Environmental-friendly foam brick and preparation method thereof

A green and environmentally friendly foam brick technology, applied in the field of building materials, can solve problems such as environmental pollution, occupation of land resources, inconvenience in production and life, etc., achieve good thermal insulation performance, clean indoor environment, and improve durability and stability. Effect

Inactive Publication Date: 2015-02-18
HEFEI KANGLING HEALTH TECH
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical properties of waste glass are stable, which not only brings inconvenience to people's production and life, but also pollutes the environment, and the placement of waste glass takes up a lot of land resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Non-limiting examples of the present invention are as follows:

[0022] A kind of green environmental protection foam brick, is prepared from the component raw material of following weight (kg):

[0023] Waste glass 55, medical stone powder 4, river sand 12, olive oil 8, citric acid fatty acid glyceride 0.15, sodium lauryl sulfate 0.8, sodium carbonate 1.5, sodium tripolyphosphate 1.5, water-soluble lanolin 0.4, calcium oxalate 4. Sodium dodecylbenzene sulfonate 0.3, organosilicon quaternary ammonium salt 3, composite filler 18, water 55;

[0024] Among them, the composite filler is made of raw materials with the following weight (kg):

[0025] Bagasse 12, Bran 4, Peanut Hull 4, Oat Hull 3, Tea Seed Hull 3, Bean Cake Powder 4, Alfalfa Powder 2, Superphosphate 3, Calcium Citrate 3, Potassium Dihydrogen Phosphate 0.8, Triethanolamine 4, Water 12;

[0026] Preparation method of composite filler:

[0027] Bagasse, bran, peanut husk, oat husk, tea seed husk and superphos...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environmental-friendly foam brick which is characterized by being prepared from the following raw materials in parts by weight: 50-60 parts of waste glass, 3-5 parts of medical stone powder, 10-15 parts of river sand, 6-10 parts of olive oil, 0.1-0.2 part of citrem, 0.5-1 part of sodium dodecyl sulfate, 1-2 part of sodium carbonate, 1-2 parts of sodium tripolyphosphate, 0.3-0.5 parts of water-soluble lanolin, 3-5 parts of calcium oxalate, 0.2-0.4 part of sodium dodecyl benzene sulfonate, 2-4 parts of organosilicon quaternary ammonium salt, 15-20 parts of composite fillers and 50-60 parts of water. The foam brick uses the waste glass and agricultural wastes as main raw materials, is natural, environmental-friendly, safe and harmless, has a good heat insulation performance, a good antibacterial mouldproof performance and a high mechanical property, and is suitable for indoor environment.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a green and environment-friendly foam brick and a preparation method thereof. Background technique [0002] Foam brick is a kind of aerated concrete block. After using a foaming agent to physically foam through a foaming machine, the air bubbles are added to the slurry for mixing, pouring, and finally a foam brick with internal pores is obtained. Foam bricks are mainly used for non-load-bearing walls. They have the characteristics of low cost, light weight, and good thermal insulation effects. They have been widely used in industrial and civil buildings and are a wall material with good performance. [0003] Glass materials are indispensable and indispensable materials for people's daily life. The extensive use of glass also leads to the inevitable generation of a large amount of waste glass waste in daily production and life. The chemical properties of waste glass are stable,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B41/47B09B3/00
Inventor 张百庆韩立平
Owner HEFEI KANGLING HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap