Novel protective agent for back of stainless steel weld

A protective agent, stainless steel technology, applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc., can solve the problems that cannot meet the welding protection requirements of stainless steel factory pipes, and the welding protection of long stainless steel pipes is not suitable, so as to achieve good shape , good surface corrosion resistance and high pressure resistance

Inactive Publication Date: 2015-04-29
广东万事达实业有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, in the welding process of stainless steel, the main protection methods used are back nitrogen protection, ceramic liner protection, mixed gas protection, etc., but in specific operations, the above various protection methods are not suitable for welding protection of long stainless steel pipes. Therefore, it cannot meet the welding protection requirements of stainless steel plant pipelines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A new protective agent for the back of a stainless steel weld seam, comprising raw materials of the following components: magnesium oxide, aluminum oxide, titanium dioxide, calcium oxide, sodium chloride, manganese oxide, silicon dioxide, an adhesive, and the balance being acetone. The mass percentage of each component in the raw material is: magnesium oxide: 32%, aluminum oxide 5.5%, titanium dioxide 8.5%, calcium oxide 5%, sodium chloride 6.5%, manganese oxide 13%, silicon dioxide 9%, adhesive 3%, the balance is acetone.

[0015] Further, the adhesive is made of acrylates such as methyl acrylate, methyl methacrylate, 2-ethyl methacrylate, and diphenylmethane diisocyanate (MDI).

[0016] Further, the following steps are included: first, put magnesium oxide, aluminum oxide, titanium dioxide, calcium oxide, sodium chloride, manganese oxide, and silicon dioxide on an electronic scale to weigh according to the percentage, and then put the weighed raw materials into the gri...

Embodiment 2

[0020] A new protective agent for the back of a stainless steel weld seam, comprising raw materials of the following components: magnesium oxide, aluminum oxide, titanium dioxide, calcium oxide, sodium chloride, manganese oxide, silicon dioxide, an adhesive, and the balance being acetone. The mass percentage of each component in the raw material is: magnesium oxide: 35%, aluminum oxide 7%, titanium dioxide 9%, calcium oxide 5.5%, sodium chloride 7.5%, manganese oxide 1413%, silicon dioxide 9.5%, adhesive 3.5%, the balance is acetone.

[0021] Further, the adhesive is made of acrylates such as methyl acrylate, methyl methacrylate, 2-ethyl methacrylate, and diphenylmethane diisocyanate (MDI).

[0022] Further, the following steps are included: first, put magnesium oxide, aluminum oxide, titanium dioxide, calcium oxide, sodium chloride, manganese oxide, and silicon dioxide on an electronic scale to weigh according to the percentage, and then put the weighed raw materials into the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel protective agent for a back of a stainless steel weld. The novel protective agent comprises a raw material containing the following components in mass percent: 25-35 percent of magnesium oxide, 2.5-7 percent of aluminum oxide, 5-10 percent of titanium dioxide, 3.5-6.5 percent of calcium oxide, 5-8 percent of sodium chloride, 10-15 percent of manganese oxide, 6.5-10 percent of silicon dioxide, 2-3.5 percent of adhesive and the balance of acetone; the invention also discloses a preparation method for the protective agent. Through the manner, according to the novel protective agent for the back of the stainless steel weld, disclosed by the invention, the back of the weld can be free of oxidation, has a good shape and is smooth; meanwhile, the novel protective agent has good surface corrosion resistance and high pressure resistance, and is especially suitable for the back protection in stainless steel TIG (tungsten inert gas) welding.

Description

technical field [0001] The invention relates to a welding protection material, in particular to a new type of protection agent for the back of a stainless steel weld seam. Background technique [0002] Stainless steel has excellent corrosion resistance, heat resistance, oxidation resistance, good mechanical properties and processing properties, and is widely used in medical equipment, petrochemical and other industries. With the expansion of stainless steel application fields, the stainless steel welding market is also growing rapidly. [0003] At present, in the welding process of stainless steel, the main protection methods used are back nitrogen protection, ceramic liner protection, mixed gas protection, etc., but in specific operations, the above various protection methods are not suitable for welding protection of long stainless steel pipes. Therefore, it is also unable to meet the welding protection requirements of stainless steel plant pipelines. Contents of the i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/362
CPCB23K35/362
Inventor 杨伟帅
Owner 广东万事达实业有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com