Method for preparing geopolymer adsorption material by using Bayer process red mud

A Bayer method red mud and adsorption material technology, applied in the field of inorganic non-metallic material preparation, can solve the problem of no substantial progress in the comprehensive utilization of Bayer method red mud, and achieve the effects of strong scalability, small environmental impact, and simple process

Active Publication Date: 2014-07-16
徐州星皓乐器有限公司
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the treatment of red mud is mainly used for building materials and extracting useful substances from it. After a lot of experimental research, the application of sintered red mud in building materials has entered the stage of large-scale production, and has accumulated decades of production experience , and there is no substantial progress in the comprehensive utilization of Bayer process red mud

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] (1) First, kaolin and red mud are dried to a moisture content of 0.8%, and then the kaolin is calcined at 800°C for 6 hours and then ball milled to a specific surface area of ​​800m 2 / Kg, ball mill the red mud to a specific surface area of ​​400m 2 / Kg.

[0018] (2) Mix the red mud treated in step (1) with the calcined kaolin treated in step (1) at a mass ratio of 3:7.

[0019] (3) Utilize chemically pure NaOH to transfer high-modulus industrial water glass to a water glass solution with a modulus of 1.5.

[0020] (4) the mixture that step (2) is made is placed in stirring pot, then add the water glass solution that the modulus that a certain amount of step (3) makes is 1.5, make the sodium oxide quality in the water glass solution be step ( 2) 8% of the total mass of the prepared mixture, the water-cement ratio of the slurry is 0.36, and the mixture is evenly stirred.

[0021] (5) get the aluminum powder that accounts for the mixture gross mass 0.05 wt% that step (...

Embodiment 2

[0023] (1) First, kaolin and red mud are dried to a moisture content of 0.5%, and then the kaolin is calcined at 800°C for 6 hours and then ball milled to a specific surface area of ​​800m 2 / Kg, ball mill the red mud to a specific surface area of ​​400m 2 / Kg.

[0024] (2) Mix the red mud treated in step (1) with the calcined kaolin treated in step (1) at a mass ratio of 1:1.

[0025] (3) Utilize chemically pure NaOH to transfer high-modulus industrial water glass to a water glass solution with a modulus of 1.5.

[0026] (4) the mixture that step (2) is made is placed in stirring pot, then add the water glass solution that the modulus that a certain amount of step (3) makes is 1.5, make the sodium oxide quality in the water glass solution be step ( 2) 8% of the total mass of the prepared mixture, the water-cement ratio of the slurry is 0.36, and the mixture is evenly stirred.

[0027] (5) get the aluminum powder that accounts for the mixture gross mass 0.06 wt% that step (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing geopolymer adsorption material by using Bayer process red mud. According to the invention, kaolin and red mud are respectively dried, kaolin is calcined after ball milling, then red mud and calcined kaolin are mixed according to mass ratio of 3: 7-6: 4, placed in a stirring pan, a soluble glass solution with 1.5 of modulus is added for uniformly stirring until the sodium oxide mass in the soluble glass solution accounts for 8% of total mass of a mixture of the calcined kaolin and red mud, the water cement ratio of the slurry is 0.35-0.38; a proper amount of aluminum powder and powdered soap are placed in a few water, and uniformly dispersed and then added in the obtained slurry, uniformly stirred; after waiting for 3-5 minutes, the expanded slurry is filled in a die, and the expanded slurry is placed in a baking oven with the die or placed in the baking oven without die for maintenance, so that the geopolymer adsorption material is prepared. The method has the advantages of simple equipment, low cost, easy popularization and little environmental influence, the prepared geopolymer adsorption material has the advantages of uniform pore and high strength, and can be reused after being processed by an acid solution.

Description

technical field [0001] The invention belongs to the technical field of preparation of inorganic non-metallic materials, and in particular relates to a method for preparing geopolymer adsorption materials by using Bayer process red mud. Background technique [0002] Geopolymer materials are completely different from Portland cement in terms of mineral composition. It is composed of amorphous minerals, and its main raw material is high-activity metakaolin; alkaline activators (caustic potash, caustic soda, water glass, potassium silicate etc.); hardening accelerator (calcium silicate and silica fume with low calcium-silicon ratio, all of which are amorphous); admixture (mainly retarder). After entering the 1990s, the selection range of raw materials and activators has been greatly expanded, and the sources of silicon-alumina raw materials have been expanded to four categories: volcanic zeolite, fly ash, mineral waste residue, and burnt clay; activators include single alkali me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/16B01J20/30C02F1/28
Inventor 朱文凤彭鹏王林江王斌王珏
Owner 徐州星皓乐器有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com