Modified attapulgite heavy metal ion adsorbing agent and preparation method thereof

A technology of modifying attapulgite and heavy metal ions, which is applied in chemical instruments and methods, adsorption water/sewage treatment, and other chemical processes. It can solve the problems that the performance cannot meet the needs of production and life, and achieve increased acid and salt resistance. The effect of uniform modification and increased dispersion

Active Publication Date: 2014-12-10
MINGGUANG GUOXING ATTAPULGITE CLAY
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current modified attapulgite cannot meet the needs of production and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] A modified attapulgite heavy metal ion adsorbent made of the following parts by weight (kg) of raw materials: ammonium sulfate 1.5, water glass 2.5, malonic acid 2.5, layered expanded vermiculite 7, citronellol 0.3, belt Amino silane coupling agent 1.5, sodium carboxymethyl cellulose 1.5, attapulgite 110, appropriate amount of water, auxiliary agent 7, 2.5% sodium hydroxide solution 25;

[0016] The additives are made of the following parts by weight (kg) of raw materials: isooctyl palmitate 0.2, porous silica beads 2.5, polyurethane resin 0.5, ethylene glycol 4, vitamin E 0.4, activated alumina 0.4, linoleic acid 0.3, sodium lignosulfonate 0.4, pearl powder 1.3, bamboo fiber 0.2, magnesium sulfate heptahydrate 0.2, charcoal powder 2.5, succinic acid 0.2, aluminum distearate 0.3, medical stone powder 4, silane coupling agent KH-5721.5 The preparation method is: mix and grind the porous silica beads, pearl powder, charcoal powder, medical stone powder, and silane coupling a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a modified attapulgite heavy metal ion adsorbing agent. The modified attapulgite heavy metal ion adsorbing agent is prepared from the following raw materials in parts by weight: 1 to 2 parts of ammonium sulfate, 2 to 3 parts of water glass, 2 to 3 parts of malonic acid, 6 to 9 parts of layering expanded vermiculite, 0.2 to 0.4 part of citronellol, 1 to 2 parts of a silane coupling agent with amino group, 1 to 2 parts of sodium carboxymethylcellulose, 100 to 120 parts of attapulgite, an appropriate amount of water, 5 to 10 parts of assistants and 20 to 30 parts of a 2% to 3% sodium hydroxide solution. The dispersibility, suspension property, adsorption property and thickening performance of the attapulgite are improved, and the attapulgite is endowed with acid resistance and salt resistance as well as a toxic-free property; the attapulgite modification agent is uniform in modification and unlikely to drop, can be used as an adsorbing agent or a flocculating agent and can remove heavy metal ions, such as copper, in water.

Description

technical field [0001] The invention belongs to the field of attapulgite processing, in particular to a modified attapulgite heavy metal ion adsorbent and a preparation method thereof. Background technique [0002] Attapulgite has good colloidal properties such as unique dispersion, high temperature resistance, salt and alkali resistance, and high adsorption and decolorization ability. It also has certain plasticity and cohesive force, strong water absorption, stickiness and plasticity when wet, small shrinkage after drying, no obvious cracks, soaking in water and disintegration, and suspension does not flocculate and precipitate when it encounters dielectrics. Therefore, attapulgite is widely used in many fields such as sewage treatment, adsorption purification, detergent, rubber, paint, papermaking, light industry, agriculture, cosmetics, etc. It is an important non-metallic mineral. [0003] In order to further improve the use effect of attapulgite and enhance its overal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/26B01J20/30C02F1/28C02F1/52C02F1/62
Inventor 李振国
Owner MINGGUANG GUOXING ATTAPULGITE CLAY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap