Outer ultraviolet-resistant polyethylene wallboard prepared from waste brick dregs and production method of wallboard

A kind of external wall panel and ultraviolet type technology, which is applied in the field of building materials, can solve the problems of large waste, achieve the effects of avoiding pollution, improving mechanical properties, and having a large market prospect

Inactive Publication Date: 2015-11-18
CHANGZHOU CITY WUJIN DISTRICT KAILIDA ELECTRONICS
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The demand for zirconia as a functional material and structural material is also increasing, and its production process cost is low, but the disadvantage is that it produces a large amount of waste (about 5m3 of dilute lye and acidic silicon slag are discharged per 1 ton of zirconia products) 1t)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A waste brick residue anti-ultraviolet polyethylene exterior wall board, which is made of the following weight raw materials: waste brick residue 70kg, polypropylene resin 40kg, chlorinated polyethylene 20kg, polyurethane elastomer 15kg, tetrafluoroethylene-hexafluoropropylene copolymer Material 20kg, isoprene rubber 15kg, nano alumina 2kg, mesh soil 10kg, sea mud 8kg, polyvinyl acetate 5kg, tung oil 4kg, waste syrup 3kg, sodium lauroyl sarcosinate 1kg, fir gum 3kg, asbestos wool 4kg , Additive 8kg, appropriate amount of water;

[0013] The additive is made of the following parts by weight of raw materials: Mg(NO3)2·6H2O and Al(NO3)3·9H2O are formulated into a mixed salt solution with a molar ratio of Mg2+ / Al3+ of 2:1, where [Mg2+]= 1mol / L, and use 2mol / L NaOH solution to adjust the pH value of the mixed salt solution to 10; take 400mL of the mixed salt solution, add it to a three-necked flask, condense and reflux in a constant temperature water bath at 80℃ and stir for 24...

Embodiment 2

[0017] Waste brick residue 70-75, polypropylene resin 50kg, chlorinated polyethylene 25kg, polyurethane elastomer 25kg, tetrafluoroethylene-hexafluoropropylene copolymer 25kg, isoprene rubber 20kg, nano alumina 4kg, mesh soil 12kg, sea Mud 810kg, polyvinyl acetate 8kg, tung oil 5kg, waste syrup 4.5kg, sodium lauroyl sarcosinate 1.5kg, fir gum 4kg, asbestos wool 6kg, additives 7kg, appropriate amount of water;

[0018] The additive is made of the following parts by weight of raw materials: Mg(NO3)2·6H2O and Al(NO3)3·9H2O are formulated into a mixed salt solution with a molar ratio of Mg2+ / Al3+ of 2:1, where [Mg2+]= 1mol / L, and use 2mol / L NaOH solution to adjust the pH value of the mixed salt solution to 10; take 400mL of the mixed salt solution, add it to a three-necked flask, condense and reflux in a constant temperature water bath at 80℃ and stir for 24 hours, and let the precipitate stand still After aging, the filter cake and the filtrate are separated by vacuum filtration, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an outer ultraviolet-resistant polyethylene wallboard prepared from waste brick dregs and a production method of the wallboard. The wallboard is prepared from raw materials in parts by weight as follows: 70-75 parts of the waste brick dregs and the like. The outer wallboard takes ceramic waste as a main raw material, the clay resource is saved, the production cost is reduced, the problem about treatment of the ceramic waste is also solved, and environmental pollution caused by the ceramic waste is avoided; laminated dihydroxy composite metal hydroxide adopts a multi-level overlapped laminated structure comprising main laminated bodies, namely, double metal hydroxide laminates, and interlamination objects, namely, anions, and the laminated dihydroxy composite metal hydroxide has the excellent physical shielding effect on ultraviolet rays and can effectively improve the ultraviolet aging resistance.

Description

Technical field [0001] The invention relates to the technical field of building materials, and more specifically to a waste brick slag UV-resistant polyethylene exterior wall board and a production method thereof. Background technique [0002] At present, most bricks are made by clay sintering. However, as the amount of clay mining increases, clay resources are increasingly scarce, which not only increases mining costs, but also has a serious impact on the ecological environment. Therefore, it is urgent to optimize and improve the current situation. Some brick-making methods to change the status quo. [0003] Decomposing zircon sand with sodium hydroxide is the main production process for producing zirconium oxychloride and zirconium dioxide in my country. my country's annual production capacity of zirconium oxychloride in 2007 has reached 150,000 tons, ranking first in the world. The demand for zirconium dioxide as a functional material and structural material is also increasing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/16C04B18/16
CPCY02W30/91
Inventor 臧磊
Owner CHANGZHOU CITY WUJIN DISTRICT KAILIDA ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products