Foam brick produced from biogas residues and preparation method thereof

A technology of biogas slag and foam bricks, applied in the field of foam bricks and its preparation, can solve problems such as environmental pollution, inconvenience in production and life, occupation of land resources, etc., achieve high environmental and economic benefits, protect the environment, and save resources

Inactive Publication Date: 2015-02-18
HEFEI KANGLING HEALTH TECH
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical properties of waste glass are stable, which not only brings inconvenience to people's producti...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] Non-limiting examples of the present invention are as follows:

[0020] A foam brick produced from biogas slag is prepared from the following component raw materials in weight (kg):

[0021] Waste glass 65, biogas slag 18, attapulgite 8, plant ash 8, bamboo charcoal powder 4, sisal fiber 4, sodium tripolyphosphate 3, tartaric acid 3, carboxymethyl chitosan 1.5, sodium lauryl sulfate 1- 2. Polyvinyl alcohol 0.8, modification additive 3, water 55;

[0022] Among them, the modified auxiliary agent is made of the following weight (kg) of raw materials:

[0023] Nano zinc oxide 3, nano titanium dioxide 4, nano silicon dioxide 3, triethanolamine 3, sorbitol 1.5, polyethylene glycol 1.5, gallic acid 0.15, tannic acid 0.8, isopropanol 1.5, silane coupling agent KH-550 0.15;

[0024] The preparation method of modified auxiliary agent:

[0025] Add nano-zinc oxide, nano-titanium dioxide and nano-silica to ultrasonic dispersion after adding appropriate amount of ethanol, then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a foam brick produced from biogas residues. The foam brick is characterized by being prepared from the following raw materials in parts by weight: 60-70 parts of waste glass, 15-10 parts of biogas residues, 5-10 parts of attapulgite, 5-10 parts of plant ash, 3-5 parts of bamboo charcoal powder, 3-5 parts of sisal fiber, 2-4 parts of sodium tripolyphosphate, 2-4 parts of tartaric acid, 1-2 parts of carboxymethyl chitosan, 1-2 parts of lauryl sodium sulfate, 0.5-1 part of polyvinyl alcohol, 2-4 parts of a modifying additive and 50-60 parts of water. The waste residues generated by a biogas digester are recycled to produce the foam brick, the effects of saving resources, protecting environment and reducing cost are achieved, the product performance reaches the standard, and the foam brick is safe, harmless and high in environmental and economic benefits.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a foam brick produced by using biogas slag and a preparation method thereof. Background technique [0002] Foam brick is a kind of aerated concrete block. After using a foaming agent to physically foam through a foaming machine, the air bubbles are added to the slurry for mixing, pouring, and finally a foam brick with internal pores is obtained. Foam bricks are mainly used for non-load-bearing walls. They have the characteristics of low cost, light weight, and good thermal insulation effects. They have been widely used in industrial and civil buildings and are a wall material with good performance. [0003] Glass materials are indispensable and indispensable materials for people's daily life. The extensive use of glass also leads to the inevitable generation of a large amount of waste glass waste in daily production and life. The chemical properties of waste glass are stable, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/02B09B3/00
Inventor 张百庆韩立平
Owner HEFEI KANGLING HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap