Rustproof water-based grinding fluid with high settleability and preparation method thereof

A technology of anti-rust water and sedimentation, which is applied in the field of grinding fluid, can solve the problem that fine dust such as iron powder and oil stone powder cannot be effectively settled, and achieve chemical stability and comprehensive performance, good protection, and long-lasting life. Effect

Inactive Publication Date: 2015-05-06
马艳荣
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiencies of the prior art, the present invention provides a settling antirust water-based grinding fluid and its preparation method, which solves the problem that fine dust such as iron powder and oilstone powder cannot effectively settle during the honing process, and can Make the grinding fluid maintain long-term stable lubricating performance and cleaning performance during processing, long service life, excellent anti-rust performance, and excellent comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rustproof water-based grinding fluid with high settleability and preparation method thereof
  • Rustproof water-based grinding fluid with high settleability and preparation method thereof
  • Rustproof water-based grinding fluid with high settleability and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of precipitating antirust water-based grinding fluid, comprising the following groups by mass percentage:

[0046]

[0047]

[0048] Described settling agent is made up of organosulfur, organoborate and water-soluble macromolecule surfactant; The mass percent content of three in described grinding fluid is:

[0049] Organic sulfur 1%

[0050] Ethylene glycol monobutyl ether 2%

[0051] Polydichloroethyl ether tetramethylethylenediamine 2%.

[0052] The organic sulfur is mercaptan.

[0053] The flocculant is selected from polymeric polyferric sulfate (PFS).

[0054] The lubricant comprises a mixture of potassium tetraborate and isomeric alcohol polyoxyethylene ethers.

[0055] The antirust agent is a mixture of tridecanedibasic acid and benzoic acid.

[0056] The fungicide is 1-hydroxyl-2(1H)-pyridinethione.

[0057] The coupling agent is diethylene glycol monobutyl ether.

[0058] The preparation method of described antirust antirust water base grind...

Embodiment 2

[0066] A kind of precipitating antirust water-based grinding fluid, comprising the following groups by mass percentage:

[0067]

[0068] The settling agent is made up of organic sulfur, ethylene glycol monobutyl ether and polydichloroethyl ether tetramethylethylenediamine; the three mass percentages in the grinding fluid are:

[0069] Organic Sulfur 4%

[0070] Ethylene glycol monobutyl ether 3%

[0071] Polydichloroethyl ether tetramethylethylenediamine 3%.

[0072] The organic sulfur is a disulfide.

[0073] The flocculant is polyferric chloride.

[0074] The lubricant is potassium tetraborate.

[0075] The antirust agent is a mixture of undecanedibasic acid and methylbenzotriazole.

[0076] The bactericide is an alkylisothiazolinone.

[0077] The coupling agent is diethylene glycol monobutyl ether.

[0078] The preparation method of above-mentioned precipitative antirust water-based grinding fluid, comprises the steps:

[0079] A) Weigh or measure settling agent, ...

Embodiment 3

[0085] A kind of precipitating antirust water-based grinding fluid, comprising the following groups by mass percentage:

[0086]

[0087] The settling agent is made up of organic sulfur, ethylene glycol monobutyl ether and polydichloroethyl ether tetramethylethylenediamine; the three mass percentages in the grinding fluid are:

[0088] Organic Sulfur 8%

[0089] Ethylene glycol monobutyl ether 2%

[0090] Polydichloroethyl ether tetramethylethylenediamine 5%.

[0091] The organic sulfur is a mixture of sulfides and disulfides.

[0092] The flocculant is a mixture of polyaluminum chloride and polyaluminum sulfate (PAS).

[0093] The lubricant is a mixture of isomeric alcohol polyoxyethylene ether and glycerin.

[0094] The rust inhibitor is a mixture of nitrogen-containing heterocyclic tricarboxylic acid and potassium hydroxide.

[0095] The bactericide is iodoalkyl carbamate.

[0096] The coupling agent is diethylene glycol monobutyl ether.

[0097] The preparation m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides rustproof water-based grinding fluid with high settleability. The rustproof water-based grinding fluid is characterized by comprising the following components in percentage by mass: 5-15 percent of a settling agent, 5-10 percent of flocculating agents, 15-30 percent of lubricants, 25-30 percent of rustproof agents, 1-2 percent of sterilizing agents, 1-5 percent of coupling agents, 1-2 percent of anti-foaming agents and the balance of water; the settling agent is a mixture of organic sulfur, ethylene glycol monobutyl ether and poly-dichloro ethyl ether tetramethyl ethylenediamine. According to the rustproof water-based grinding fluid with high settleability, the problem that fine dust such as iron powder, oil stone powder and the like cannot be effectively settled in a quilted grinding process is solved, the grinding fluid can keep long-term and stable lubrication performance and cleaning performance during processing, and is long in service life, high in rustproof performance and high in comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of grinding fluid, in particular to a sedimentation antirust water-based grinding fluid and a preparation method thereof. Background technique [0002] Honing is widely used in mechanical processing because of its high dimensional accuracy and smooth surface. However, the particle size of the iron powder and oil stone powder produced in the honing process is small, and it is easy to suspend in the grinding fluid and re-penetrate into the interface between the grinding wheel and the workpiece, thereby affecting the processing efficiency and destroying the processing quality of the workpiece surface. Therefore, grinding must be required. The cutting fluid has good cleaning and settling properties. In the traditional honing process, diesel oil or kerosene is mostly used as the grinding fluid. However, due to the low flash point of diesel and kerosene, they are easy to burn and cause fires. In addition, diese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M173/02C10N30/06C10N30/04C10N30/12C10N40/24
Inventor 张胜勇马艳荣
Owner 马艳荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More