Environment-friendly type self-crosslinking water and oil repellent textile finishing agent and preparation method thereof

A fabric finishing agent, water-repellent and oil-repellent technology, applied in fiber treatment, textiles and papermaking, etc., can solve the problems of continuous processing, affect the quality stability of finished textiles, affect the utilization rate of finishing agents, etc., and achieve excellent water repellency Effect of oil repellency, improvement of processing continuity, and reduction of migration

Active Publication Date: 2015-02-18
ANHUI LINGDA CHEM TECH
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In addition, the processing sustainability of short fluorocarbon chain emulsion polymers has always been a problem in the dyeing and finishing industry, which affects the quality stability of the finished textiles and the utilization rate of the finishing agent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly type self-crosslinking water and oil repellent textile finishing agent and preparation method thereof
  • Environment-friendly type self-crosslinking water and oil repellent textile finishing agent and preparation method thereof
  • Environment-friendly type self-crosslinking water and oil repellent textile finishing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 0.8g Span 80, 0.5g octadecyl trimethyl chloride (bromide) ammonium, 2.0g N-(perfluorooctylethyl acetate)-N-(ethanol acrylate) dimethyl bromide Mix ammonium, 1.4g butyl acrylate, 0.6g glycidyl acrylate, 0.2g azobisisobutyronitrile and 40g deionized water, stir and emulsify at high speed under nitrogen protection for 15-20 minutes, and heat up to 65°C-70°C , keep warm for 25 minutes to prepare the seed emulsion;

[0035] The emulsion changes from gray to blue light translucence, and 12.6g of butyl acrylate, 5.4g of glycidyl acrylate, 4g of perfluorohexylethyl acrylate, 0.6g of azobisisobutyronitrile and 2g of vinyl are continuously added to the above seed emulsion Add the mixed solution of trimethoxysilane dropwise within 2 hours under the condition of 65°C-70°C; after adding all the materials, keep it warm for 2 hours; cool down to below 50°C; finally, filter to obtain the product.

[0036] In this embodiment, the total amount of organic fluorine materials accounts for ...

Embodiment 2

[0038] 0.5g Span 85, 0.5g hexadecyl trimethyl quaternary ammonium salt, 3.6g N-(perfluorooctyl isobutyl acetate)-N-(butanol acrylate) dimethyl ammonium bromide , 1.4g butyl acrylate, 0.1g azobisisoheptanonitrile, 0.2g V50 and 45g deionized water were mixed together, stirred and emulsified at high speed under nitrogen protection for 20 minutes, heated to 60°C-65°C, kept for 30 minutes, prepared get seed emulsion;

[0039] The emulsion changes from gray to blue light translucent, and 10g of butyl acrylate, 4g of methyl methacrylate, 6g of perfluorohexyl ethyl acrylate, 0.4g of azobisisobutyronitrile, 0.3g of V50 and 4g of The mixed solution of vinyltriethoxysilane is added dropwise within 2 hours under the condition of 60℃~65℃; after all the materials are added, it is kept for 2 hours; the temperature is lowered to below 50℃; finally, the product is obtained by filtration.

[0040] In this embodiment, the total amount of organic fluorine materials accounts for 32% of the total ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly type self-crosslinking water and oil repellent fluorinated acrylate textile finishing agent and a preparation method thereof. The preparation method comprises the following steps: mainly introducing a reaction type cation fluorinated emulsifier and a polymerizable cross-linking agent, applying the emulsifier and the cross-linking agent to seeded emulsion polymerization of short fluorocarbon chain perfluoroalkyl acrylate, in situ forming an macromolecular cation organic fluorine copolymer emulsifier during the seeded polymerization process, and in the follow-up emulsion polymerization, enabling the fluorine-containing group to be stably arranged in an emulsion particle shell layer under the action of the polymerizable cross-linking agent; with the results of comprehensive functions of the emulsifier and the polymerizable cross-linking agent, the resin can be used as the textile finishing agent to show up good water repellency, oil repellency and processing continuity.

Description

technical field [0001] The invention relates to the field of fabric finishing auxiliaries, in particular to an environment-friendly self-crosslinking water- and oil-repellent fabric finishing agent and a preparation method thereof. Background technique [0002] The electronegativity of the fluorine atom is large, the radius is small, the bond energy of the carbon-fluorine bond is large, the bond distance is short, and the polarization is small, which makes the fluoropolymer have high heat resistance stability, high chemical stability, high surface activity and Hydrophobic and oil repellent. Fluoroacrylates are easy to copolymerize with acrylate monomers to prepare copolymer emulsions, so they become the most important application of fluoropolymers. [0003] Fluorine-containing acrylates are widely used in many fields such as textile finishing, construction and antifouling coatings, paper processing, electronic appliances, and optical components. However, at present, long f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/356C08F220/18C08F220/32C08F220/22C08F230/08C08F2/30C08F2/28
Inventor 蒋国忠张立军邓瑾妮蒋韶贤蒋红霞邓希平
Owner ANHUI LINGDA CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap