washing the lead-free white cullet, mixing, fusing, molding, annealing and frosting all materials. The product has the advantages that main materials are recovered waste lead-free glass products, and are low in price; the quartz sand is abundant in real estate resource source; the product does not contain toxic elements such as lead, arsenic and chromium, and is free of harm to a human body; the product is various in sculpt, and beautiful in appearance; the product is mainly used as fast-moving consumer goods wrappers, such as white spirit, yellow wine and red wine.

Description

technical field [0001] The invention belongs to the field of glass manufacturing, in particular to a method for producing lead-free ground glass wine bottles. Background technique [0002] Glass is a transparent or translucent solid substance that forms a continuous network structure when it is melted. During the cooling process, the viscosity gradually increases and hardens without crystallization. The silicate non-metallic material, the main variety is silicate glass, of which Silicate glass refers to the glass whose basic composition is silica, in which the content of silica is between 55% and 65%, and it also contains 15% sodium oxide, 15% calcium oxide and a certain amount of lead oxide. Because it contains a certain amount of lead, if it is directly used to make tea sets, wine sets, and wine bottles, lead may enter the human body during the process of drinking tea or wine. Although some of the lead that enters the human body can be excreted through feces and sweat , b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C6/02
Inventor 孙敬宝
Owner XINYI XINAODE GLASS PROD LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap