Lead plaster composition of positive electrode of internally formalized storage battery

A battery positive electrode and composition technology, applied in battery electrodes, circuits, electrical components, etc., can solve problems such as large sewage, battery capacity attenuation, dust generation, etc.

Active Publication Date: 2014-03-12
HENAN CHAOWEI POWER SUPPLY
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this lead-antimony-cadmium externalized battery are as follows: 1. Since the plates are charged, rinsed and dried before assembly during the externalized formation of the battery, a large amount of sewage and dust are generated; 2. The grid alloy of the externalized battery contains cadmium , and cadmium is a toxic metal banned by the country. In recent years, the country has paid more and more attention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lead plaster composition of positive electrode of internally formalized storage battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] In this embodiment, the positive lead paste composition of internalized battery is made of the following raw materials in parts by weight: 1000 parts of lead powder, 1 part of fiber, 0.75 part of phosphoric acid, 1.5 parts of antimony trioxide, 1 part of zinc oxide, and 1 part of aluminum sesquioxide. 0.6 parts of ammonium bicarbonate, 0.4 parts of cerium hydroxide, 1.1 parts of tin oxide, 120 parts of water, and 85 parts of dilute sulfuric acid.

[0027] The density of dilute sulfuric acid is 1.40 g / cm 3 ; The apparent density of the lead paste composition is 4.4 g / cm 3 .

[0028] Table 1 is a comparison of the technical indicators of the electric vehicle lead-acid battery made of the lead paste of this embodiment (taking 6DZM12 battery as an example). The results show that: the conventional electric bicycle battery can be deeply discharged for 300 cycles, while the lead Batteries made of paste can be improved to 350 times.

[0029]

Embodiment 2

[0031] In this embodiment, the positive lead paste composition of the internalized battery is made of the following raw materials in parts by weight: 990 parts of lead powder, 1.5 parts of fiber, 0.5 part of phosphoric acid, 2 parts of antimony trioxide, 0.7 part of zinc oxide, and 1.5 parts of aluminum sesquioxide. 0.5 parts of ammonium bicarbonate, 0.5 parts of cerium hydroxide, 0.7 parts of tin monoxide, 130 parts of water, and 80 parts of dilute sulfuric acid.

[0032] The density of dilute sulfuric acid is 1.45 g / cm 3 ; The apparent density of the lead paste composition is 4.2 g / cm 3 .

Embodiment 3

[0034] In this embodiment, the positive lead paste composition of the internalized battery is made of the following raw materials in parts by weight: 1010 parts of lead powder, 0.5 part of fiber, 1 part of phosphoric acid, 1 part of antimony trioxide, 1.2 parts of zinc oxide, and 0.5 part of aluminum sesquioxide. 0.8 parts of ammonium bicarbonate, 0.3 parts of cerium hydroxide, 1.5 parts of tin oxide, 110 parts of water, and 90 parts of dilute sulfuric acid.

[0035] The density of dilute sulfuric acid is 1.35 g / cm 3 ; The apparent density of the lead paste composition is 4.6 g / cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Apparent densityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of storage batteries, and specifically relates to a lead plaster composition of a positive electrode of an internally formalized storage battery. The lead plaster composition of the positive electrode of the internally formalized storage battery is prepared from the following raw materials in parts by weight: 990-1010 parts of lead powder, 0.5-1.5 parts of fibers, 0.5-1.0 part of phosphoric acid, 1-2 parts of antimonous oxide, 0.7-1.2 parts of zinc oxide, 0.5-1.5 parts of aluminum oxide, 0.5-0.8 part of ammonium hydrogen carbonate, 0.3-0.5 part of cerium hydroxide, 0.7-1.5 parts of tin monoxide, 110-130 parts of water and 80-90 parts of dilute sulphuric acid. The lead plaster composition of the positive electrode is improved, so that capacity attenuation of the internally formalized battery in the early stage is inhibited, and the service life of deep circular discharge of the battery is prolonged.

Description

technical field [0001] The invention belongs to the technical field of accumulators, and in particular relates to a lead paste composition internalized into a positive electrode of a battery. Background technique [0002] Batteries can be divided into internal formation and external formation. The grid used for external formation contains antimony and cadmium, and the grid used for internal formation contains calcium. During the external formation process, the charge formation time is short, and the formation of the plates is complete. In addition, the formation of the plates can also be visually judged and screened. The role of antimony and cadmium in the grid is: antimony can increase the strength of the grid, which is beneficial to the filling of lead paste without deformation, and cadmium is a compensation for the corrosion resistance of antimony, so the plate containing this alloy has good corrosion resistance. The adhesive force between the paste and the grid is stron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/57H01M4/62
CPCH01M4/57H01M4/62Y02E60/10
Inventor 李松林柴成雷
Owner HENAN CHAOWEI POWER SUPPLY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap