A protein plastic material
A technology of plastic materials and proteins, applied in the field of plastics, can solve the problems of large consumption of agricultural products, low tensile strength, high brittleness, etc., to improve ductility, tensile and impact resistance, and wear resistance. The effect of tearing properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0012] A kind of protein plastic material that the present invention proposes, its raw material comprises by weight: polybutylene succinate PBS50 parts, poly-beta-hydroxybutyric acid PHB30 parts, peanut protein powder 25 parts, potassium titanate fiber 2.5 parts 7 parts of silk fiber, 1.2 parts of silane coupling agent KH570, 3 parts of sodium sorbate, 1.1 parts of ethyl p-hydroxybenzoate, 1.9 parts of diisooctyl phthalate DIOP, 3 parts of epoxy soybean oil , 5 parts of acetate starch, 15 parts of talcum powder, 11 parts of wollastonite powder, 5 parts of calcite powder, 1.4 parts of tert-butyl hydroquinone TBHQ;
[0013] During the preparation process, the silane coupling agent KH570 was added to the potassium titanate fiber and stirred at a stirring speed of 27rpm for 8min, then silk fiber was added and stirred at a stirring speed of 30rpm for 8min, then peanut protein powder was added and stirred at a stirring speed of 38rpm for 6min , then add polybutylene succinate PBS, p...
Embodiment 2
[0015] A kind of protein plastic material proposed by the present invention, its raw material comprises by weight: 45 parts of polybutylene succinate PBS, 35 parts of poly-beta-hydroxybutyric acid PHB, 20 parts of peanut protein powder, 3 parts of potassium titanate fiber , 5 parts of silk fiber, 1.7 parts of silane coupling agent KH570, 2 parts of sodium sorbate, 1.6 parts of ethyl p-hydroxybenzoate, 1.7 parts of diisooctyl phthalate DIOP, 6 parts of epoxy soybean oil, 3 parts of acetate starch, 18 parts of talc powder, 7 parts of wollastonite powder, 9 parts of calcite powder, 1 part of tert-butyl hydroquinone TBHQ;
[0016] During the preparation process, the silane coupling agent KH570 was added to the potassium titanate fiber and stirred at a stirring speed of 24rpm for 9min, then silk fiber was added and stirred at a stirring speed of 25rpm for 11min, then peanut protein powder was added and stirred at a stirring speed of 37rpm for 7min , then add polybutylene succinate ...
Embodiment 3
[0018] A kind of protein plastic material that the present invention proposes, its raw material comprises by weight: polybutylene succinate PBS part, poly-beta-hydroxybutyric acid PHB31 parts, peanut protein powder 24 parts, potassium titanate fiber 2.7 parts , 6.5 parts of silk fiber, 1.3 parts of silane coupling agent KH570, 2.7 parts of sodium sorbate, 1.2 parts of ethyl p-hydroxybenzoate, 1.82 parts of diisooctyl phthalate DIOP, 3.4 parts of epoxy soybean oil, 4.5 parts of acetate starch, 16 parts of talcum powder, 10 parts of wollastonite powder, 6 parts of calcite powder, 1.3 parts of tert-butyl hydroquinone TBHQ.
[0019] During the preparation process, the silane coupling agent KH570 was added to the potassium titanate fiber and stirred at a stirring speed of 30rpm for 5min, then silk fiber was added and stirred at a stirring speed of 32rpm for 7min, then peanut protein powder was added and stirred at a stirring speed of 40rpm for 5min , then add polybutylene succinate...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com