Clean preparation method of hydrocracking catalyst

A hydrocracking and catalyst technology, applied in the direction of physical/chemical process catalysts, molecular sieve catalysts, chemical instruments and methods, etc., can solve problems such as difficult to meet, low metal salt solubility, difficult to prepare high-concentration stable metal salt solution, etc. To achieve the effect of improving efficiency, reducing blocking effect and reducing loss

Active Publication Date: 2016-08-17
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the low solubility of metal salts of group VIII of organic acids, it is difficult to prepare a high-concentration stable metal salt solution, and it is difficult to meet the problems of preparing hydrocracking catalysts by impregnation method. Provide metal ions to make the metal solution in a stable state exceeding saturation, so as to meet the requirements of high concentration and stability of the metal salt solution prepared by the impregnation method, and realize the clean preparation of the hydrocracking catalyst with high metal content by the impregnation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Based on the weight of the final hydrocracking catalyst, it contains 15% of Y molecular sieve, 35% of amorphous silica-alumina, 5.0% of nickel oxide, 22.0% of tungsten oxide, and the balance is alumina. , 3824 aluminum hydroxide dry rubber powder and 3903 amorphous silica aluminum dry rubber powder.

[0035] The catalyst preparation process is as follows: fully mix the modified Y molecular sieve, aluminum hydroxide dry rubber powder, amorphous silica-alumina dry rubber powder, and turnip powder in a kneader, and add a concentration of 13.2g acetic acid / 100mL and 8.0gβ- Carboxyethyl acrylate / 100mL mixed acid solution for peptization, extruded into a cylindrical shape with a diameter of 1.5mm. Then it was dried at 120° C. for 4 hours and calcined at 480° C. for 3 hours to prepare a molded catalyst carrier, and its dry basis was measured. Distilled water is used to prepare a mixed solution of ammonium metatungstate and nickel acetate. For the solution preparation process,...

Embodiment 2

[0037] Based on the weight of the final hydrocracking catalyst, it contains 40% of Y molecular sieve, 15% of amorphous silica-alumina, 5.0% of nickel oxide, 22.0% of tungsten oxide, and the balance is alumina. , 3824 aluminum hydroxide dry rubber powder and 3903 amorphous silica aluminum dry rubber powder.

[0038] The preparation method is the same as in Example 1, the ultrasonic frequency is 80kHz, the power is 35W / mL based on the solution volume, and the catalyst number obtained is CHC-2.

Embodiment 3

[0040] According to the weight of the final hydrocracking catalyst, it contains 55% of Y molecular sieve, 5.0% of nickel oxide, 22.0% of tungsten oxide, and the balance is alumina. Select the aforementioned catalyst for preparation of raw materials: modified Y molecular sieve 1, 3824 aluminum hydroxide dry rubber powder .

[0041] The preparation method is the same as in Example 1, the ultrasonic frequency is 150 kHz, the power is 15 W / mL based on the solution volume, and the catalyst number obtained is CHC-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a clean preparation method of a hydrocracking catalyst. The clean preparation method comprises following steps of: (1) preparing a carrier of the hydrocracking catalyst; (2) preparing a dipping solution containing hydrocracking active components that are metal salts, wherein the hydrocracking active components comprise W and / or Mo in the VIB group and Ni and / or Co in the VIII group, the VIII metal salt is a salt of an organic acid, a dissolution process is performed under stirring at high temperature, the solution is placed in an ultrasonic wave environment and is cooled to the room temperature; and (3) dipping the carrier prepared in the step (1) into a measured amount of the metal salt dipping solution prepared in the step (2) with the dipping process being in an ultrasonic wave environment; performing solid-liquid separation after the dipping step, drying the dipped catalyst and calcinating to obtain a catalyst product. According to the clean preparation method, a pollution problem in the catalyst production process is overcome under the premise of guaranteeing the using performances of the catalyst, thus achieving clean production of the catalyst.

Description

technical field [0001] The present invention relates to a kind of preparation method of hydrocracking catalyst, especially in the preparation process without NO x Process for the preparation of vented hydrocracking catalysts. technical background [0002] Hydrocracking technology has the characteristics of strong adaptability to raw materials, great flexibility in production operations and product plans, and good product quality. It can directly convert various heavy and low-quality feedstocks into high-quality jet fuel, diesel, and lubricating oil base materials that are urgently needed by the market. As well as chemical naphtha and steam cracking ethylene feedstock (hydrocracking tail oil), it has become one of the most important heavy oil deep processing processes in modern oil refining and petrochemical industries, and has been increasingly widely used at home and abroad. The key to hydrocracking technology is hydrocracking catalyst, and its improvement depends on the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/16C10G47/20
Inventor 杜艳泽范丹丹王凤来
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products