Ethyl lauroyl arginate hydrochloride microcapsule and preparation technology thereof

A kind of lauroyl arginine ethyl ester hydrochloride, the technology of preparation process, applied in the direction of botany equipment and method, chemicals used for biological control, food ingredients as antimicrobial preservation, etc., can solve the problem of affecting the antiseptic effect, Problems such as easy crystallization and low solubility of ethyl lauroyl arginine hydrochloride have been achieved, and the effects of continuous large-scale production, low solubility, and improved usability and water solubility have been achieved.

Inactive Publication Date: 2015-11-18
武汉志邦化学技术有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the solubility of ethyl lauroyl arginate hydrochloride is very low at low temperature, and it is easy to crystallize and precipitate, which affects its antiseptic effect and limits its use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Add 10kg of sodium starch octenyl succinate, 10kg of cyclodextrin, and 10kg of pectin into 50-90% water at 60-80°C, and stir to dissolve them. Add 64kg of maltodextrin, 4kg of ascorbic acid, and 0.9kg of calcium phosphate into the dissolved wall material, stir while adding to make it evenly mixed, keep it at 50-70°C for later use, and prepare the water phase;

[0023] (2) Add 1.1kg (purity 98%) ethyl lauroyl arginine hydrochloride into the water phase, and mix online with a pipeline shearing machine, with a rotation speed of 10000-16000 rpm for 5-10min, 19000-28000 Rotate / min for 5-8min, then homogenize at 30-50Mpa to prepare microemulsion;

[0024] (3) Spray-dry the microemulsion, control the temperature of the air inlet of the spray tower at 150-190°C, control the temperature of the air outlet at 60-90°C, and the speed of the atomizer at 1000-1400r / min; Ester hydrochloride microcapsules.

Embodiment 2

[0026] (1) Add 10kg of sodium starch octenyl succinate, 10kg of cyclodextrin, and 10kg of gum arabic to 60-80°C, 50-90% water, and stir to dissolve them. Add 64kg of polydextrose, 4kg of sodium ascorbate, and 0.9kg of calcium phosphate into the dissolved wall material, stir while adding to make it evenly mixed, keep it at 50-70°C for later use, and prepare the water phase;

[0027] (2) Add 1.1kg (purity 98%) ethyl lauroyl arginine hydrochloride into the water phase, and mix online with a pipeline shearing machine, with a rotation speed of 10000-16000 rpm for 5-10min, 19000-28000 Rotate / min for 5-8min, then homogenize at 30-50Mpa to prepare microemulsion;

[0028] (3) Spray-dry the microemulsion, control the temperature of the air inlet of the spray tower at 150-190°C, control the temperature of the air outlet at 60-90°C, and the speed of the atomizer at 1000-1400r / min; Ester hydrochloride microcapsules.

Embodiment 3

[0030] (1) Add 10kg of sodium starch octenyl succinate, 10kg of cyclodextrin, and 10kg of sodium alginate into 50-90% water at 60-80°C, and stir to dissolve them. Add 64kg of maltodextrin, 4kg of EDTA-Na, and 0.9kg of calcium phosphate into the dissolved wall material, stir while adding to make it evenly mixed, keep it at 50-70°C for later use, and prepare the water phase;

[0031] (2) Add 1.1kg (purity 98%) ethyl lauroyl arginine hydrochloride into the water phase, and mix online with a pipeline shearing machine, with a rotation speed of 10000-16000 rpm for 5-10min, 19000-28000 Rotate / min for 5-8min, then homogenize at 30-50Mpa to prepare microemulsion;

[0032] (3) Spray-dry the microemulsion, control the temperature of the air inlet of the spray tower at 150-190°C, control the temperature of the air outlet at 60-90°C, and the speed of the atomizer at 1000-1400r / min; Ester hydrochloride microcapsules.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to an ethyl lauroyl arginate hydrochloride microcapsule and preparation technology thereof. The preparation technology is prepared by: using ethyl lauroyl arginate hydrochloride as core materials; using starch sodium octenyl succinate and cyclodextrin as wall materials, proportionally mixing the wall materials with anticaking agents, dispersants and aqueous phase antioxidants, and homogenizing and spray drying the mixture to obtain ethyl lauroyl arginate hydrochloride microcapsule powder. There is no need to add any organic solvents in the preparation process of the ethyl lauroyl arginate hydrochloride microcapsule, and the function activity of obtained products can be kept; and the ethyl lauroyl arginate hydrochloride microcapsule is characterized by increased solubility at low temperature and greatly improved usability and water solubility. The ethyl lauroyl arginate hydrochloride microcapsule is more conducive to processing, transportation and storage, and is excellent antiseptic materials. The ethyl lauroyl arginate hydrochloride microcapsule produced by the preparation technology is high in yield, and suitable for large-scale preparation to realize the continuous and large-scale production.

Description

technical field [0001] The invention relates to the technical field of production of ethyl lauroyl arginine hydrochloride microcapsules, in particular to a preparation process of ethyl lauroyl arginine hydrochloride microcapsules. Background technique [0002] Lauroyl arginine ethyl ester hydrochloride is a new type of antibacterial agent. The antibacterial properties of lauroyl arginine ethyl ester hydrochloride can reduce the surface tension of microbial cells and the formation of ion polymerization, so that the conductivity of microbial cell membranes and solubility changes, thereby disrupting cell membrane proteins. Disruption of membrane proteins results in the leakage of ions and other cellular components, altering the permeability of the microbial cell, which can inhibit the growth of the microbe, or inactivate it. According to research, ethyl lauroyl arginate hydrochloride has a strong antibacterial effect on Gram-negative and Gram-positive bacteria, yeast and mold....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A23L3/3526A01N47/44A01N25/28A01P1/00A01P3/00
CPCA01N25/28A01N47/44A23L3/3526A23V2002/00A23V2200/10A01N2300/00
Inventor 何同胜关荣荣
Owner 武汉志邦化学技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap