Preparation method of aluminium-doped cerium-zirconium solid-solution polishing powder

A cerium zirconium solid solution and polishing powder technology, which is applied to polishing compositions containing abrasives, etc., can solve the problems of surface scratches, increased surface roughness, and difficulty in forming a solid solution of a polished workpiece with a doping amount, and achieves low raw material prices, The particle size is uniform and the effect of the synergistic polishing action is pronounced

Active Publication Date: 2013-12-18
HUNAN HAOZHI TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, CeO 2 with Al 2 o 3 It is difficult to form a solid solution, and Al 2 o 3 and ZrO 2 Abrasive particle size and hardness are larger, in CeO 2 The increase of the amount of doping in the medium is likely to cause scratches on the surface of the polished workpiece and increase the surface roughness
Therefore, the existing Zr or Al-doped CeO 2 Polishing powder is rarely used in the field of high-grade optical processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of aluminium-doped cerium-zirconium solid-solution polishing powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The specific preparation steps of this implementation are as follows:

[0026] (1) Preparation of colloidal solution:

[0027] ①. Disperse 9 g of pseudo-boehmite into 80 ml of pure water under high-speed stirring to obtain a solid-liquid mixed slurry for subsequent use;

[0028] 2. Slowly add 3 ml of hydrochloric acid with a mass fraction of 38% dropwise to the standby solid-liquid mixed slurry, and carry out peptization to obtain an aluminum hydroxide colloidal solution for subsequent use;

[0029] ③. Disperse 13.5 g of citric acid in the aluminum hydroxide colloidal solution, and mix well to obtain the colloidal solution A;

[0030] 2. Preparation of mixed system:

[0031] 1. 250 g of cerium carbonate and 11.2 g of zirconium carbonate are dissolved in hydrochloric acid with a mass fraction of 38% respectively, and the pH value of the solution is controlled between 1-1.5. After the dissolution is complete, cerium chloride solution and zirconium chloride solution are ...

Embodiment 2

[0041] This embodiment is basically the same as Embodiment 1, except that the content of zirconium is 4%, and the content of aluminum is 1%.

Embodiment 3

[0043] This embodiment is basically the same as Embodiment 1, except that the content of zirconium is 2%, and the content of aluminum is 1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of aluminium-doped cerium-zirconium solid-solution polishing powder and relates to the technical field of preparation of the polishing powder materials. The preparation method disclosed by the invention comprises the following steps of (1) preparation of colloidal solution; (2) preparation of a mixed system; (3) coprecipitation; and (4) roasting and aftertreatment. The preparation method disclosed by the invention has the characteristics of simple preparation process, cheap and easily available materials and suitability for industrial production and the like, is applicable to the field of processing of high-grade optical instruments and can be especially used for precise optical-glass polishing.

Description

Technical field: [0001] The invention relates to the technical field of preparation of polishing powder materials, in particular to a preparation method of aluminum-doped cerium-zirconium solid solution polishing powder. Background technique: [0002] Due to CeO 2 -ZrO 2 Composite oxide solid solutions have a wide range of applications in the fields of catalysis, fuel cells, ceramics, etc. Therefore, they have received widespread attention from scholars at home and abroad. The research on its synthesis method and application performance has also been quite extensive, but most of them are carried out for the application targets such as catalysis and ceramics, CeO 2 -ZrO 2 The application of composite oxide solid solution as abrasive in the field of chemical mechanical polishing is rare. In fact, CeO 2 and ZrO 2 Both oxides can be used in the polishing of optical glass, especially CeO 2 The application of base polishing powder in cold processing of glass surface, flat g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09G1/02
Inventor 杨广乾巩强
Owner HUNAN HAOZHI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com