Non-asbestos-fiber oil-resistant and high-temperature-resistant calcium silicate plate and preparation method thereof

A non-asbestos fiber and calcium silicate board technology is applied in the field of building wall materials, which can solve the problems of environmental pollution and flammability of materials, and achieve the effects of protecting the natural environment, improving mechanical properties and reducing production costs.

Inactive Publication Date: 2015-12-23
CHANGZHOU WUJIN GOLDEN SUNSHINE ELECTRONICS
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the wall insulation materials used are foam boards made of polymer materials. Although these materials can meet the requirements of building energy conservation, they are generally flammable and have certain pollution to the environment during the production process. , therefore, this type of material has been classified as a strictly restricted use material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board is made of the following raw materials in a weight percentage ratio: 10% polyurethane elastomer, 50% tetrafluoroethylene-hexafluoropropylene copolymer, 5% fly ash, isoprene rubber 15%, polyvinyl alcohol 1%, sodium dodecylbenzene sulfonate 9%, lime sand 0.5%, ethoxylated sodium alkyl sulfate 1%, glass fiber 7.5%, polycarboxylate high-performance water reducer 1%;

[0016] A preparation method of non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board: including the following steps: (1) adding 10% polyurethane elastomer, 5% fly ash, 0.5% lime sand and 15% expanded perlite to a ball mill (2) Add the composite powder into the mixer, add water twice the volume of the composite powder and stir, and add tetrafluoroethylene-hexafluoropropylene copolymer to it after stirring evenly 50%, polyvinyl alcohol 1%, sodium dodecylbenzene sulfonate 9%, glass fiber 7.5%...

Embodiment 2

[0019] A non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board, which is made of the following raw materials in a weight percentage ratio: polyurethane elastomer 20%, tetrafluoroethylene-hexafluoropropylene copolymer 40%, fly ash 7%, isoprene rubber 13%, polyvinyl alcohol 4%, sodium dodecylbenzene sulfonate 6%, lime sand 0.7%, ethoxylated alkyl sodium sulfate 1%, glass fiber 7.3%, polycarboxylate high-performance water reducer 1%;

[0020] A preparation method of non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board: including the following steps: (1) adding 20% ​​polyurethane elastomer, 7% fly ash, 0.7% lime sand and 13% expanded perlite to a ball mill (2) Add the composite powder into the mixer, add water twice the volume of the composite powder and stir, and add tetrafluoroethylene-hexafluoropropylene copolymer to it after stirring evenly 40%, polyvinyl alcohol 4%, sodium dodecylbenzene sulfonate 6%, glass f...

Embodiment 3

[0023] A non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board, which is made of the following raw materials in a weight percentage ratio: 30% polyurethane elastomer, 30% tetrafluoroethylene-hexafluoropropylene copolymer, 10% fly ash, isoprene rubber 10%, polyvinyl alcohol 5%, sodium dodecylbenzene sulfonate 5%, lime sand 1%, ethoxylated sodium alkyl sulfate 0.5%, glass fiber 6%, polycarboxylate high-performance water reducer 1.5%;

[0024] A preparation method of non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board: including the following steps: (1) adding 30% polyurethane elastomer, 10% fly ash, 1% lime sand and 10% expanded perlite to a ball mill (2) Add the composite powder into the mixer, add water twice the volume of the composite powder and stir, and add tetrafluoroethylene-hexafluoropropylene copolymer to it after stirring evenly 30%, polyvinyl alcohol 5%, sodium dodecylbenzene sulfonate 5%, glass fib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention relates to the field of building wall materials, particularly to a non-asbestos-fiber oil-resistant and high-temperature-resistant calcium silicate plate and a preparation method thereof, wherein the non-asbestos-fiber oil-resistant and high-temperature-resistant calcium silicate plate comprises, by weight, 30-45% of cement, 3-4% of fly ash, 3-3.5% of sodium silicate, 45-60% of polyisoprene rubber, and 3-3.5% of a water reducer. According to the present invention, the produced non-asbestos-fiber oil-resistant and high-temperature-resistant calcium silicate plate has characteristics of good sound insulation, good thermal insulation, good fire resistance and environmental protection during the production and use process; the added polyurethane elastomer has excellent wear resistance and excellent oil resistance, belongs to the polar polymer, and can be organically and integrally combined with polypropylene so as to efficiently improve the mechanical property of polypropylene; the added fluorine rubber has characteristics of high temperature resistance, oil resistance and the like; and the added other fillers have other physical properties and processability.

Description

technical field [0001] The invention relates to building wall materials, in particular to a non-asbestos fiber oil-resistant and high-temperature-resistant calcium silicate board. Background technique [0002] In recent years, with the rapid development of the real estate industry, people pay more and more attention to the construction industry closely related to it. Therefore, people's requirements for wall materials, which are an important part of building materials, are also getting higher and higher. And because in recent years, people pay more and more attention to environmental protection and energy saving, so integrating the concepts of environmental protection and energy saving into wall materials is the development trend of wall materials in the future. [0003] At present, most of the wall insulation materials used are foam boards made of polymer materials. Although these materials can meet the requirements of building energy conservation, they are generally flamma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/18C08L75/04C08L9/00C08K13/04C08K7/14C08K3/36C08K3/22
Inventor 上官挺
Owner CHANGZHOU WUJIN GOLDEN SUNSHINE ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka