Pesticide suspending agent containing inorganic nano-material and preparation method thereof

A technology of inorganic nanomaterials and suspending agents, applied in the field of pesticides, can solve the problems of fast photolysis of active ingredients, low utilization rate, and environmental pollution, and achieve the effects of increasing the risk of environmental pollution, reducing the amount of use, and protecting the environment

Inactive Publication Date: 2013-11-20
GUANGDONG ZHONGXUN AGRI TECH
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems of excessively fast photolysis and low utilization rat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1 : (5% emamectin suspension concentrate).

[0020] First weigh the following materials in proportion: emamectin 5%, fatty alcohol polyoxyethylene alcohol 1%, naphthalenesulfonate formaldehyde condensate 1.5%, polycarboxylate dispersant 2%, nano-titanium dioxide 5%, White carbon black 1%, aluminum magnesium silicate 1.5%, XG 0.08%, propylene glycol 5%, silicone defoamer 0.3%, deionized water balance. Then use deionized water to dissolve fatty alcohol polyoxyethylene alcohol, naphthalenesulfonate formaldehyde condensate, polycarboxylate dispersant, and propylene glycol, and then add them to the reaction kettle with stirring and mixing functions, turn on the stirring and shearing, and then put the Nano-titanium dioxide and emamectin benzoate raw materials are fully mixed and then added to the reaction kettle. Finally, white carbon black, propylene glycol, and silicone antifoaming agent are added and mixed evenly. , and finally poured into the shearing tank, addi...

Embodiment 2

[0021] Example 2: (5% Abamectin Suspension Concentrate).

[0022] First weigh the following materials in proportion: Abamectin 5%, fatty alcohol polyoxyethylene alcohol 1%, naphthalenesulfonate formaldehyde condensate 1.5%, polycarboxylate dispersant 2%, nano-titanium dioxide 3%, white carbon Black 2% magnesium aluminum silicate 1.5%, XG 0.1%, propylene glycol 5%, silicone defoamer 0.3%, deionized water balance. Then use deionized water to dissolve fatty alcohol polyoxyethylene alcohol, naphthalenesulfonate formaldehyde condensate, polycarboxylate dispersant, and propylene glycol, and then add them to the reaction kettle with stirring and mixing functions, turn on the stirring and shearing, and then put the Nano-titanium dioxide and emamectin benzoate raw materials are fully mixed and then added to the reaction kettle. Finally, white carbon black, propylene glycol, and silicone antifoaming agent are added and mixed evenly. , and finally poured into the shearing tank, adding...

Embodiment 3

[0023] Example 3: (15% indoxacarb suspension).

[0024] First weigh the following materials in proportion: indoxacarb 15%, sodium dioctyl sulfosuccinate 2%, EO-PO block copolymer 2.5%, polycarboxylate dispersant 1%, nano-titanium dioxide 1%, White carbon black 2%, aluminum magnesium silicate 1.5%, XG 0.1%, urea 5%, silicone defoamer 0.3%, deionized water balance. Dissolve diisooctyl sodium sulfosuccinate, EO-PO block copolymer, polycarboxylate dispersant, and urea with deionized water and add them to the reaction kettle with stirring and mixing functions, turn on the stirring and shearing , and then fully mix the nano-titanium dioxide and emamectin benzoate original drug and add it to the reaction kettle, and finally add white carbon black, urea, and organic silicon defoamer to mix evenly, first coarsely pulverize it through a colloid mill, and then grind it to Qualified particle size, finally into the shearing tank, add thickener xanthan gum, shear until qualified

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a pesticide suspending agent containing an inorganic nano-material and a preparation method thereof. The suspending agent comprises the components of pesticide active ingredients, an inorganic nano-material, a wetting dispersant, a thickening agent, an antifreeze, an antifoaming agent and water. The method comprises steps of: dissolving the wetting dispersant and antifreeze with deionized water, and adding the mixture into a reaction kettle; fully mixing the nano-material and an emamectin benzoate chlorfenapyr original drug, and adding the mixture into the reaction kettle; and mixing, grinding and shearing. The pesticide suspending agent provided by the invention has strong anti-photolysis performance, and increases utilization rate of the pesticide and reduces the application amount and usage frequency of the pesticide; in addition, the pesticide suspending agent can sterilize for a long time under the effect of ultraviolet ray in the light, so as to reduce the usage amount of the bactericide pesticide.

Description

technical field [0001] The invention belongs to the field of pesticides, and in particular relates to a pesticide suspension containing inorganic nanomaterials and a preparation method thereof. Background technique [0002] According to research, most of the active ingredients of pesticides will accelerate their decomposition speed under sunlight exposure. If the decomposition speed is not high, it is benign. If the decomposition speed is too fast, it will affect the active ingredients to play a role. This leads to repeated use of pesticides by farmers, which increases costs and increases the risk of environmental pollution. Especially those containing double bond structure in the structure of the active ingredient are especially unstable to light. A large number of studies and literature have shown that photolysis may first be an oxidation reaction, that is, the transition from a non-oxidized state to an oxidized state. The mechanism may be that when the oxygen in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01N59/00A01N25/22A01P1/00A01N43/90A01N47/38A01N43/36
Inventor 彭述明杨勇林阎工程刘鹏
Owner GUANGDONG ZHONGXUN AGRI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap