High-temperature resisting phosphorus-bromines type solvent-free epoxy matrix resin for carbon fiber cable core and preparation method of epoxy matrix resin

An epoxy matrix and epoxy resin technology, applied in the field of matrix resin, can solve the problems of high price, unfavorable large-scale popularization and application, high cost of polyetherimide resin, and achieve the advantages of convenient operation, low cost and good comprehensive performance. Effect

Inactive Publication Date: 2015-04-01
DONGHUA UNIV +1
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] (2) 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane (BAHPFP) and other monomers are expensive, resulting in high cost of polyetherimide resin (HPEI) and adhesives, which is not conducive to Large-scale promotion and application can only be limited to some special fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature resisting phosphorus-bromines type solvent-free epoxy matrix resin for carbon fiber cable core and preparation method of epoxy matrix resin
  • High-temperature resisting phosphorus-bromines type solvent-free epoxy matrix resin for carbon fiber cable core and preparation method of epoxy matrix resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Put 100.0 grams of ES216 epoxy resin and 25.0 grams of 2,2-bis[4-(2,4-bismaleimidophenoxy)phenyl]propane into the reaction kettle, stir and mix, and set at 120°C After reacting for 0.5 hours, cool down to below 80°C, add 70.0 grams of reactive diluent CE793, stir and mix evenly to obtain 195.0 grams of component A, which is designated as A1.

[0041] Put 50.0 grams of tetrabromobisphenol A epoxy resin and 10.0 grams of DOPO (9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide) into the reactor, and react at 120 ° C for 0.5 After 1 hour, add 10.0 grams of tetrabromophthalic anhydride, continue the reaction for 0.5 hours, add 30.0 grams of reactive diluent CE793, stir and mix evenly to obtain 100.0 grams of component B, which is designated as B1.

[0042] Component C consists of 100.0 grams of dodecenyl succinic anhydride and 20.0 grams of N,N-dimethyl-p-methylaniline, denoted as C1. Put components A1 and B1 into a reaction kettle, stir and mix at 110°C for 10 minutes, co...

Embodiment 2

[0044] Mix 100.0 grams of ES216 epoxy resin with 2.0 grams of 1,4-bis(2,4-bismaleimidophenoxy)benzene, 2.0 grams of 2,2-bis[4-(2,4-dimaleimide Put imidophenoxy)phenyl]propane into the reaction kettle, stir and mix, react at 100°C for 1.5 hours, cool to below 80°C, add 10.0 grams of reactive diluent CE793, stir and mix evenly, and get 114.0 grams of component A, denoted as A2.

[0045] Put 10.0 grams of tetrabromobisphenol A epoxy resin and 100.0 grams of DOPO (9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide) into the reactor, and react at 100°C for 1.5 After 1 hour, add 85.0 grams of tetrabromophthalic anhydride, continue the reaction for 1.5 hours, add 20.0 grams of reactive diluent CE793, stir and mix evenly to obtain 215.0 grams of component B, which is designated as B2.

[0046] Component C consists of 200.0 grams of methyltetrahydrophthalic anhydride, 100.0 grams of dodecenyl succinic anhydride, 5.0 grams of 2-ethyl-4-methylimidazole, and 5.0 grams of N,N-dimethyl-p-m...

Embodiment 3

[0048] Take an appropriate amount of high temperature resistant phosphorous bromine type solvent-free epoxy matrix resins for carbon fiber cable cores in Example 1 and Example 2 respectively, i.e. CFPM-1 and CFPM-2, and apply them evenly on standard stainless steel test pieces respectively, and let them dry in the air at room temperature. After standing for 10 minutes, stack, clamp, and put it into a blast oven for curing: start from room temperature to 100°C, keep warm for 1.5 hours, continue to heat up to 140°C, keep warm for 1.5 hours, continue to heat up to 170°C, keep warm Reacted for 1.5 hours and cooled naturally to room temperature. The tensile shear strength (σ) test was carried out at room temperature (25°C) and high temperature (240°C) using an electronic tensile machine, and the results are shown in Table 1.

[0049] Take appropriate amount of high temperature resistant phosphorus bromine type solvent-free epoxy matrix resin for carbon fiber cable core of embodimen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to high-temperature resisting phosphorus-bromines type solvent-free epoxy matrix resin for a carbon fiber cable core and a preparation method of the epoxy matrix resin. The matrix resin is composed of ES216 epoxy resin, tetrabromo-bisphenol-A epoxy resin, DOPO, tetrabromophthalic anhydride, four-maleimide resin, a curing agent, a promoter and a reactive diluent. The preparation method comprises the following steps: (1), the ES216 epoxy resin is mixed the four-maleimide resin, heating is performed to rise temperature, stirring for reaction is performed, the reactive diluents is added, and a component A is obtained after stirring; (2), the tetrabromo-bisphenol-A epoxy resin is mixed with the DOPO and the tetrabromophthalic anhydride, heating is performed to rise temperature, stirring for reaction is performed, the reactive diluents is added, and a component B is obtained after stirring; (3), components C are the curing agent and the promoter; the components A, B and C are stirred and mixed evenly. The high-temperature resisting phosphorus-bromines type solvent-free epoxy matrix resin provided by the invention is suitable for manufacturing fiber-reinforced advance composite materials including carbon fiber, glass fiber, aramid fiber and the like, particularly to pultrusion formation of carbon fiber cable cores.

Description

technical field [0001] The invention belongs to the field of matrix resins, in particular to a high-temperature-resistant phosphorus-bromine type solvent-free epoxy matrix resin for carbon fiber cable cores and a preparation method thereof. Background technique [0002] As we all know, epoxy resin has many excellent properties: (1) Good bonding performance: high bonding strength, wide bonding surface, it is compatible with many metals (such as iron, steel, copper, aluminum, metal alloys, etc.) The bonding strength of metal materials (such as glass, ceramics, wood, plastics, etc.) is very high, and some even exceed the strength of the bonded material itself, so it can be used in many stressed structural parts and is the main component of structural adhesives One; (2) good processing performance: the flexibility of epoxy resin formula, the diversity of processing technology and product performance are the most prominent among polymer materials; (3) good stability performance: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L79/08C08K5/5313
Inventor 虞鑫海吴冯周志伟
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap