Nickel-phosphorus/nano V8C7 composite plating liquid

A V8C7, composite electroplating technology, applied in the direction of electrolytic coatings, coatings, etc., can solve the problems of local adiabatic shear zone single shear cracks, fracture failures, etc., to achieve high utilization of raw materials, less energy consumption, and improved stability sexual effect

Inactive Publication Date: 2015-03-11
CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when amorphous materials are deformed at room temperature, it is easy to induce local adiabatic shear bands to form single shear cracks and suddenly break and fail.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) Nano V 8 C 7 For the pretreatment of powder, first weigh 8 grams of nano V 8 C 7 powder, add 500ml of 15wt% hydrochloric acid solution, heat to 60°C in a water bath, stir for 30min, and V 8 C 7 Wash the powder twice with deionized water after filtration;

[0019] (2) First weigh 0.1 g of tartaric acid and 0.1 g of sodium dodecylbenzenesulfonate, add 1000 ml of deionized water, heat to 90°C in a water bath, and stir until the sodium dodecylbenzenesulfonate is dissolved; Then weigh 150 grams of nickel sulfate (NiSO 4 ·6H 2 O), 15 grams of nickel chloride (NiCl 2 ·6H 2 O), 30 grams of sodium hypophosphite (NaH 2 PO 2 ·H 2 O), 20 grams of boric acid (H 3 BO 3 ) was added to the above solution, stirred at room temperature until dissolved; then added the cleaned V 8 C 7 The powder was continuously stirred for 2 hours, then 0.2 g of potassium iodide and 0.1 g of potassium chloride were added, stirred and dissolved, and then 10 wt% hydrochloric acid solution ...

Embodiment 2

[0021] (1) Nano V 8 C 7 For the pretreatment of powder, first weigh 10 grams of nanometer V 8 C 7 powder, add 500ml of 15wt% hydrochloric acid solution, heat to 60°C in a water bath, stir for 30min, and V 8 C 7 Wash the powder twice with deionized water after filtration;

[0022] (2) First weigh 0.1 g of tartaric acid and 0.1 g of sodium dodecylbenzenesulfonate, add 1000 ml of deionized water, heat to 90°C in a water bath, and stir until the sodium dodecylbenzenesulfonate is dissolved; Then weigh 140 grams of nickel sulfate (NiSO 4 ·6H 2 O), 22 grams of nickel chloride (NiCl 2 ·6H 2 O), 35 grams of sodium hypophosphite (NaH 2 PO 2 ·H 2 O), 15 grams of boric acid (H 3 BO 3 ) was added to the above solution, stirred at room temperature until dissolved; then added the cleaned V 8 C 7 The powder was continuously stirred for 2 hours, then 0.2 g of potassium iodide and 0.1 g of potassium chloride were added, stirred and dissolved, and then 10 wt % hydrochloric acid so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nickel-phosphorus / nano V8C7 composite plating liquid. The plating liquid comprises the following components: 120-180 g / L of nickel sulfate, 10-30 g / L of nickel chloride, 30-50 g / L of sodium hypophosphite, 10-25 g / L of boric acid, 0.2-2 g / L of a complexing agent, 0.1-0.5 g / L of a brightening agent and 5-20 g / L of nano V8C7. Compared with the prior art, by adopting the composite plating liquid disclosed by the invention, a composite plate taking nickel-phosphorus amorphous alloy as a basal body and the nano V8C7 as a second phase can be prepared, and the surface is free of microcracks. The nickel-phosphorus / nano V8C7 composite plating liquid is high in abrasion resistance and corrosion resistance. The composite plating liquid is simple in composition, little in damage of reagents to the environment, stable in technology, simple in operation and high in current efficiency.

Description

technical field [0001] The invention relates to a composite electroplating solution in the field of material surface treatment, specifically a nickel-phosphorus / nanometer V 8 C 7 Composite plating solution. Background technique [0002] Composite electroplating uses electrochemical methods to co-deposit metals (or alloys) and solid particles (or fibers). There is almost no diffusion phenomenon between the base metal and the added solid particles in the composite coating, so it has the comprehensive properties of the base metal and solid particles. The particularity of amorphous structure (short-range order) makes amorphous materials have excellent mechanical properties, corrosion resistance, and chemical activity compared with traditional metals. However, when the amorphous material is deformed at room temperature, it is easy to induce the local adiabatic shear band to form a single shear crack and suddenly break and fail. On the other hand, the structural characteristic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D15/00C25D3/56
Inventor 罗奕兵戴晓元张健
Owner CHANGSHA UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap