Catalyst for catalytic combustion and preparation method thereof
A catalytic combustion and catalyst technology, which is applied in the direction of catalyst activation/preparation, combustion methods, physical/chemical process catalysts, etc., can solve the problems of easy cracking of the coating, unfavorable industrialization, peeling, etc., and achieve simple preparation methods, promotion of penetration, Good penetration and wetting properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0035] Example 1
[0036] Cordierite pretreatment: The cordierite honeycomb ceramic is completely immersed in 5wt% nitric acid solution for 1 hour. After taking it out, it is rinsed with deionized water 3 times, and placed in an oven at 120°C for 10 hours to obtain Surface activated cordierite honeycomb ceramic carrier.
[0037] Preparation of aluminum sol: add 20 grams of pseudo-boehmite to 150 mL of deionized water, and add 7 grams of concentrated nitric acid dropwise while stirring. After stirring for a certain period of time, heating to 80°C, adding nitric acid dropwise to complete peptization, controlling the pH of the solution at 2-5, aging for 24 hours, to obtain a transparent aluminum sol with a content of 8wt% based on alumina.
[0038] Preparation of silicon-aluminum coating slurry: firstly mix 90 grams of aluminum sol with 6 grams of fumed silica, and add 4 grams of fatty alcohol polyoxyethylene ether (the molecular formula is RO(CH 2 CH 2 O) 5 H, where R is C 7 ~C 9 ) Af...
Example Embodiment
[0043] Example 2
[0044] After mixing 5 g / L platinum nitrate solution and 5 g / L palladium nitrate solution in equal volume, it is used as the active component liquid. Others are the same as in Example 1. The carrier coated with the silicon-aluminum coating and the composite coating obtained in this embodiment is ZT2, the final product is CT2, and the platinum-palladium loading is 0.05 wt% of the total weight of the catalyst.
Example Embodiment
[0045] Example 3
[0046] Cordierite pretreatment: the same as in Example 1.
[0047] Aluminum sol is a commercially available product (solid content is 15%, pH is 3-4).
[0048] Preparation of silicon-aluminum coating slurry: first mix 87 grams of aluminum sol with 10 grams of fumed silica, and add 3 grams of alkylphenol polyoxyethylene ether (the molecular formula is RC 6 H 4 O(CH 2 CH 2 O) n H, where R is C 9 ~C 12 , N is 9~12) After stirring and mixing for 30 minutes, the coating liquid can be obtained.
[0049] Preparation of composite coating slurry: add 54 grams of nano titanium dioxide (50-100nm), 32 grams of fumed white carbon black (10-80nm), and 17.2 grams of nano cerium oxide into 280ml of carbonic acid solution (0.2mol / L) and stir well Then, add 43 grams of aluminum sol to it, stir and mix for 90 minutes until uniform, add 4.3 grams of alkylphenol polyoxyethylene ether (the molecular formula is RC 6 H 4 O(CH 2 CH 2 O) n H, where R is C 9 ~C 12 , N is 9~12), stir and mix ...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Concentration | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap