Photocatalystc composite floor board and production process of photocatalystc composite floor board

A composite flooring and production process technology, which is applied in the direction of layered products, wood layered products, buildings, etc., can solve the problems that the floor structure and its performance need to be improved, and achieve good insect resistance, good shear strength and water resistance, and strong Effect of Adhesive Strength and Hydrophobicity

Inactive Publication Date: 2015-10-21
DEHUA TB NEW DECORATION MATERIAL CO LTD
View PDF9 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] CN202467086U (2012-2-29) discloses a photocatalyst antibacterial floor, but the structure and performance of the floor still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Photocatalystc composite floor board and production process of photocatalystc composite floor board
  • Photocatalystc composite floor board and production process of photocatalystc composite floor board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] Biomass soybean gum preparation: add 3g of alkali and 100g of water in a three-neck round bottom flask, the alkali is sodium hydroxide, stir for 3 minutes to dissolve the sodium hydroxide, then add 0.5g of silicate, 0.5 g sulfite and 0.2g modifier, the silicate is sodium silicate, the modifier is urea, the sulfite is sodium sulfite, and stirred for 3 minutes, the temperature is 80-96 °C to obtain a preliminary mixed solution; then add 15 g of soybean derivatives to the preliminary mixed solution, the soybean derivatives are soybean protein isolate, stir for 10 minutes, and the temperature is 80 °C, so that the soybean protein isolate is fully dispersed in the solution, Obtain a mixed solution; then add 0.3 g of an aqueous solution of curing agent polyamide polyamine-epichlorohydrin (PAE) with a mass concentration of 12.5%, and stir for 10 minutes to obtain a solidified mixed solution; then add an acid, the acid being 0.1 The mass concentration of phosphoric acid was 35%...

Embodiment 2

[0099] Preparation of biomass soybean gum: Add 8g of alkali and 100g of water into a three-neck round bottom flask, the alkali is sodium hydroxide, stir for 10 minutes to dissolve the sodium hydroxide, then add 3g of silicate and 3g of sulfite to the alkali solution And 5g modifier, silicate is sodium silicate, modifier is urea, sulfite is sodium sulfite, and stirs 10 minutes, and temperature is 96 ℃, obtains preliminary mixed solution; Then in the preliminary mixed solution Add 40g of soybean derivatives, the soybean derivatives are soybean protein isolate, stir for 60 minutes at a temperature of 96°C, so that the soybean protein isolate is fully dispersed in the solution to obtain a mixed solution; then add 2.5g of curing agent with a mass concentration of 12.5% The aqueous solution of polyamide polyamine-epichlorohydrin (PAE) was stirred for 60 minutes to obtain a solidified mixed solution; then an acid was added, and the acid was 4 g of phosphoric acid with a mass concentra...

Embodiment 3

[0127] Preparation of biomass soybean gum: Add 5g of alkali and 100g of water into a three-neck round bottom flask, the alkali is sodium hydroxide, stir for 6 minutes to dissolve the sodium hydroxide, then add 2g of silicate and 2g of sulfite to the alkali solution and 2g modifier, the silicate is sodium silicate, the modifier is urea, the sulfite is sodium sulfite, and stirred for 6 minutes, the temperature is 90 ° C, to obtain a preliminary mixed solution; then to the preliminary mixed solution Add 25g of soybean derivatives, the soybean derivatives are soybean protein isolate, stir for 30 minutes, and the temperature is 90°C, so that the soybean protein isolate is fully dispersed in the solution to obtain a mixed solution; then add 3g of curing agent polymer with a mass concentration of 12.5%. The aqueous solution of amidopolyamine-epichlorohydrin (PAE) was stirred for 30 minutes to obtain a solidified mixed solution; then an acid was added, and the acid was 2 g of phosphori...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a photocatalystc composite floor board, and belongs to the field of a functional environment-friendly healthy floorboard. The formaldehyde emission content of the composite floorboard is less than 0.3mg / L; the antibacterial rate is higher than or equal to 90 percent; the surface wear-resistant coefficient is less than or equal to 0.08g / 100r; a substrate layer is an oriented shaving board layer; the oriented shaving board layer comprises an upper surface layer and a lower surface layer which are formed by glue mixing wood shavings in longitudinal arrangement according to the fiber direction and a core layer shaving layer formed by glue mixing wood shavings in transverse arrangement according to the fiber direction; and a decoration layer, a wear-resistant primer layer and a photocatalystc antibacterial paint decoration layer are sequentially arranged on the substrate layer. A production process of the photocatalystc composite floor board comprises the steps of shaving board layer sorting, glue preparation, glue distribution and assembling for the first time, cold pressing for the first time, core trimming, glue distribution and assembling for the second time, cold pressing for the second time, hot pressing for the first time, fixed-thickness sanding, edge cutting, puttying, polishing, sorting, reconditioning, glue distribution and veneering, cold pressing for the third time, hot pressing for the second time, multi-blade sawing, sanding, double-end milling, priming, finish paint preparing and finish paint painting. The composite floorboard has the advantages of good antibacterial function, high strength, good wear-resistant performance and comfortable foot feeling.

Description

technical field [0001] The invention relates to a photocatalyst composite floor, which belongs to the field of functional environment-friendly and healthy floors. Background technique [0002] There are various volatile organic compounds and harmful microorganisms in people's living environment, which directly affect people's physical and mental health. Most pathogenic bacteria in the living environment often come from the ground dirt and pets. The floor is in direct contact with the human body, and it is easier to transmit the microorganisms that breed germs and bacteria to the human body. In the past, people sprayed chemical anti-mold and anti-bacterial agents around the room to solve the air quality problem in the room. However, ordinary anti-mold and anti-bacterial agents are highly toxic, have poor heat resistance and durability, and are sprayed on floors and decorations. The surface of the board is easy to change color and affect the appearance. As people's requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/02B32B21/02B32B21/04B32B7/12B32B33/00B32B37/06B32B37/08B32B37/10B32B37/12
Inventor 杨勇沈金祥刘元强詹先旭叶交友钱仁龙朱丹莎
Owner DEHUA TB NEW DECORATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com