Blue phosphorescence material iridium metal complex, preparation method and organic electroluminescent device

A technology of iridium metal complexes and blue phosphorescence, which is applied in luminescent materials, electrical solid devices, organic chemistry, etc., and can solve the problems of lagging development and poor luminous performance of light-emitting devices

Inactive Publication Date: 2014-12-03
OCEANS KING LIGHTING SCI&TECH CO LTD +2
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with red light and green light materials, the development of blue light materials is relatively lagging behind. Improving the efficiency and color purity of blue light materials has become the breakthrough point of people's research. There are bottleneck problems in terms of efficiency and device efficiency attenuation, which makes the luminous performance of organic electroluminescent devices poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blue phosphorescence material iridium metal complex, preparation method and organic electroluminescent device
  • Blue phosphorescence material iridium metal complex, preparation method and organic electroluminescent device
  • Blue phosphorescence material iridium metal complex, preparation method and organic electroluminescent device

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] see figure 1 , the preparation method of the blue phosphorescence iridium metal complex of an embodiment, comprises the steps:

[0042] Step S110: In a protective gas atmosphere, dissolve compound F and 2,4-bis(trifluoromethyl)phenylboronic acid in a molar ratio of 1:1 to 1.5 in the first solvent, and add an organopalladium catalyst and carbonic acid The aqueous solution of salt, carry out Suzuki coupling reaction 8~15 hours, obtain compound A after separation and purification, the structural formula of compound F is The structural formula of compound A is Wherein, R is hydrogen or an alkyl group having 1 to 20 carbon atoms.

[0043] The protective gas is argon, helium or neon.

[0044] The first solvent is toluene or N.N-dimethylformamide DMF. The amount of the first solvent is suitable for fully dissolving compound F and 2,4-bis(trifluoromethyl)phenylboronic acid. Preferably, the concentration of compound F in the first solvent is 0.07-0.125 mol / L.

[0045] Th...

Embodiment 1

[0073] Blue phosphorescent bis(2-(4',6'-bis(trifluoromethyl)phenyl)pyrimidine-N,C 2' )(2,4-bis(trifluoromethyl)-5-(pyridin-2'-yl)pyrrole)iridium complex

[0074] Blue phosphorescent bis(2-(4',6'-bis(trifluoromethyl)phenyl)pyrimidine-N,C 2' ) (2,4-bis(trifluoromethyl)-5-(pyridine-2'-yl)pyrrole) iridium complex has the following structural formula:

[0075]

[0076] (1) Synthesis of 2-(2',4'-bis(trifluoromethyl)phenyl)pyrimidine

[0077]

[0078] Under nitrogen protection, 0.79g (5mmol) of 2-bromopyrimidine, 1.55g (6mmol) of 2,4-bis(trifluoromethyl)phenylboronic acid and 0.23g (0.2mmol) of tetrakis(triphenylphosphine)palladium were dissolved in 30 mL of tetrahydrofuran, and then 10 mL of an aqueous solution containing 1.38 g (10 mmol) of potassium carbonate was added dropwise to the reaction system. Heated and stirred under reflux for 15h. After the reaction solution was cooled to room temperature, it was extracted with dichloromethane, separated, washed with water unt...

Embodiment 2

[0100] Blue Phosphorescent Bis(2-(4',6'-bis(trifluoromethyl)phenyl)-5-methylpyrimidine-N,C 2' )(2,4-bis(trifluoromethyl)-5-(pyridin-2'-yl)pyrrole)iridium complex

[0101] Blue Phosphorescent Bis(2-(4',6'-bis(trifluoromethyl)phenyl)-5-methylpyrimidine-N,C 2' ) (2,4-bis(trifluoromethyl)-5-(pyridine-2'-yl)pyrrole) iridium complex has the following structural formula:

[0102]

[0103] (1) Synthesis of 2-(2',4'-bis(trifluoromethyl)phenyl)-5-methylpyrimidine

[0104]

[0105] Under nitrogen protection, 0.86g (5mmol) 2-bromo-5-methylpyrimidine, 1.29g (5mmol) 2,4-bis(trifluoromethyl)phenylboronic acid and 0.35g (0.30mmol) tetrakis(triphenylphosphine) ) and palladium were dissolved in 40mL of toluene, and then 15mL of an aqueous solution containing 2.76g (20mmol) of potassium carbonate was added dropwise to the reaction system. Heated and stirred under reflux for 10h. After the reaction solution was cooled to room temperature, it was extracted with dichloromethane, separated...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a blue phosphorescence material iridium metal complex, its preparation method and an organic electroluminescent device. The blue phosphorescence iridium metal complex is characterized in that the structural formula of the blue phosphorescence iridium metal complex is as defined in the specification, wherein R is hydrogen or an alkyl group with carbon atom number being 1-20. By the use of the above blue phosphorescence iridium metal complex, electroluminescent performance of the organic electroluminescent device can be raised.

Description

technical field [0001] The invention relates to the technical field of electroluminescent materials, in particular to a blue phosphorescent material iridium metal complex, a preparation method thereof and an organic electroluminescent device. Background technique [0002] Organic electroluminescence refers to a luminescence phenomenon in which organic materials directly convert electrical energy into light energy under the action of an electric field. In the early days, the research on organic electroluminescence was stagnant because of the high driving voltage and low luminous efficiency of organic electroluminescent devices. Until 1987, people such as Tang of American Kodak Company invented 8-hydroxyquinoline aluminum (Alq 3 ) is a light-emitting material, and a uniform and dense high-quality thin film is made with aromatic diamines, and an organic electroluminescent device with low operating voltage, high brightness, and high efficiency is prepared, which opens a new pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F15/00C09K11/06H01L51/54
Inventor 周明杰王平张娟娟张振华
Owner OCEANS KING LIGHTING SCI&TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com