Unlock instant, AI-driven research and patent intelligence for your innovation.

A kind of environmental protection material containing diatom ooze and its preparation method and the use of preparation floor

An environmentally friendly material and diatom mud technology, which is applied in the fields of environmental protection materials and their preparation, and floor coating, can solve the problems that the functions need to be diversified and the performance needs to be improved, and achieve excellent protection and indoor purification. Widely industrialized application prospects and practical Value, excellent environmental protection effect

Active Publication Date: 2016-05-18
BEIJING SHENGHAO UNIVERSE TECH DEV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Although there are many coating compositions containing diatom ooze components in the prior art, their performance still needs to be improved, and their functions also need to be diversified.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of environmental protection material containing diatom ooze and its preparation method and the use of preparation floor
  • A kind of environmental protection material containing diatom ooze and its preparation method and the use of preparation floor
  • A kind of environmental protection material containing diatom ooze and its preparation method and the use of preparation floor

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0044] Preparation Example 1: Complex Auxiliary (Acetylacetonate Isoniazid Molybdenum Complex)

[0045] Add 1mol isonicotinic acid hydrazide and 30mol pyridine to the industrial reactor, heat up to 75°C, stir to dissolve, then add 1.5mol acetylacetone and stir for 1.5 hours, finally add 1mol molybdenum acetylacetonate and continue stirring for 2.5 hours, suction filtration, washing, Vacuum-dried to obtain the required complex auxiliary agent acetylacetonate isoniazid molybdenum complex, ready for use.

[0046] In all the following examples, unless otherwise specified, all "complex additives" are molybdenum complexes of isoniazid acetylacetonate prepared in this preparation example.

preparation example 2

[0047] Preparation Example 2: Fullerene Amine Adducts

[0048] Under a nitrogen atmosphere, add an appropriate amount of toluene to the reactor, then add 10mmol C60 fullerene and 150mmol N,N-dimethyl-1,3-diaminopropane, stir and dissolve, then heat to reflux for nitrogen-hydrogen addition reaction 12 hours, the reaction is over, cooled to room temperature, concentrated in vacuo, the residue is added to n-hexane for precipitation, and the precipitate is collected by filtration to obtain the desired fullerene adduct, which is set aside.

[0049] In all the following examples, unless otherwise specified, all "fullerene amine adducts" are the fullerene amine adducts prepared in this preparation example.

preparation example 3

[0050] Preparation Example 3: Plant Extract

[0051] In the industrial extraction kettle, adding completely dry chestnut flower and lavender with a mass ratio of 1:0.4 is a total of 500g, then adding 4500g of a mass ratio of N-butylpyridine tetrafluoroborate and ethanol mixed solvent at room temperature Extract under microwave power 280W for 25 minutes, then microwave, continue to heat to 65°C for extraction for 45 minutes, then filter and vacuum concentrate to 1 / 10 of the volume to obtain the plant extract for future use.

[0052] In all the following examples, unless otherwise specified, all "plant extracts" are plant extracts prepared in this preparation example.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an environmentally-friendly material containing diatom ooze, a preparation method of the material and an application of the material to preparation of floors. The material contains a diatom ooze component which is compounded with various components such as a complex, a fullerene derivative additive and a plant extract; by virtue of the collaborative and assistant actions of the components, the material is excellent in environmentally-friendly performance, moisturizing performance, bactericidal performance and smell removing performance; the unexpected technical effect is achieved; the requirements of modern indoor decoration can be fully met; and the environmentally-friendly material has a wide industrial application prospect.

Description

technical field [0001] The present invention relates to an environment-friendly material and its preparation method and application, more specifically to a new type of environment-friendly material containing diatom ooze, its preparation method and its use in preparing floors, especially floor coatings, belonging to the field of environment-friendly materials. Background technique [0002] With the development of the times and the advancement of science and technology, people are paying more and more attention to the comfort of the living environment. Creating a warm and beautiful living atmosphere and maintaining a healthy and environmentally friendly quality of life are the ideal life that many people dream of. Interior decoration is a key element to ensure the indoor living environment, making the research and development of interior decoration materials more and more generally valued by researchers. [0003] Diatom mud is a kind of interior decoration wall material with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/10E04F15/02C07F11/00C07C211/41C07C209/60C04B24/12C04B14/08
Inventor 唐喜军
Owner BEIJING SHENGHAO UNIVERSE TECH DEV