Fast curable environment friendly epoxy paint for drilling water tanks and making method thereof

An epoxy coating, rapid curing technology, applied in the direction of epoxy resin coating, anti-corrosion coating, coating, etc., can solve the problems of high brittleness, too fast increase in viscosity, easy cracking and peeling, etc., achieve good construction performance and simple production process , good adhesion effect

Inactive Publication Date: 2015-03-25
BC P INC CHINA NAT PETROLEUM CORP +2
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

High-solid coatings are formulated with liquid epoxy resin and low-viscosity curing agent. The paint film has high cross-linking density and good adhesion, but has the problems of high brittleness and poor impact resistance. It is frequently loaded and unloaded in the drilling water tank Easy to crack and peel off during alternating changes
According to reports, solvent-free pure epoxy anti-corrosion coatings have been tested on drilling water tanks, but there are defects such as too fast increase in viscosity during construction, short service life, and unsatisfactory construction performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fast curable environment friendly epoxy paint for drilling water tanks and making method thereof
  • Fast curable environment friendly epoxy paint for drilling water tanks and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] In a stainless steel barrel, add 0.6 parts of bisphenol A low-viscosity epoxy resin, 0.2 parts of bisphenol F epoxy resin, 0.2 parts of bisphenol A and bisphenol F mixed epoxy resin, and 0.1 part of cashew nut oil modification. 0.05 part of anionic compound containing fatty acid and rosin acid, 0.005 part of organosilicon polymer containing hydrophobic particles, 0.005 part of modified urea solution, control its temperature at 25±2°C, and stir at a high speed. While stirring, add 0.2 parts of zinc chrome yellow, 0.3 parts of aluminum tripolyphosphate, 0.3 parts of ultrafine silica powder, and 0.4 parts of talc powder, and stir at a high speed for 0.25 After 1 hour, use a sand mill to grind for 0.5 hour to make liquid A in the coating. 0.8 parts by weight of phenalkamine curing agent and 0.2 parts of linear aliphatic amine and adduct epoxy curing agent are stirred at high speed and mixed evenly to prepare liquid B in the coating. When in use, 1 weight part of liquid A a...

Embodiment 2

[0062] A method for manufacturing a fast-curing environment-friendly epoxy coating for drilling water tanks. In a stainless steel barrel, add 0.5 parts of bisphenol A low-viscosity epoxy resin, 0.3 parts of bisphenol F epoxy resin, 0.2 parts of bisphenol A and bisphenol F mixed epoxy resin, and 0.2 parts of cashew oil modification. 0.1 part of anionic compound containing fatty acid and rosin acid, 0.01 part of organosilicon polymer containing hydrophobic particles, 0.01 part of modified urea solution, control its temperature at 25±2°C, stir at high speed, add 0.2 parts of zinc chrome yellow, 0.4 parts of aluminum tripolyphosphate, 0.3 parts of ultrafine silica powder, 0.3 parts of talc powder, and stir at high speed for 0.25 After 1 hour, use a sand mill to grind for 0.5 hour to make liquid A in the coating. By weight, 0.7 parts of phenalkamine curing agent and 0.3 parts of linear aliphatic amine and adduct epoxy curing agent are stirred at high speed and mixed evenly to prep...

Embodiment 3

[0064] A method for manufacturing a fast-curing environment-friendly epoxy coating for drilling water tanks. In a stainless steel barrel, add 0.4 parts of bisphenol A low-viscosity epoxy resin, 0.4 parts of bisphenol F epoxy resin, 0.2 parts of bisphenol A and bisphenol F mixed epoxy resin, and 0.3 parts of cashew oil modification. 0.08 part of anionic compound containing fatty acid and rosin acid, 0.008 part of silicone polymer containing hydrophobic particles, 0.008 part of modified urea solution, control its temperature at 25±2°C, stir at high speed, add 0.1 part of zinc chrome yellow, 0.3 part of aluminum tripolyphosphate, 0.3 part of ultrafine silica powder, 0.4 part of talc powder, and stir at high speed for 0.25 After 1 hour, use a sand mill to grind for 0.5 hour to make liquid A in the coating. In parts by weight, 0.6 part of phenalkamine curing agent and 0.4 part of linear aliphatic amine and adduct epoxy curing agent are stirred at high speed and mixed evenly to pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Belonging to the technical field of paint and making methods, the invention relates to a fast curable environment friendly epoxy paint for drilling water tanks and a making method thereof. The method includes: in a stainless steel charging basket, adding bisphenol A low viscosity type epoxy resin, bisphenol F type epoxy resin, bisphenol A and bisphenol F mixed type epoxy resin and a cashew oil modified monoglycidyl ether epoxy active diluent, mixing the materials, under stirring, adding an anionic compound containing fatty acid and rosin acid, a hydrophobic particle containing organosilicon polymer and a modified urea solution, controlling the temperature at 25+ / -2DEG C, performing high speed stirring, and under stirring, adding zinc chrome, aluminum triphosphate, superfine silica powder and talcum powder, conducting high speed stirring for 0.25h, then carrying out grinding for 0.5-1h by a sand mill so as to obtain an A solution in the paint; and in another stainless steel charging basket, adding a phenolic aldehyde amine curing agent, linear aliphatic amine and an adduct epoxy curing agent, conducting high-speed stirring to mix the materials evenly to obtain a B solution in the paint.

Description

technical field [0001] The invention relates to a fast-curable environment-friendly epoxy coating for drilling water tanks and a manufacturing method, belonging to the technical field of coatings and manufacturing methods. Background technique [0002] The anticorrosion of drilling water tanks of early offshore drilling platforms or drilling ships mostly adopts epoxy coal tar pitch paint, which has excellent salt water resistance and low surface treatment construction adaptability, but its scope of application is limited because it contains carcinogens. Asphalt substitutes, aromatic C9 resin and coumarone resin, have the advantages of both performance and price, but have a high softening point, and need to add plasticizers and solvents to make coatings, and there are still problems of solvent volatilization and environmental pollution during use. question. When the coating system containing solvent is applied in the cabin, the solvent volatilizes slowly, and it takes more t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D7/12C09D5/08
CPCC09D163/00C08L2205/035C09D5/08C09D7/61C09D7/65C08L63/00C08L93/04C08L83/00C08K13/02C08K3/24C08K3/32C08K3/36C08K3/34
Inventor 徐忠苹韩文礼张彦军张贻刚杨耀辉李玲杰
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap