A kind of preparation method of macromolecule crosslinking agent for ultraviolet light crosslinking polyolefin

A macromolecular cross-linking agent and cross-linked polyolefin technology, which is applied in the field of preparation of macromolecular cross-linking agents, can solve the problems of easy volatilization and migration, reduced cross-linking efficiency, high vapor pressure, etc., and achieve molecular weight increase and conversion rate High, vapor pressure reduction effect

Active Publication Date: 2016-07-13
UNIV OF SCI & TECH OF CHINA
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the crosslinking agent used also has a high vapor pressure at the processing temperature, which is easy to volatilize and migrate, resulting in a decrease in crosslinking efficiency and polluting the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of macromolecule crosslinking agent for ultraviolet light crosslinking polyolefin
  • A kind of preparation method of macromolecule crosslinking agent for ultraviolet light crosslinking polyolefin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Under the conditions of nitrogen atmosphere and ice-water bath, 30g1,6-hexanediol bis(2-mercaptoacetate) and 70.2g triallyl isocyanate were dissolved in 76g toluene respectively, mixed and stirred evenly and Add 1.0g of azobisisobutyronitrile, and slowly heat to 65°C to react until 2570cm on the infrared spectrum -1 The characteristic peak of the mercapto group disappears; after the reaction, the solvent is evaporated to dryness to obtain an allyl-type macromolecular cross-linking agent.

[0027] figure 1 It is the infrared spectrogram of the macromolecular crosslinking agent used for ultraviolet light crosslinking polyolefin prepared in this embodiment. Depend on figure 1 It can be seen that 2570cm -1 The characteristic absorption peak of the sulfhydryl group disappears, indicating that the dithiol compound is completely consumed; 3082cm -1 ,993cm -1 It is the absorption peak of the C-H bond on the allyl group, 2943cm -1 It is the absorption peak of the C-H bond ...

Embodiment 2

[0035] Under nitrogen atmosphere and room temperature, 20g of 1,4-butanediol bis(3-mercaptopropionate) and 57.3g of trimethylolpropane triallyl ether were respectively dissolved in 77g of acetonitrile, mixed and stirred evenly and added 1.55g benzoin dimethyl ether, at 20mw / cm 2 Under the irradiation of ultraviolet lamp, the reaction is carried out until 2570cm on the infrared spectrum -1 The characteristic peak of the mercapto group disappears; after the reaction, the solvent is evaporated to dryness to obtain an allyl-type macromolecular cross-linking agent.

[0036] The molecular weight and distribution of the macromolecular crosslinking agent prepared in this example were measured by gel permeation chromatography, and the number average molecular weight was measured to be 3800, and the molecular weight distribution was 2.1. It can be seen that the molecular weight of the macromolecular crosslinking agent prepared in this example is much larger than that of the small molec...

Embodiment 3

[0042] Under the condition of nitrogen atmosphere and ice-water bath, 30g triethylene glycol bis(2-mercaptoacetate) and 33.5g pentaerythritol triallyl ether were respectively dissolved in 95g xylene, mixed and stirred evenly and added 0.51 g benzoyl peroxide, slowly heated to 70 ° C to react until 2570 cm on the infrared spectrum -1 The characteristic peak of the mercapto group disappears; after the reaction, the solvent is evaporated to dryness to obtain an allyl-type macromolecular cross-linking agent.

[0043] The molecular weight and distribution of the macromolecular crosslinking agent prepared in this example were measured by gel permeation chromatography, and the number average molecular weight was measured to be 7300, and the molecular weight distribution was 1.9. It can be seen that the molecular weight of the macromolecular crosslinking agent prepared in this example is much larger than that of the small molecular crosslinking agent pentaerythritol triallyl ether (it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a macromolecular crosslinking agent used for ultraviolet light crosslinking polyolefin, which is to add a dimercapto compound, an allyl crosslinking agent and an initiator into a solvent, and react under the condition of nitrogen protection To 2570cm on the infrared spectrum -1 The characteristic peak of the mercapto group disappears, and the solvent is removed after the reaction to obtain a macromolecular crosslinking agent with a hyperbranched structure. Compared with the small molecular crosslinking agent, the molecular weight of the macromolecular crosslinking agent of the present invention is significantly improved, and the volatility under the same operating temperature is significantly reduced; at the same time, due to the uniqueness of the hyperbranched structure, the macromolecular crosslinking agent of the present invention has many terminal groups Group, good cross-linking effect. The preparation method adopted in the present invention has mild reaction conditions, high conversion rate, simple and easy operation, and effectively solves the volatility and migration problems of small molecule crosslinking agents in the storage and processing of ultraviolet light crosslinked polyolefins, and It has high cross-linking efficiency and good compatibility with polyolefins.

Description

1. Technical field [0001] The invention relates to a macromolecular crosslinking agent, in particular to a preparation method of the macromolecular crosslinking agent used for ultraviolet light crosslinking polyolefin. 2. Background technology [0002] Polyolefin is the most widely used general-purpose thermoplastic polymer material among polymer materials, and plays a huge role in national economic construction and daily life. However, polyolefins generally have low softening points and mechanical strengths, limiting their applications. The most effective way to improve the performance of polyolefin is to promote its crosslinking to form a three-dimensional network structure, which will significantly increase its service temperature and enhance its resistance to stress cracking. Cross-linked polyolefins have become increasingly important and widely used polymeric materials. [0003] Ultraviolet light cross-linking is a newest method for producing cross-linked polyolefin d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G83/00C08L23/06C08L87/00C08J3/28C08J3/24
Inventor 谢寒吴强华施文芳瞿保钧
Owner UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com