Optical film, polarizing plate and image display device using the same

A technology of optical film and polarizing film, which is applied in the direction of optics, polarizing elements, optical elements, etc., can solve the problem of thickening of surface components, and achieve the effects of high productivity, high surface hardness, and excellent black density

Active Publication Date: 2013-10-23
FUJIFILM CORP
View PDF76 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If it is desired to provide a hard coat film on the surface of the optically anisotropic layer (usually formed by providing a hard coat layer on a transparent support), it becomes hard coat / transparent support / adhesive layer / optical anisotropic Layer / alignment film / transparent support / polarizer / protective film, there is a problem that the surface part (polarizer) becomes thicker

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical film, polarizing plate and image display device using the same
  • Optical film, polarizing plate and image display device using the same
  • Optical film, polarizing plate and image display device using the same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0468] As the solvent used for the preparation of the coating liquid, an organic solvent is preferably used. Examples of organic solvents include amides (such as N,N-dimethylformamide), sulfoxides (such as dimethylsulfoxide), heterocyclic compounds (such as pyridine), hydrocarbons (such as benzene, hexane), alkyl Halides (e.g. chloroform, methylene chloride), esters (e.g. methyl acetate, ethyl acetate, butyl acetate), ketones (e.g. acetone, methyl ethyl ketone), ethers (e.g. tetrahydrofuran, 1,2-dimethoxyethane ). Alkyl halides and ketones are preferred. Two or more organic solvents may be used in combination.

[0469] [Coating method]

[0470] Coating of the coating liquid can be performed by known methods (for example, wire bar coating method, extrusion coating method, direct gravure coating method, reverse gravure coating method, die coating method).

[0471] [Orientation film]

[0472]In the present invention, it is preferable to apply the composition on the surface o...

Embodiment 1

[0500] (Manufacturing of Optical Film 101)

[0501] "Formation of Optically Anisotropic Layers Containing Liquid Crystalline Compounds"

[0502] (alkaline saponification treatment)

[0503] As a transparent support, use TD80UL (manufactured by Fujifilm Co., Ltd., thickness 80 μm), pass it through an induction heating roller at a temperature of 60°C, raise the surface temperature of the film to 40°C, and then place the film on the belt Surface the alkaline solution of the composition shown below with a bar coater at 14ml / m 2 Coated with a coating amount of , it was conveyed under a steam-type far-infrared heater made by Noritake Co. Limited, which had been heated to 110° C., in 10 seconds. Next, use a bar coater in the same way to apply 3ml / m 2 of pure water. Then, after repeating water washing with a fountain coater and dewatering with an air knife three times, it was transported to a drying area at 70°C for 10 seconds and dried to produce an alkali-saponified coating. Ce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

There is provided an optical film including: a transparent support; an optically anisotropic layer on the outermost surface at one side of the transparent support; a hardcoat layer; and a low refractive index layer, wherein the hardcoat layer and the low refractive index layer are provided at the other side of the transparent support, the transparent support, the hardcoat layer, and the low refractive index layer contains an organic fine particles A having a specific particle size, an organic fine particles B having a specific particle size, and a binder such that a refractive index of 1.20 to 1.40 and average film thickness of 50 to 120 nm, a content of the inorganic fine particles B is appropriately controlled, and arithmetic mean roughness Ra of the optical film surface at a side having the low refractive index layer is a specific value.

Description

technical field [0001] The present invention relates to an optical film having an optically anisotropic layer on one side of a transparent support, a hard coat layer and a low-refractive index layer on the other side, a polarizer having the optical film, and an image display device. In particular, the present invention relates to an optical film suitable for use as a surface film for a liquid crystal display device, a polarizing plate including the optical film as a protective film, and the optically anisotropic layer in such a way that the hard coat layer becomes the viewing side and the optically anisotropic layer A liquid crystal display device in which the optical film is disposed on the surface so as to be on the polarizing film side. Background technique [0002] Liquid crystal display devices (LCDs) are widely used due to their thin thickness, light weight, and low power consumption. A liquid crystal display device includes a liquid crystal unit and a polarizer. A p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B1/04G02B5/30G02F1/1335B32B7/02B32B27/30C08K3/00C08L101/00G02B1/10G02B1/11G02B1/111G02B1/14G02F1/13363
CPCG02F1/133528G02B1/105G02B5/30G02B5/3008G02B5/305Y10T428/24364G02B1/14C09K2323/033
Inventor 胁阪大树福田谦一山口智彦
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com