Adsorption filtering agent for nano strontium titanate modified montmorilonite clay and preparation method therefor

A technology of nano-strontium titanate and montmorillonite clay, applied in separation methods, filtration separation, chemical instruments and methods, etc., can solve the problems of insufficient utilization of the first layer, wear and corrosion, and low dust removal effect, and achieve good filtration of exhaust gas Function, prolong service life, good adsorption and filtration performance

Inactive Publication Date: 2015-08-12
ANHUI PHOENIX INT CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the actual operation process, the use of the first layer is not enough, resulting in low dust removal effect and serious wear and corrosion of the filter material after long-term use. There is an urgent need for an adsorption filter with high efficiency and multiple functions to be sprayed on the filter before the dust collector starts to work. The surface of the material is used as the first layer, which can not only improve the dust removal effect of the dust collector, but also filter and absorb the harmful exhaust gas discharged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The adsorption filter of nano-strontium titanate modified montmorillonite clay is characterized in that it is made of the following raw materials in parts by weight: montmorillonite clay 74, coke powder 12, fly ash 16, rosin 4 , magnesium chloride 1, sodium metaphosphate 1.9, antimony trioxide 0.7, nano-strontium titanate 4.9, silane coupling agent YDH-151 0.6, appropriate amount of water.

[0012] The preparation method comprises the following steps:

[0013] (1) Grind coke powder through a 120-180 mesh sieve, add nano-strontium titanate and silane coupling agent YDH-151, stir and grind for 1-2 hours, and dry at 150-180°C to obtain modified nano-strontium titanate ;

[0014] (2) Take the montmorillonite clay and heat it at 600-720°C for 2-4 hours, cool and grind it into powder and put it into a high mixer, add modified nano strontium titanate and rosin, mix and stir for 30-50 minutes at 180-220°C ;

[0015] (3) Stir the magnesium chloride with water until it is comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses an adsorption filtering agent for nano strontium titanate modified montmorilonite clay. The dsorption filtering agent is prepared from the following raw materials in parts by weight: 70-80 parts of montmorilonite clay, 11-14 parts of coke powder, 15-20 parts of coal ashes, 2-4 parts of rosin, 1-3 parts of magnesium chloride, 1.1-2.4 parts of sodium metaphosphate, 0.6-0.9 part of antimonous oxide, 4.2-5.7 parts of nano strontium titanate, 0.4-0.8 part of a silane coupling agent YDH-151 and an appropriate amount of water. The adsorption filtering agent prepared by the preparation method has the characteristics of a rough and hard surface, a large specific surface area, high porosity, good adsorption filtering performance and low cost, the nano strontium titanate is loaded on the surface of the montmorilonite clay through a physical and chemical modifying method for decomposing organic pollutants into carbon dioxide and oxygen gas, so that harmful substances adsorbed on the montmorilonite clay are reduced, the service life of the adsorption filtering agent is prolonged, and the adsorption filtering agent is provided with a good waste gas filter function while being sprayed to a dust collector filter material and is suitable for being used in high temperature soot treatment.

Description

technical field [0001] The invention relates to the technical field of adsorption filter materials, in particular to an adsorption filter of nano strontium titanate modified montmorillonite clay and a preparation method thereof. Background technique [0002] With the rapid development of industrialization, the problem of air quality is becoming more and more serious. Especially in recent years, smog has seriously threatened people's health across the country, and the side effects caused by it have become increasingly serious. The culprits are domestic building materials, chemicals, For the smoke and dust discharged from kiln heads and kiln tails, calcium carbide furnaces, ferroalloy furnaces, etc. in metallurgical industries, the most commonly used dust removal equipment is the bag filter. The bag filter is a dry dust filter device. After the filter material is used for a period of time, due to effects such as screening, collision, retention, diffusion, and static electricit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/14B01J20/22B01J20/30
Inventor 陈登宇
Owner ANHUI PHOENIX INT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products